CN106987187A - 一种水泥涂料及其制备方法 - Google Patents
一种水泥涂料及其制备方法 Download PDFInfo
- Publication number
- CN106987187A CN106987187A CN201710159559.2A CN201710159559A CN106987187A CN 106987187 A CN106987187 A CN 106987187A CN 201710159559 A CN201710159559 A CN 201710159559A CN 106987187 A CN106987187 A CN 106987187A
- Authority
- CN
- China
- Prior art keywords
- parts
- cement
- sodium
- cement paint
- rosin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及水泥涂料技术领域，具体涉及一种水泥涂料及其制备方法，主要由以下重量份原料制成：水泥80‑100份、聚丙烯酸酯乳液90‑110份、纳米二氧化钛4‑6份、偏硼酸钡2‑4份、五氯苯酚钠2‑3份、2，2'‑二羟基‑5，5'‑二氯二苯基甲烷2‑4份、脂肪酸钠3‑5份、松香4‑6份、烷基苯磺酸钠0.2‑0.3份、糊精0.5‑1.0份、葡萄糖0.5‑1.0份、壬基酚聚氧乙烯醚4‑7份及水45‑55份，其制备包括原料混合、搅拌、检测等步骤。该水泥涂料具有优异的防霉、防潮及抗冻性能，有效延长水泥涂料的使用寿命，制备方法简单，易生产。
Description
技术领域
本发明涉及水泥涂料技术领域，具体涉及一种水泥涂料及其制备方法。
背景技术
水泥涂料是一种主要由水泥组成的涂料，广泛应用于大面积的地下室、墙壁、地面等。水泥涂料因光、热、细菌等因素的影响导致性能下降，导致水泥涂料的寿命短。如水泥涂料遭到霉菌等多种生物体的破坏，造成涂膜色变、发粘、穿孔、破坏和剥落，失去附着力，影响涂膜的保护性能及材料的整洁和外观，降低力学性能，缩短使用寿命，给环境卫生造成危害。梅雨天气或回南天，墙壁十分潮湿，水泥涂料涂膜出水，使得室内环境潮湿，不舒适。但是目前市场上的水泥涂料防霉性、防潮性、抗冻性等性能不理想，使用寿命短，应用范围小，远远不能满足人们的需求。
发明内容
本发明的发明目的在于：针对上述存在的问题，提供一种水泥涂料及其制备方法，具有优异的防霉、防潮及抗冻性能，有效延长水泥涂料的使用寿命，其制备方法简单，易生产。
为了实现上述目的，本发明采用的技术方案如下：
一种水泥涂料，主要由以下重量份原料制成：水泥80-100份、聚丙烯酸酯乳液90-110份、纳米二氧化钛4-6份、偏硼酸钡2-4份、五氯苯酚钠2-3份、2，2'-二羟基-5，5'-二氯二苯基甲烷2-4份、脂肪酸钠3-5份、松香4-6份、烷基苯磺酸钠0.2-0.3份、烷基苯酚聚氧乙烯醚0.2-0.3份、糊精0.5-1.0份、葡萄糖0.5-1.0份及水45-55份。
优选地，主要由以下重量份原料制成：水泥90份、聚丙烯酸酯乳液100份、纳米二氧化钛5份、偏硼酸钡3份、五氯苯酚钠2.5份、2，2'-二羟基-5，5'-二氯二苯基甲烷2.5份、脂肪酸钠4份、松香5份、烷基苯磺酸钠0.25份、烷基苯酚聚氧乙烯醚0.25份、糊精0.7份、葡萄糖0.7份及水50份。
如上所述的水泥涂料的制备方法，具体包括以下步骤：
(1)分别按重量份准确称取纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精及葡萄糖，加入研磨机内进行研磨，过筛，备用；
