CN107471518A

CN107471518A - The manufacture method of the latex bed mattress of health

Info

Publication number: CN107471518A
Application number: CN201710664011.3A
Authority: CN
Inventors: 王松明
Original assignee: Anji County Zhejiang Province Mei Jiaqi Household Articles Co Ltd
Current assignee: Anji County Zhejiang Province Mei Jiaqi Household Articles Co Ltd
Priority date: 2017-08-06
Filing date: 2017-08-06
Publication date: 2017-12-15

Abstract

The invention discloses a kind of manufacture method of healthy latex bed mattress, comprise the following steps：1）The acquisition of raw material：Oak Tree is selected, an openning is then cut at the 120cm of ground 90 in Oak Tree, then connects latex.The present invention, so as to ensure that mattress surface is smooth, ensure that the comfortableness of user by being repaiied to mattress except the projection on mattress, pass through flexibility test, the mechanical compression that the latex bed mattress that effectively can ensure to produce can be subjected to, so that it is determined that the quality of mattress, ensure that product is qualified.

Description

The manufacture method of the latex bed mattress of health

Technical field

The invention belongs to home life supplieshome life supplies technical field, more particularly, to a kind of manufacturer of healthy latex bed mattress Method.

Background technology

Among modern house life, people are constantly pursued the quality self lived, and the latex bed mattress on existing market is Through starting progressively to step among our life；The mattress that existing many business mens produce just is not sold after testing, some Underproof mattress customer is just useless using a period of time when purchase is gone back.

The content of the invention

The present invention is for overcome the deficiencies in the prior art, there is provided a kind of making side of up-to-standard healthy latex bed mattress Method.

To achieve these goals, the present invention uses following technical scheme：A kind of manufacture method of healthy latex bed mattress, Comprise the following steps：

1）The acquisition of raw material：Oak Tree is selected, an openning is then cut at the 90-120cm of ground in Oak Tree, then connects breast Glue；

2）Raw material processing：By step 1）Middle acquisition adds accelerator 15-29 parts, age resistor 7-12 among latex raw material Part, thickener 4-8 parts and oxidant 21-38 part foaming agent 22-29 parts, it is then placed among foaming machine and foams；

3）Latex gel：Heat sensitizer is added among the latex raw material that foaming is completed, is then placed into a length of 200cm, it is wide For 180cm, among a height of 25cm square dies, mould is placed into high-temperature steam room together with latex raw material and carries out high temperature Heating, the heat time is 120-150 minutes, and the latex after the completion of heating takes out immediately；

4）Latex notes shape：The latex that gel is completed is cut by shear；

5）The deburring of latex bed mattress：The latex that step 4 is completed carries out deburring, while removes the latex portion of surface protrusion Point, after deburring completion, manufactured latex bed mattress is placed and placed when under the shady and cool environment dried, after placing 3-5 days Flexibility test is carried out to latex bed mattress.

The present invention to mattress by repairing except the projection on mattress, and so as to ensure that mattress surface is smooth, ensure that makes The comfortableness of user, the mechanical compression that can be subjected to by flexibility test, the latex bed mattress that effectively can ensure to produce, from And the quality of mattress is determined, it ensure that product is qualified.

Further, step 5）The flexibility test is carries out the mechanical compression of 85-150 times to each latex bed mattress, so The mechanical compression for carrying out a 15000-25000 times test is extracted among every 800 afterwards；By carrying out machine to latex bed mattress The pressing test of tool, thereby may be ensured that the quality of each latex bed mattress to dispatch from the factory, while to latex by way of examination at random Mattress carries out more pressing, the service life per a collection of latex bed mattress produced can be supervised, so as to more preferable For serve.

Further, the interior that the shady and cool environment preferable temperature dried is 26 DEG C；Latex bed bottom is placed into 26 DEG C In the environment of, it can ensure that mattress will not be damaged because of high temperature, so as to ensure that the quality of mattress.

In summary, the present invention to mattress by repairing except the projection on mattress, so as to ensure that mattress surface is smooth, The comfortableness of user is ensure that, the machine that can be subjected to by flexibility test, the latex bed mattress that effectively can ensure to produce Tool presses, so that it is determined that the quality of mattress, ensure that product is qualified.

Embodiment

In order that those skilled in the art are better understood from the present invention program, it is right below in conjunction with the embodiment of the present invention Technical scheme in the embodiment of the present invention carries out clear, complete description.

Embodiment one：

A kind of manufacture method of healthy latex bed mattress, comprises the following steps：

1）The acquisition of raw material：Oak Tree is selected, 22:00-4:Latex is collected between 00；Then in Oak Tree at the 95cm of ground An openning is cut, and the openning is shaped as arc, stainless steel groove is inserted in the lower end of openning, described stainless A glassware is placed below steel groove；A screen pack is placed on the glassware simultaneously.

