CN107162222A - 一种水处理用环保缓释长效阻垢剂 - Google Patents
一种水处理用环保缓释长效阻垢剂 Download PDFInfo
- Publication number
- CN107162222A CN107162222A CN201710521343.6A CN201710521343A CN107162222A CN 107162222 A CN107162222 A CN 107162222A CN 201710521343 A CN201710521343 A CN 201710521343A CN 107162222 A CN107162222 A CN 107162222A
- Authority
- CN
- China
- Prior art keywords
- parts
- antisludging agent
- acting
- slow release
- water process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种水处理用环保缓释长效阻垢剂，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：20~30份，三乙醇胺：10~15份，聚丙烯酸钠：20~30份，硫酸锌：10~15份，木质素磺酸盐：5~10份，乙二醇：5~10份，苯并三唑：5~10份，改性聚羧酸盐：5~10份，甲基苯骈三氮唑：5~10份，分散剂：5~10份，阻聚剂：5~10份，抗氧剂：5~10份，去离子水：40~50份。所述阻垢剂成分设计合理，制备工艺简单，对环境友好，生产成本低，经济效益好。
Description
技术领域
本发明属于水处理净化技术领域，具体地，涉及一种水处理用环保缓释长效阻垢剂。
背景技术
阻垢剂（scale inhibitor）：是具有能分散水中的难溶性无机盐、阻止或干扰难溶性无机盐在金属表面的沉淀、结垢功能，并维持金属设备有良好的传热效果的一类药剂。
阻垢剂能除去垢和阻止水垢的形成,提高热交换效率,减少电能或减少燃料的消耗；水处理还可减少排污，提高水的利用率，一般可节约60%以上，符合我国节能减排的新政策。
按照阻垢剂的聚合成份，可将其分为天然聚合物阻垢剂和合成聚合物阻垢剂两大类。而合成聚合物阻垢剂又可进一步分成羧酸类聚合物阻垢剂、磺酸类聚合物阻垢剂、含磷聚合物阻垢剂和环境友好型阻垢剂4种。
对于综合集装架层板，目前国内主要存在如下专利文献：
中国专利公开号：CN106809962A，公开了一种复合缓蚀阻垢剂及其制备方法和应用，所述方法包括：将含聚环氧琥珀酸水溶液与无机酸溶液混合，搅拌均匀，静置，待形成沉淀后取上清液，并将上清液与水解聚马来酸酐、有机膦酸类缓蚀阻垢剂、磺酸类共聚物和含锌化合物中的一种或多种进行复配。本发明的方法能够有效避免制备得到的复合缓蚀阻垢剂产生浑浊和沉淀的问题，并能够保证复合缓蚀阻垢剂具有优异的缓蚀阻垢效果。然而，该专利所提供的阻垢剂，生产成本高。
发明内容
为解决上述存在的问题，本发明的目的在于提供一种水处理用环保缓释长效阻垢剂，所述阻垢剂成分设计合理，制备工艺简单，对环境友好，生产成本低，经济效益好。
为达到上述目的，本发明的技术方案是：
一种水处理用环保缓释长效阻垢剂，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：20~30份，三乙醇胺：10~15份，聚丙烯酸钠：20~30份，硫酸锌：10~15份，木质素磺酸盐：5~10份，乙二醇：5~10份，苯并三唑：5~10份，改性聚羧酸盐：5~10份，甲基苯骈三氮唑：5~10份，分散剂：5~10份，阻聚剂：5~10份，抗氧剂：5~10份，去离子水：40~50份。
