CN106987185B - 一种丙烯酸乳胶涂料 - Google Patents
一种丙烯酸乳胶涂料 Download PDFInfo
- Publication number
- CN106987185B CN106987185B CN201710213806.2A CN201710213806A CN106987185B CN 106987185 B CN106987185 B CN 106987185B CN 201710213806 A CN201710213806 A CN 201710213806A CN 106987185 B CN106987185 B CN 106987185B
- Authority
- CN
- China
- Prior art keywords
- parts
- cardanol
- latex paint
- leveling agent
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液30～75份；颜填料1～12份；分散剂1～4份；流平剂3～9份；乳化剂10～22份；消泡剂3～6份；成膜助剂2～5份；水20～40份；所述乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成。本发明各个组分具有很好的配伍性，并且各组分之间相辅相成、具有协同增效作用，本发明耐洗刷性好，耐碱性好，遮盖力强，可用水洗抹，并且本发明干燥时间较短，使用起来非常方便，同时游离甲醛含量较低，符合环保要求，因此本发明综合性能较好，为一种高性能的环保乳胶漆，其适用范围较广。
Description
技术领域
本发明属于化工生产技术领域，具体涉及一种丙烯酸乳胶涂料。
背景技术
涂料，在中国传统名称为油漆，所谓涂料是涂覆在被保护或被装饰的物体表面，并能与被涂物形成牢固附着的连续薄膜，通常是以树脂、或油、或乳液为主，添加或不添加颜料、填料，添加相应助剂，用有机溶剂或水配制而成的粘稠液体。
乳胶漆是水分散性涂料，它是以合成树脂乳液为基料，填料经过研磨分散后加入各种助剂精制而成的涂料。乳胶漆具备了与传统墙面涂料不同的众多优点，如易于涂刷、干燥迅速、漆膜耐水、耐擦洗性好等。在我国，人们习惯上把合成树脂乳液为基料，以水为分散介质，加入颜料、填料(亦称体质颜料)和助剂，经一定工艺过程制成的涂料。
随着科学技术的进步，人类生活水平的提高，人们对室内环境、空气质量的要求越来越高；同时现代工业对地坪提出了越来越严格的要求，如食品、医药等工业要求地坪不起灰，无有害挥发物，干净无尘；机械工业要求耐强烈的机械冲击，耐磨损，能长期经受叉车等车辆的辗轧，即使局部损坏也容易维修；机床、仪器仪表等工业车间地面常受到各种油类侵蚀渗漏，难以彻底清除，要求地坪耐油性好，化学工业则要求地坪能耐各种化学介质的腐蚀；因此随着涂料技术的飞快发展，为了适应不同的场合、环境，涂料需要满足相应的特性。
发明内容
本发明要解决的技术问题是提供一种丙烯酸乳胶涂料，综合性能强，适用性广泛。
为了解决上述技术问题，本发明的技术方案为：一种丙烯酸乳胶涂料，其特征在于，由以下重量份数的组分组成：
丙烯酸乳液30～75份；颜填料1～12份；分散剂1～4份；流平剂3～9份；乳化剂10～22份；消泡剂3～6份；成膜助剂2～5份；水20～40份；
所述乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成。
作为优选，所述腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为1～3：3～5：2～4。
作为优选，所述腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为2：4：3。
作为优选，所述颜填料为钛白粉、高岭土、硅藻土、云母粉以及氧化亚铜中的至少一种。
作为优选，所述分散剂为三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、以及脂肪酸聚乙二醇酯中的至少一种。
作为优选，所述的流平剂为有机硅流平剂、丙烯酸酯类流平剂、氟改性有机硅流平剂、蜡改性有机硅流平剂中至少一种。
作为优选，所述流平剂由有机硅流平剂以及丙烯酸酯类流平剂组成，所述有机硅流平剂与丙烯酸酯类流平剂的重量比为1～3:2～3。
作为优选，所述消泡剂为磷酸三丁酯、二异丙醇胺聚氧丙烯聚氧乙烯醚以及聚氧丙烯聚氧乙烯甘油醚中的至少一种。