2）Raw material processing：By step 1）Middle acquisition among latex raw material add 15 parts of accelerator, 7 parts of age resistor, 4 parts of thickener and 21 parts of oxidant, 22 parts of foaming agent, are then placed among foaming machine, then by the adjustment of rotational speed of foaming machine To 50 revolutions per seconds, foamed time is 8 minutes.

3）Latex gel：Heat sensitizer is added among the latex raw material that foaming is completed, is then placed into a length of 200cm, a width of 180cm, among a height of 25cm square dies, mould is heated at high temperature together with latex raw material, heated Time is 120 minutes, and the latex after the completion of heating takes out immediately.

4）Latex notes shape：The latex that gel is completed is cut by shear, after completion is cut, then to breast Glue is punched, a diameter of 10mm in the hole beaten, and the spacing in the hole beaten is 25mm.

5）The deburring of latex bed mattress：The latex that step 4 is completed carries out deburring, while removes the latex of surface protrusion Part, after deburring completion, manufactured latex bed mattress is placed and placed when under the shady and cool environment dried, the environmental selection temperature 26 DEG C of interior；Flexibility test is carried out to latex bed mattress after placing 3 days；The test is to carry out 85 to each latex bed mattress Secondary mechanical compression, the mechanical compression for carrying out a 15000 times test is then extracted among every 800.

Embodiment two：

1）The acquisition of raw material：Oak Tree is selected, 22:00-4:Latex is collected between 00；Then in Oak Tree at the 91cm of ground An openning is cut, and the openning is shaped as arc, stainless steel groove is inserted in the lower end of openning, described stainless A glassware is placed below steel groove；A screen pack is placed on the glassware simultaneously.

2）Raw material processing：By step 1）Middle acquisition among latex raw material add 29 parts of accelerator, 12 parts of age resistor, 8 parts of thickener and 38 parts of oxidant, 29 parts of foaming agent, are then placed among foaming machine, then by the adjustment of rotational speed of foaming machine To 50-90 revolutions per seconds, foamed time is 5-10 minutes.

3）Latex gel：Heat sensitizer is added among the latex raw material that foaming is completed, is then placed into a length of 200cm, a width of 180cm, among a height of 25cm square dies, mould is heated at high temperature together with latex raw material, heated Time is 10-15 minutes, and the latex after the completion of heating takes out immediately.

4）Latex notes shape：The latex that gel is completed is cut by shear, after completion is cut, then to breast Glue is punched, a diameter of 15mm in the hole beaten, and the spacing in the hole beaten is 45mm.

5）The deburring of latex bed mattress：The latex that step 4 is completed carries out deburring, while removes the latex of surface protrusion Part, after deburring completion, manufactured latex bed mattress is placed and placed when under the shady and cool environment dried, the environmental selection temperature 26 DEG C of interior；Flexibility test is carried out to latex bed mattress after placing 5 days；The test is that each latex bed mattress is carried out The mechanical compression of 150 times, the mechanical compression for carrying out a 2500 times test is then extracted among every 800.

Obviously, described embodiment is only the part of the embodiment of the present invention, rather than whole embodiments.It is based on Embodiment in the present invention, those of ordinary skill in the art are obtained every other under the premise of creative work is not made Embodiment, it should all belong to the scope of protection of the invention.

Claims

1. a kind of manufacture method of healthy latex bed mattress, comprises the following steps：

1) acquisition of raw material：Oak Tree is selected, an openning is then cut at the 90-120cm of ground in Oak Tree, then connects breast Glue；

2) Raw material processing：Accelerator 15-29 parts, age resistor 7-12 are added among latex raw material by being obtained in step 1) Part, thickener 4-8 parts and oxidant 21-38 part foaming agent 22-29 parts, it is then placed among foaming machine and foams；

3) latex gel：Heat sensitizer is added among the latex raw material that foaming is completed, is then placed into a length of 200cm, it is wide For 180cm, among a height of 25cm square dies, mould is placed into high-temperature steam room together with latex raw material and carries out high temperature Heating, the heat time is 120-150 minutes, and the latex after the completion of heating takes out immediately；

4) latex note shape：The latex that gel is completed is cut by shear；

5) deburring of latex bed mattress：The latex that step 4) is completed carries out deburring, while removes the latex portion of surface protrusion Point, after deburring completion, manufactured latex bed mattress is placed and placed when under the shady and cool environment dried, after placing 3-5 days Flexibility test is carried out to latex bed mattress.

A kind of 2. manufacture method of healthy latex bed mattress according to claim 1, it is characterised in that：Step 5) the bullet Property test be that the mechanical compression of 85-150 times is carried out to each latex bed mattress, a progress is then extracted among every 800 The mechanical compression test of 15000-25000 times.

A kind of 3. manufacture method of healthy latex bed mattress according to claim 1, it is characterised in that：It is described shady and cool dry Environment preferable temperature be 26 DEG C of interior.