CN107313083A - 一种零件镀银环保电镀液 - Google Patents
一种零件镀银环保电镀液 Download PDFInfo
- Publication number
- CN107313083A CN107313083A CN201710610614.5A CN201710610614A CN107313083A CN 107313083 A CN107313083 A CN 107313083A CN 201710610614 A CN201710610614 A CN 201710610614A CN 107313083 A CN107313083 A CN 107313083A
- Authority
- CN
- China
- Prior art keywords
- parts
- sodium
- silver
- acid
- sodium sulphate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种零件镀银环保电镀液，由以下份数的原料组分组成：硝酸银60～90份、醋酸铵10～20份、氮苯羧酸80～120份、焦亚硫酸钠20～40份、月桂醇聚氧乙烯醚硫酸钠6～10份，椰油酰胺丙基甜菜碱12～20份，硫酸钠10～20份、全氟丁基磺酰氟10～15份、三乙醇胺2～18份、柠檬酸1～5份、石油磺酸钠5～15份、脂肪醇聚氧乙烯醚2～4份、对硝基苯甲酸2～4份、四硼酸钠1～2份、二甲基马来酸酐2～3份、去离子水若干，本发明的一种零件镀银环保电镀液可以改善汽车零件加工设备的冷却效果，方便根据需要使用，便于更好地针对汽车零件加工设备进行冷却。
Description
技术领域
本发明属于汽车零件电镀液技术领域，具体涉及一种零件镀银环保电镀液。
背景技术
镀银层很容易抛光，有很强的反光本领和良好的导热、导电、焊接性能，对有机酸和碱的化学稳定性高，且其价格相对于其他贵金属便宜，已广泛应用于电子工业、装饰品、餐具和各种工艺品的领域。
由于具有电流效率高、分散能力好、覆盖能力强、镀层结晶细致等优点，目前，国内外大多还是采用有氰镀银工艺电镀银层。但氰化物镀银液具有剧毒性，严重污染环境，危害生产者的健康，而且废液处理成本较高，所以人们希望用其它电镀工艺来取代氰化物电镀银工艺。但目前使用的无氰镀银体系普遍存在镀层性能较低等问题，因此从安全、环境保护等方面考虑，研制一种低毒、稳定的镀银液和镀银工艺来代替氰化物电镀银的意义深远而又迫在眉睫。
发明内容
本发明要解决的技术问题是提供一种零件镀银环保电镀液，更好地改善汽车零件加工设备的电镀效果，方便根据需要使用，便于更好地针对汽车零件加工设备进行电镀处理。
为实现上述技术目的，达到上述技术效果，本发明通过以下技术方案实现：
一种零件镀银环保电镀液，由以下份数的原料组分组成：硝酸银60～90份、醋酸铵10～20份、氮苯羧酸80～120份、焦亚硫酸钠20～40份、月桂醇聚氧乙烯醚硫酸钠6～10份，椰油酰胺丙基甜菜碱12～20份，硫酸钠10～20份、全氟丁基磺酰氟10～15份、三乙醇胺2～18份、柠檬酸1～5份、石油磺酸钠5～15份、脂肪醇聚氧乙烯醚2～4份、对硝基苯甲酸2～4份、四硼酸钠1～2份、二甲基马来酸酐2～3份、去离子水若干。