作为优选，所述成膜助剂为丙二醇甲醚醋酸酯、苯甲醇、十二碳醇酯以及己二醇丁醚醋酸酯中的至少一种。
与现有技术相比，本发明的有益效果体现在：
(1)本发明各个组分具有很好的配伍性，并且各组分之间相辅相成、具有协同增效作用，本发明耐洗刷性好，耐碱性好，遮盖力强，可用水洗抹，并且本发明干燥时间较短，使用起来非常方便，同时游离甲醛含量较低，符合环保要求，因此本发明综合性能较好，为一种高性能的环保乳胶漆，其适用范围较广。
(2)本发明中腰果酚聚氧乙烯醚可代替壬基酚聚氧乙烯醚，辛基酚聚氧乙烯醚，仲辛基酚聚氧乙烯醚等酚类聚氧乙烯醚等石化产品，由于石化产品生物降解性差，本发明可以提高生物降解性，降低对环境的污染。
具体实施方式
下面对本发明的具体实施方式作进一步说明。在此需要说明的是，对于这些实施方式的说明用于帮助理解本发明，但并不构成对本发明的限定。此外，下面所描述的本发明各个实施方式中所涉及的技术特征只要彼此之间未构成冲突就可以相互组合。
实施例1
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液45份；钛白粉5份；高岭土5份；十二烷基硫酸钠1份；丙烯酸酯类流平剂8份；乳化剂8份；二异丙醇胺聚氧丙烯聚氧乙烯醚6份；丙二醇甲醚醋酸酯1份；水20份；
其中乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成，腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为1：5：4。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
实施例2
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液35份；硅藻土1份；云母粉0.5份；氧化亚铜0.5份；三乙基己基磷酸3份；甲基戊醇2份；丙烯酸酯类流平剂1份；氟改性有机硅流平剂1份；乳化剂20份；二异丙醇胺聚氧丙烯聚氧乙烯醚1份；聚氧丙烯聚氧乙烯甘油醚1份；苯甲醇3份；十二碳醇酯2份；水40份；
其中乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成，腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为2：3：3。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
实施例3
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液65份；硅藻土3份；氧化亚铜3份；聚丙烯酰胺1份；脂肪酸聚乙二醇酯2份；有机硅流平剂3份；丙烯酸酯类流平剂3份；乳化剂16份；聚氧丙烯聚氧乙烯甘油醚4份；苯甲醇1份；十二碳醇酯3份；水30份。
其中乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成，腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为3：3：2。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
实施例4
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液65份；硅藻土3份；氧化亚铜3份；聚丙烯酰胺1份；脂肪酸聚乙二醇酯2份；有机硅流平剂3份；丙烯酸酯类流平剂3份；乳化剂16份；聚氧丙烯聚氧乙烯甘油醚4份；苯甲醇1份；十二碳醇酯3份；水30份。
其中乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成，腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为1：3：2。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
实施例5
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液65份；硅藻土3份；氧化亚铜3份；聚丙烯酰胺1份；脂肪酸聚乙二醇酯2份；有机硅流平剂3份；丙烯酸酯类流平剂3份；乳化剂16份；聚氧丙烯聚氧乙烯甘油醚4份；苯甲醇1份；十二碳醇酯3份；水30份。