进一步，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：25~30份，三乙醇胺：10~13份，聚丙烯酸钠：25~30份，硫酸锌：10~13份，木质素磺酸盐：5~8份，乙二醇：7~10份，苯并三唑：8~10份，改性聚羧酸盐：5~7份，甲基苯骈三氮唑：6~10份，分散剂：5~6份，阻聚剂：8~10份，抗氧剂：7~10份，去离子水：45~50份。
优选地，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：25份，三乙醇胺：13份，聚丙烯酸钠：25份，硫酸锌：12份，木质素磺酸盐：7份，乙二醇：8份，苯并三唑：8份，改性聚羧酸盐：7份，甲基苯骈三氮唑：7份，分散剂：6份，阻聚剂：9份，抗氧剂：7份，去离子水：45份。
优选地，所述改性聚羧酸盐为丙烯酸-丙烯酸酯-磺酸盐。
优选地，所述分散剂为脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、脂肪酸聚氧乙烯醚或硬脂酸甘油酯。
优选地，所述阻聚剂为乙基羟胺、N,N’-二乙基羟胺、异丙基羟胺或N,N’-二异丙基羟胺。
优选地，所述抗氧剂为2,6-二叔丁基对甲酚、2,6-二叔丁基苯酚，2-叔丁基-4,6-二甲基苯酚或2,6-二叔丁基-4-乙基苯酚。
优选地，所述制备方法包括如下步骤：1)按照配比将乙二醇加入反应釜，边搅拌边升温至60~70℃，另取容器，加入三乙醇胺、聚丙烯酸钠、硫酸锌、木质素磺酸盐、苯并三唑、改性聚羧酸盐、甲基苯骈三氮唑及去离子水，搅拌混合后得混合液，将混合液以100~200ml/min的速度加入反应釜内，升温至80~90℃，保温、搅拌30~50min；2)继续搅拌，边搅拌边向反应釜内加入分散剂、阻聚剂、抗氧剂，控制釜内温度在130~140℃之间，搅拌1~2h，降温至常温，得到所述水处理用环保缓释长效阻垢剂成品。
本发明的有益效果在于：
所述阻垢剂成分设计合理，制备工艺简单，对环境友好，生产成本低，经济效益好。
具体实施方式
下面通过具体实施例对本发明做进一步的说明，但实施例并不限制本发明的保护范围。
本发明所述的一种水处理用环保缓释长效阻垢剂，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：20~30份，三乙醇胺：10~15份，聚丙烯酸钠：20~30份，硫酸锌：10~15份，木质素磺酸盐：5~10份，乙二醇：5~10份，苯并三唑：5~10份，改性聚羧酸盐：5~10份，甲基苯骈三氮唑：5~10份，分散剂：5~10份，阻聚剂：5~10份，抗氧剂：5~10份，去离子水：40~50份。
进一步，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：25~30份，三乙醇胺：10~13份，聚丙烯酸钠：25~30份，硫酸锌：10~13份，木质素磺酸盐：5~8份，乙二醇：7~10份，苯并三唑：8~10份，改性聚羧酸盐：5~7份，甲基苯骈三氮唑：6~10份，分散剂：5~6份，阻聚剂：8~10份，抗氧剂：7~10份，去离子水：45~50份。
优选地，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：25份，三乙醇胺：13份，聚丙烯酸钠：25份，硫酸锌：12份，木质素磺酸盐：7份，乙二醇：8份，苯并三唑：8份，改性聚羧酸盐：7份，甲基苯骈三氮唑：7份，分散剂：6份，阻聚剂：9份，抗氧剂：7份，去离子水：45份。
优选地，所述改性聚羧酸盐为丙烯酸-丙烯酸酯-磺酸盐。
优选地，所述分散剂为脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、脂肪酸聚氧乙烯醚或硬脂酸甘油酯。
优选地，所述阻聚剂为乙基羟胺、N,N’-二乙基羟胺、异丙基羟胺或N,N’-二异丙基羟胺。