(2)将步骤(1)中研磨的纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精、葡萄糖和水泥一起加入搅拌机内搅拌混合均匀，得到混合物，备用；
(3)按重量份准确称取聚丙烯酸酯乳液和水，加入所述混合物中，高速搅拌混合，过筛，得到所述水泥涂料；
(4)将所述水泥涂料进行性能检测，并包装，入库。
优选地，步骤(1)和步骤(3)中所述过筛的目数均为60-80目。
优选地，步骤(3)中所述高速搅拌的速度均为400-500r/min。
如上所述的水泥涂料的使用方法，所述的水泥涂料分2次涂膜，待第一次涂膜表面干燥后，继续第二次涂膜，涂膜总厚度为1.0-1.5mm。
综上所述，由于采用了上述技术方案，本发明的有益效果是：
本发明的水泥涂料由水泥、聚丙烯酸酯乳液、纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精、葡萄糖及水机械搅拌混合而成。其中，纳米二氧化钛、偏硼酸钡、五氯苯酚钠及2，2'-二羟基-5，5'-二氯二苯基甲烷属于防霉剂，纳米二氧化钛的抗菌范围广泛，在光的作用下发生光催化作用产生一系列的活性氧化物质，这些活性氧化物质具有很强的氧化活性，能降解微生物的有机组分，从而杀死微生物，且纳米二氧化钛粒径小，分散于水泥涂料中，有效增强水泥涂料的拉伸强度，偏硼酸钡遇水分解，金属离子与细菌接触反应造成细菌固有成分被破坏，导致细菌死亡，不与其他物质发生反应，因此能长时间的防霉，五氯苯酚钠水中溶解度大，含有氯原子较多，其氯化程度高，因此具有很强的灭菌能力，2，2'-二羟基-5，5'-二氯二苯基甲烷含有亲水基团羟基和氯原子，能快速分散于水泥涂料中，与微生物快速接触进入细胞抑制微生物的繁殖，杀菌范围广泛，以上多种防霉剂混合使用，相互作用，大大增加了防霉范围，有效促进的水泥涂料的防霉功能；脂肪酸钠及松香是防潮剂，挥发速度缓慢，因此所需的挥发热量减少，表面温度下降不够，空气中的水汽未能凝结，松香中含有共轭双键和羧基，具有较强的反应性，能与水泥中的钙离子反应生成钙化松香，与脂肪酸钠中的钠离子反应生成松香钠皂，这些生成物不溶于水，随水进入水泥孔隙内，从而有效促进水泥涂料的防潮性；烷基苯磺酸钠及烷基苯酚聚氧乙烯醚是引气剂，所含亲水基和亲油基的吸附性能较好，有效降低水泥涂料的界面自由能，使得水泥涂料在搅拌过程时更加容易引入空气而形成均匀稳定的气泡，能和水泥中的钙离子形成钙盐沉淀，吸附于气泡膜上形成薄膜，能有效防止气泡破灭，促进水泥涂料的抗冻性。这些物质加入到水泥涂料中，取长补短，相铺相成，显著提高了水泥涂料的综合性能，使其具有优异的防霉性、防潮性及抗冻性，有效延长了水泥涂料的使用寿命。
具体实施方式
下面通过具体实施例对本发明的技术方案进行清楚、完整地描述。
实施例1
一种水泥涂料，主要由以下重量份原料制成：水泥80份、聚丙烯酸酯乳液90份、纳米二氧化钛4份、偏硼酸钡2份、五氯苯酚钠2份、2，2'-二羟基-5，5'-二氯二苯基甲烷2份、脂肪酸钠3份、松香4份、烷基苯磺酸钠0.2份、烷基苯酚聚氧乙烯醚0.2份、糊精0.5份、葡萄糖0.5份及水45份。
将上述配比的预料使用下述的方法制备水泥涂料，具体包括以下步骤：
(1)分别按重量份准确称取纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精及葡萄糖，加入研磨机内进行研磨，过60目筛，备用；