其中乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成，腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为2：4：3。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
对比例1
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液65份；硅藻土3份；氧化亚铜3份；聚丙烯酰胺1份；脂肪酸聚乙二醇酯2份；有机硅流平剂3份；丙烯酸酯类流平剂3份；聚氧丙烯聚氧乙烯甘油醚4份；苯甲醇1份；十二碳醇酯3份；水30份。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
对比例2
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液65份；硅藻土3份；氧化亚铜3份；聚丙烯酰胺1份；脂肪酸聚乙二醇酯2份；聚氧丙烯聚氧乙烯甘油醚4份；苯甲醇1份；十二碳醇酯3份；水30份。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
对比例3
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液65份；硅藻土3份；氧化亚铜3份；聚丙烯酰胺1份；脂肪酸聚乙二醇酯2份；有机硅流平剂3份；丙烯酸酯类流平剂3份；聚氧丙烯聚氧乙烯甘油醚4份；苯甲醇1份；十二碳醇酯3份；腰果酚聚氧乙烯醚16份；水30份。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
对比例4
一种丙烯酸乳胶涂料，由以下重量份数的组分组成：丙烯酸乳液65份；硅藻土3份；氧化亚铜3份；聚丙烯酰胺1份；脂肪酸聚乙二醇酯2份；有机硅流平剂3份；丙烯酸酯类流平剂3份；聚氧丙烯聚氧乙烯甘油醚4份；苯甲醇1份；十二碳醇酯3份；腰果酚磺酸盐7份；腰果酚缩水甘油醚9份；水30份。
上述乳胶涂料的制备方法，包括以下步骤：
按照配方称取各种物料，在搅拌的情况下，在水中将各物料加入，高速搅拌分散，得到所述乳胶涂料。
将实施例1～5以及对比例1～4制备得到的乳胶涂料进行各项性能指标的测定，具体测定项目参见表1，检测结果见表2。
表1
表2
以上对本发明的实施方式作了详细说明，但本发明不限于所描述的实施方式。对于本领域的技术人员而言，在不脱离本发明原理和精神的情况下，对这些实施方式进行多种变化、修改、替换和变型，仍落入本发明的保护范围内。
Claims (8)
1.一种丙烯酸乳胶涂料，其特征在于，由以下重量份数的组分组成：
丙烯酸乳液 30~75 份；颜填料 1~12 份；分散剂 1~4 份；流平剂 3~9 份；乳化剂 10~22 份；消泡剂 3~6 份；成膜助剂 2~5 份；水 20~40 份；
所述乳化剂由腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚混合制备而成；所述腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为 1~3：3~5：2~4。
2.如权利要求 1 所述的丙烯酸乳胶涂料，其特征在于，所述腰果酚聚氧乙烯醚、腰果酚磺酸盐以及腰果酚缩水甘油醚的质量比为 2：4：3。
3.如权利要求 1 所述的丙烯酸乳胶涂料，其特征在于，所述颜填料为钛白粉、高岭土、硅藻土、云母粉以及氧化亚铜中的至少一种。
4.如权利要求 1 所述的丙烯酸乳胶涂料，其特征在于，所述分散剂为三乙基己基磷酸、十二烷基硫酸钠、甲基戊醇、纤维素衍生物、聚丙烯酰胺、以及脂肪酸聚乙二醇酯中的至少一种。
5.如权利要求 1 所述的丙烯酸乳胶涂料，其特征在于，所述的流平剂为有机硅流平剂、丙烯酸酯类流平剂、氟改性有机硅流平剂、蜡改性有机硅流平剂中至少一种。
6.如权利要求 5 所述的丙烯酸乳胶涂料，其特征在于，所述流平剂由有机硅流平剂以及丙烯酸酯类流平剂组成，所述有机硅流平剂与丙烯酸酯类流平剂的重量比为 1~3:2~3。
7.如权利要求 1 所述的丙烯酸乳胶涂料，其特征在于，所述消泡剂为磷酸三丁酯、二异丙醇胺聚氧丙烯聚氧乙烯醚以及聚氧丙烯聚氧乙烯甘油醚中的至少一种。
8.如权利要求 1 所述的丙烯酸乳胶涂料，其特征在于，所述成膜助剂为丙二醇甲醚醋酸酯、苯甲醇、十二碳醇酯以及己二醇丁醚醋酸酯中的至少一种。