优选地，所述抗氧剂为2,6-二叔丁基对甲酚、2,6-二叔丁基苯酚，2-叔丁基-4,6-二甲基苯酚或2,6-二叔丁基-4-乙基苯酚。
优选地，所述制备方法包括如下步骤：1)按照配比将乙二醇加入反应釜，边搅拌边升温至60~70℃，另取容器，加入三乙醇胺、聚丙烯酸钠、硫酸锌、木质素磺酸盐、苯并三唑、改性聚羧酸盐、甲基苯骈三氮唑及去离子水，搅拌混合后得混合液，将混合液以100~200ml/min的速度加入反应釜内，升温至80~90℃，保温、搅拌30~50min；2)继续搅拌，边搅拌边向反应釜内加入分散剂、阻聚剂、抗氧剂，控制釜内温度在130~140℃之间，搅拌1~2h，降温至常温，得到所述水处理用环保缓释长效阻垢剂成品。
需要说明的是，以上实施例仅用以说明本发明的技术方案而非限制。尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的范围，其均应涵盖在本发明的权利要求范围中。
Claims (8)
1.一种水处理用环保缓释长效阻垢剂，其特征在于，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：20~30份，三乙醇胺：10~15份，聚丙烯酸钠：20~30份，硫酸锌：10~15份，木质素磺酸盐：5~10份，乙二醇：5~10份，苯并三唑：5~10份，改性聚羧酸盐：5~10份，甲基苯骈三氮唑：5~10份，分散剂：5~10份，阻聚剂：5~10份，抗氧剂：5~10份，去离子水：40~50份。
2.根据权利要求1所述的一种水处理用环保缓释长效阻垢剂，其特征在于，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：25~30份，三乙醇胺：10~13份，聚丙烯酸钠：25~30份，硫酸锌：10~13份，木质素磺酸盐：5~8份，乙二醇：7~10份，苯并三唑：8~10份，改性聚羧酸盐：5~7份，甲基苯骈三氮唑：6~10份，分散剂：5~6份，阻聚剂：8~10份，抗氧剂：7~10份，去离子水：45~50份。
3.根据权利要求1所述的一种水处理用环保缓释长效阻垢剂，其特征在于，所述阻垢剂包括如下重量份的成分：乙二胺四乙酸二钠：25份，三乙醇胺：13份，聚丙烯酸钠：25份，硫酸锌：12份，木质素磺酸盐：7份，乙二醇：8份，苯并三唑：8份，改性聚羧酸盐：7份，甲基苯骈三氮唑：7份，分散剂：6份，阻聚剂：9份，抗氧剂：7份，去离子水：45份。
4.根据权利要求1所述的一种水处理用环保缓释长效阻垢剂，其特征在于，所述改性聚羧酸盐为丙烯酸-丙烯酸酯-磺酸盐。
5.根据权利要求1所述的一种水处理用环保缓释长效阻垢剂，其特征在于，所述分散剂为脂肪醇聚氧乙烯醚、烷基酚聚氧乙烯醚、脂肪酸聚氧乙烯醚或硬脂酸甘油酯。
6.根据权利要求1所述的一种水处理用环保缓释长效阻垢剂，其特征在于，所述阻聚剂为乙基羟胺、N,N’-二乙基羟胺、异丙基羟胺或N,N’-二异丙基羟胺。
7.根据权利要求1所述的一种水处理用环保缓释长效阻垢剂，其特征在于，所述抗氧剂为2,6-二叔丁基对甲酚、2,6-二叔丁基苯酚，2-叔丁基-4,6-二甲基苯酚或2,6-二叔丁基-4-乙基苯酚。
8.一种如权利要求1所述的水处理用环保缓释长效阻垢剂的制备方法，其特征在于，所述制备方法包括如下步骤：1)按照配比将乙二醇加入反应釜，边搅拌边升温至60~70℃，另取容器，加入三乙醇胺、聚丙烯酸钠、硫酸锌、木质素磺酸盐、苯并三唑、改性聚羧酸盐、甲基苯骈三氮唑及去离子水，搅拌混合后得混合液，将混合液以100~200ml/min的速度加入反应釜内，升温至80~90℃，保温、搅拌30~50min；2)继续搅拌，边搅拌边向反应釜内加入分散剂、阻聚剂、抗氧剂，控制釜内温度在130~140℃之间，搅拌1~2h，降温至常温，得到所述水处理用环保缓释长效阻垢剂成品。