(2)将步骤(1)中研磨的纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精、葡萄糖和水泥一起加入搅拌机内搅拌混合均匀，得到混合物，备用；
(3)按重量份准确称取聚丙烯酸酯乳液和水，加入所述混合物中，以400r/min的速度高速搅拌混合，过60目筛，得到所述水泥涂料；
(4)将所述水泥涂料进行性能检测，并包装，入库。
使用方法：使用上述制得的水泥涂料时分2次涂膜，待第一次涂膜表面干燥后，继续第二次涂膜，涂膜总厚度为1.0mm。
实施例2
一种水泥涂料，主要由以下重量份原料制成：水泥90份、聚丙烯酸酯乳液100份、纳米二氧化钛5份、偏硼酸钡3份、五氯苯酚钠2.5份、2，2'-二羟基-5，5'-二氯二苯基甲烷2.5份、脂肪酸钠4份、松香5份、烷基苯磺酸钠0.25份、烷基苯酚聚氧乙烯醚0.25份、糊精0.7份、葡萄糖0.7份及水50份。
将上述配比的预料使用下述的方法制备水泥涂料，具体包括以下步骤：
(1)分别按重量份准确称取纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精及葡萄糖，加入研磨机内进行研磨，过70目筛，备用；
(2)将步骤(1)中研磨的纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精、葡萄糖和水泥一起加入搅拌机内搅拌混合均匀，得到混合物，备用；
(3)按重量份准确称取聚丙烯酸酯乳液和水，加入所述混合物中，以450r/min的速度高速搅拌混合，过70目筛，得到所述水泥涂料；
(4)将所述水泥涂料进行性能检测，并包装，入库。
使用方法：使用上述制得的水泥涂料时分2次涂膜，待第一次涂膜表面干燥后，继续第二次涂膜，涂膜总厚度为1.3mm。
实施例3
一种水泥涂料，主要由以下重量份原料制成：水泥100份、聚丙烯酸酯乳液110份、纳米二氧化钛6份、偏硼酸钡4份、五氯苯酚钠3份、2，2'-二羟基-5，5'-二氯二苯基甲烷4份、脂肪酸钠5份、松香6份、烷基苯磺酸钠0.3份、烷基苯酚聚氧乙烯醚0.3份、糊精1.0份、葡萄糖1.0份及水55份。
将上述配比的预料使用下述的方法制备水泥涂料，具体包括以下步骤：
(1)分别按重量份准确称取纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精及葡萄糖，加入研磨机内进行研磨，过80目筛，备用；
(2)将步骤(1)中研磨的纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精、葡萄糖和水泥一起加入搅拌机内搅拌混合均匀，得到混合物，备用；
(3)按重量份准确称取聚丙烯酸酯乳液和水，加入所述混合物中，以500r/min的速度高速搅拌混合，过80目筛，得到所述水泥涂料；
(4)将所述水泥涂料进行性能检测，并包装，入库。
使用方法：使用上述制得的水泥涂料时分2次涂膜，待第一次涂膜表面干燥后，继续第二次涂膜，涂膜总厚度为1.5mm。
为了进一步说明本发明水泥涂料的性能优异，进行了大量实验，并按照国家性能检测标准对水泥涂料进行多种防霉性、防潮性及抗冻性的性能检测，实验结果如表1所示。
对照组：市面上出售的水泥涂料。
第1组：水泥涂料采用的原料为水泥、聚丙烯酸酯乳液、纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、糊精、葡萄糖及水，其他按照本发明实施例1制备得到水泥涂料。
第2组：水泥涂料采用的原料为水泥、聚丙烯酸酯乳液、脂肪酸钠、松香、糊精、葡萄糖及水，其他按照本发明实施例1制备得到水泥涂料。