优选的，还可由以下份数的原料组分组成：硝酸银60份、醋酸铵10份、氮苯羧酸80份、焦亚硫酸钠20份、月桂醇聚氧乙烯醚硫酸钠6份，椰油酰胺
丙基甜菜碱12份，硫酸钠10份、全氟丁基磺酰氟10份、三乙醇胺2份、柠檬酸1份、石油磺酸钠5份、脂肪醇聚氧乙烯醚2份、对硝基苯甲酸2份、四硼酸钠1份、二甲基马来酸酐2份、去离子水若干。
优选的，还可由以下份数的原料组分组成：硝酸银80份、醋酸铵15份、氮苯羧酸100份、焦亚硫酸钠30份、月桂醇聚氧乙烯醚硫酸钠8份，椰油酰胺丙基甜菜碱16份，硫酸钠15份、全氟丁基磺酰氟13份、三乙醇胺10份、柠檬酸3份、石油磺酸钠10份、脂肪醇聚氧乙烯醚3份、对硝基苯甲酸3份、四硼酸钠1份、二甲基马来酸酐2份、去离子水若干。
优选的，还可由以下份数的原料组分组成：硝酸银90份、醋酸铵20份、氮苯羧酸120份、焦亚硫酸钠40份、月桂醇聚氧乙烯醚硫酸钠10份，椰油酰胺丙基甜菜碱20份，硫酸钠20份、全氟丁基磺酰氟15份、三乙醇胺18份、柠檬酸5份、石油磺酸钠15份、脂肪醇聚氧乙烯醚4份、对硝基苯甲酸4份、四硼酸钠2份、二甲基马来酸酐3份、去离子水若干。
一种零件镀银环保电镀液，所述零件镀银环保电镀液的制备方法如下：
(1)将上述质量份数的去离子水加热到70～85℃，然后将上述质量份数的月桂醇聚氧乙烯醚硫酸钠、椰油酰胺丙基甜菜碱、硫酸钠、全氟丁基磺酰氟依次加入，混合均匀，获得A溶液；
(2)将上述A溶液升温至90～95℃后，依次加入上述质量份数的三乙醇胺和四硼酸钠，混合均匀后，予以冷却至室温，即获得本品。
本发明的有益效果在于：本发明的零件镀银环保电镀液可以改善汽车零件加工设备的电镀效果，方便根据需要使用，便于更好地针对汽车零件加工设备进行电镀。
具体实施方式
实施例:一种零件镀银环保电镀液，由以下份数的原料组分组成：硝酸银60～90份、醋酸铵10～20份、氮苯羧酸80～120份、焦亚硫酸钠20～40份、月桂醇聚氧乙烯醚硫酸钠6～10份，椰油酰胺丙基甜菜碱12～20份，硫酸钠10～20份、全氟丁基磺酰氟10～15份、三乙醇胺2～18份、柠檬酸1～5份、石油磺酸钠5～15份、脂肪醇聚氧乙烯醚2～4份、对硝基苯甲酸2～4份、四
硼酸钠1～2份、二甲基马来酸酐2～3份、去离子水若干。
优选的，还可由以下份数的原料组分组成：硝酸银60份、醋酸铵10份、氮苯羧酸80份、焦亚硫酸钠20份、月桂醇聚氧乙烯醚硫酸钠6份，椰油酰胺丙基甜菜碱12份，硫酸钠10份、全氟丁基磺酰氟10份、三乙醇胺2份、柠檬酸1份、石油磺酸钠5份、脂肪醇聚氧乙烯醚2份、对硝基苯甲酸2份、四硼酸钠1份、二甲基马来酸酐2份、去离子水若干。
优选的，还可由以下份数的原料组分组成：硝酸银80份、醋酸铵15份、氮苯羧酸100份、焦亚硫酸钠30份、月桂醇聚氧乙烯醚硫酸钠8份，椰油酰胺丙基甜菜碱16份，硫酸钠15份、全氟丁基磺酰氟13份、三乙醇胺10份、柠檬酸3份、石油磺酸钠10份、脂肪醇聚氧乙烯醚3份、对硝基苯甲酸3份、四硼酸钠1份、二甲基马来酸酐2份、去离子水若干。
优选的，还可由以下份数的原料组分组成：硝酸银90份、醋酸铵20份、氮苯羧酸120份、焦亚硫酸钠40份、月桂醇聚氧乙烯醚硫酸钠10份，椰油酰胺丙基甜菜碱20份，硫酸钠20份、全氟丁基磺酰氟15份、三乙醇胺18份、柠檬酸5份、石油磺酸钠15份、脂肪醇聚氧乙烯醚4份、对硝基苯甲酸4份、四硼酸钠2份、二甲基马来酸酐3份、去离子水若干。
一种零件镀银环保电镀液，所述零件镀银环保电镀液的制备方法如下：
(1)将上述质量份数的去离子水加热到70～85℃，然后将上述质量份数的月桂醇聚氧乙烯醚硫酸钠、椰油酰胺丙基甜菜碱、硫酸钠、全氟丁基磺酰氟依次加入，混合均匀，获得A溶液；
(2)将上述A溶液升温至90～95℃后，依次加入上述质量份数的三乙醇胺和四硼酸钠，混合均匀后，予以冷却至室温，即获得本品。
以上所述仅是本发明的优选应用实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进。
Claims (5)
1.一种零件镀银环保电镀液，其特征在于：由以下份数的原料组分组成：硝酸银60～90份、醋酸铵10～20份、氮苯羧酸80～120份、焦亚硫酸钠20～40份、月桂醇聚氧乙烯醚硫酸钠6～10份，椰油酰胺丙基甜菜碱12～20份，硫酸钠10～20份、全氟丁基磺酰氟10～15份、三乙醇胺2～18份、柠檬酸1～5份、石油磺酸钠5～15份、脂肪醇聚氧乙烯醚2～4份、对硝基苯甲酸2～4份、四硼酸钠1～2份、二甲基马来酸酐2～3份、去离子水若干。
2.根据权利要求1所述的零件镀银环保电镀液，其特征在于：由以下份数的原料组分组成：硝酸银60份、醋酸铵10份、氮苯羧酸80份、焦亚硫酸钠20份、月桂醇聚氧乙烯醚硫酸钠6份，椰油酰胺丙基甜菜碱12份，硫酸钠10份、全氟丁基磺酰氟10份、三乙醇胺2份、柠檬酸1份、石油磺酸钠5份、脂肪醇聚氧乙烯醚2份、对硝基苯甲酸2份、四硼酸钠1份、二甲基马来酸酐2份、去离子水若干。
3.根据权利要求1所述的零件镀银环保电镀液，其特征在于：由以下份数的原料组分组成：硝酸银80份、醋酸铵15份、氮苯羧酸100份、焦亚硫酸钠30份、月桂醇聚氧乙烯醚硫酸钠8份，椰油酰胺丙基甜菜碱16份，硫酸钠15份、全氟丁基磺酰氟13份、三乙醇胺10份、柠檬酸3份、石油磺酸钠10份、脂肪醇聚氧乙烯醚3份、对硝基苯甲酸3份、四硼酸钠1份、二甲基马来酸酐2份、去离子水若干。
4.根据权利要求1所述的零件镀银环保电镀液，其特征在于：由以下份数的原料组分组成：硝酸银90份、醋酸铵20份、氮苯羧酸120份、焦亚硫酸钠40份、月桂醇聚氧乙烯醚硫酸钠10份，椰油酰胺丙基甜菜碱20份，硫酸钠20份、全氟丁基磺酰氟15份、三乙醇胺18份、柠檬酸5份、石油磺酸钠15份、脂肪醇聚氧乙烯醚4份、对硝基苯甲酸4份、四硼酸钠2份、二甲基马来酸酐3份、去离子水若干。
5.根据权利要求1至4任一项所述的零件镀银环保电镀液，其特征在于：所述零件镀银环保电镀液的制备方法如下：
(1)将上述质量份数的去离子水加热到70～85℃，然后将上述质量份数的月桂醇聚氧乙烯醚硫酸钠、椰油酰胺丙基甜菜碱、硫酸钠、全氟丁基磺酰氟依次加入，混合均匀，获得A溶液；
(2)将上述A溶液升温至90～95℃后，依次加入上述质量份数的三乙醇胺和四硼酸钠，混合均匀后，予以冷却至室温，即获得本品。