第3组：水泥涂料采用的原料为水泥、聚丙烯酸酯乳液、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精、葡萄糖及水，其他按照本发明实施例1制备得到水泥涂料。
第4组：本发明实施例1。
第5组：本发明实施例2。
第6组：本发明实施例3。
表1水泥涂料的性能检测
| 组别 | 拉伸强度/MPa | 防霉性/d | 防潮性/d | 抗冻性/d |
| 对照组 | 0.7 | 13 | 14 | 13 |
| 第1组 | 1.3 | 23 | 11 | 12 |
| 第2组 | 1.0 | 10 | 25 | 11 |
| 第3组 | 0.9 | 11 | 12 | 25 |
| 第4组 | 1.6 | 28 | 30 | 29 |
| 第5组 | 1.8 | 30 | 32 | 31 |
| 第6组 | 2.1 | 32 | 34 | 33 |
从表1可知，第1-3组的数据与对照组比较，第1组加入防霉剂，所制得的水泥涂料的防霉性能和拉伸强度最佳，第2组加入防潮剂，所制得的水泥涂料的防潮性能最佳，第3组加入引气剂，所制得的水泥涂料的抗冻性能最佳，但是第1-3组所制得的水泥涂料与对照组的综合性能均比本发明实施例1差，第4-6组数据显示，本发明水泥涂料的综合性能随着原料用量的增加而增加，具有优异的防霉性、防潮剂及抗冻性。
上述说明是针对本发明较佳可行实施例的详细说明，但实施例并非用以限定本发明的专利申请范围，凡本发明所提示的技术精神下所完成的同等变化或修饰变更，均应属于本发明所涵盖专利范围。
Claims (6)
1.一种水泥涂料，其特征在于，主要由以下重量份原料制成：水泥80-100份、聚丙烯酸酯乳液90-110份、纳米二氧化钛4-6份、偏硼酸钡2-4份、五氯苯酚钠2-3份、2，2'-二羟基-5，5'-二氯二苯基甲烷2-4份、脂肪酸钠3-5份、松香4-6份、烷基苯磺酸钠0.2-0.3份、烷基苯酚聚氧乙烯醚0.2-0.3份、糊精0.5-1.0份、葡萄糖0.5-1.0份及水45-55份。
2.根据权利要求1所述的水泥涂料，其特征在于，主要由以下重量份原料制成：水泥90份、聚丙烯酸酯乳液100份、纳米二氧化钛5份、偏硼酸钡3份、五氯苯酚钠2.5份、2，2'-二羟基-5，5'-二氯二苯基甲烷2.5份、脂肪酸钠4份、松香5份、烷基苯磺酸钠0.25份、烷基苯酚聚氧乙烯醚0.25份、糊精0.7份、葡萄糖0.7份及水50份。
3.根据权利要求1-2中任一项所述的水泥涂料的制备方法，其特征在于，具体包括以下步骤：
(1)分别按重量份准确称取纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精及葡萄糖，加入研磨机内进行研磨，过筛，备用；
(2)将步骤(1)中研磨的纳米二氧化钛、偏硼酸钡、五氯苯酚钠、2，2'-二羟基-5，5'-二氯二苯基甲烷、脂肪酸钠、松香、烷基苯磺酸钠、烷基苯酚聚氧乙烯醚、糊精、葡萄糖和水泥一起加入搅拌机内搅拌混合均匀，得到混合物，备用；
(3)按重量份准确称取聚丙烯酸酯乳液和水，加入所述混合物中，高速搅拌混合，过筛，得到所述水泥涂料；
(4)将所述水泥涂料进行性能检测，并包装，入库。
4.根据权利要求3所述的水泥涂料的制备方法，其特征在于：步骤(1)和步骤(3)中所述过筛的目数均为60-80目。
5.根据权利要求3所述的水泥涂料的制备方法，其特征在于：步骤(3)中所述高速搅拌的速度均为400-500r/min。
6.根据权利要求1-5中任一项所述的水泥涂料的使用方法，其特征在于：所述的水泥涂料分2次涂膜，待第一次涂膜表面干燥后，继续第二次涂膜，涂膜总厚度为1.0-1.5mm。