CN106541681B - The gluing method for adhering film of eyeglass - Google Patents
The gluing method for adhering film of eyeglass Download PDFInfo
- Publication number
- CN106541681B CN106541681B CN201611038809.9A CN201611038809A CN106541681B CN 106541681 B CN106541681 B CN 106541681B CN 201611038809 A CN201611038809 A CN 201611038809A CN 106541681 B CN106541681 B CN 106541681B
- Authority
- CN
- China
- Prior art keywords
- tac
- eyeglass
- glue
- pad pastings
- backform
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of gluing method for adhering film of eyeglass, its key points of the technical solution are that including following steps：1) flat-shaped TAC pad pastings, are selected, TAC pad pastings thickness is between 0.08 0.5mm；2), the nerve of a covering plate on TAC pad pastings, mesh specification is between 100 1000 mesh on web plate；3) glue, is poured on web plate, the glue viscosity is between 1000 10000cps；4), after web plate and TAC attachment films, using the promotion glue of scraper at the uniform velocity, glue will be made to pass through mesh and be uniformly coated on TAC pad pastings；5) glue, is subjected to semi-solid preparation drying, between 40 80 DEG C, drying time is not more than 10 minutes drying temperature；6) it is, that the baking of TAC pad pastings is curved, the another side of glue is coated with the backform top TAC pad pastings of heating, the top of backform is arcwall face, and be adapted with the arcwall face of eyeglass, and for the heating temperature of backform between 100 120 DEG C, baking bent through process control at 4 10 minutes；7), TAC pad pastings are bonded with eyeglass.This method is conducive to the uniform coating of glue, effectively improves yield rate.
Description
Technical field
The present invention relates to glasses processing and manufacturing technology, more specifically, it relates to a kind of painting bond paper facing side of eyeglass
Method.
Background technology
Have the final lens product of the number of degrees in manufacturing process, be on the basis of Optical blanks distinguish attrition process convex lens face and
Concave mirror surface makes two minute surfaces reach scheduled curved surface angle, so as to which eyeglass be made to reach scheduled diopter；And there is the polariscope of the number of degrees
Piece is to be bonded polarisation substrate on convex lens face or concave mirror surface on the basis of final lens product, so as to make eyeglass in manufacturing process
Possess polarizing function, and polarisation substrate is needed completely to be bonded with eyeglass, so as to not interfere with original diopter.
It can thus be appreciated that the pad pasting of eyeglass is fitted on the convex surface or concave surface of eyeglass, regardless of glue is coated on eyeglass
Or on pad pasting, glue can downwards slide along cambered surface, uneven so as to cause glue coating, and then lead to eyeglass pad pasting effect
Difference in addition because glue layer it is uneven due to make final lens product perspective when generate refraction, cause to scrap.
Invention content
It, should in view of the deficiencies of the prior art, the present invention intends to provide a kind of gluing method for adhering film of eyeglass
Method is conducive to the uniform coating of glue, effectively improves yield rate.
To achieve the above object, the present invention provides following technical solutions：A kind of gluing method for adhering film of eyeglass, includes
Following steps：
1）, select flat-shaped TAC pad pastings, the thickness of the TAC pad pastings is between 0.08-0.5mm；
2）, on TAC pad pastings nerve of a covering plate, the mesh specification on web plate is between 100-1000 mesh；
3）, glue is poured on web plate, the viscosity of the glue is between 1000-10000cps；
4）, after web plate and TAC attachment films using the promotion glue of scraper at the uniform velocity, glue will be made to pass through mesh and uniformly applied
It overlays on TAC pad pastings；
5）, semi-solid preparation drying will be carried out coated in the glue on TAC pad pastings, drying temperature is between 40-80 DEG C, during drying
Between be not more than 10 minutes；
6）, TAC pad pastings are dried curved, the another side of glue is coated with the backform top TAC pad pastings of heating, the top of backform is
Arcwall face, and the arcwall face of backform is adapted with the arcwall face of eyeglass, and the heating temperature of backform is dried between 100-120 DEG C
Process control is bent through at 4-10 minutes；
7）, curved TAC pad pastings will be dried be bonded with eyeglass；
Step 3 started to step 7 finishing control in 30 minutes.
The present invention is further arranged to：In step 1, the thickness of TAC pad pastings selects 0.3mm.
The present invention is further arranged to：In step 2, the mesh specification on web plate selects 200 mesh.
The present invention is further arranged to：In step 3, the viscosity of glue selects 6000-8000cps.
The present invention is further arranged to：TAC pad pastings is kept to be under horizontality during step 4 to step 5.
The present invention is further arranged to：In step 5, the semi-solid preparation drying temperature of glue is between 60-80 DEG C, drying time
It is 5 minutes.
The present invention is further arranged to：In step 6, the heating temperature of backform is 110 DEG C, and baking bent through process control at 5 minutes.
The present invention is further arranged to：In step 6 when the arcwall face of backform is adapted with the arc-shaped concave of eyeglass, step
TAC pad pastings are bonded with the arc-shaped concave of eyeglass in 7；And when the arc convex phase of the arcwall face of backform and eyeglass in step 6
Curved TAC pad pastings will first be dried by, which being needed during adaptation, in step 7, does anti-folding, then TAC pad pastings are bonded with the arc convex of eyeglass.
The present invention is further arranged to：TAC pad pastings before glue is coated, to the coated sides of TAC pad pastings using acetone or
Alcohol is cleaned；Eyeglass is cleaned the binding face of eyeglass using acetone or alcohol before being bonded with TAC pad pastings.
In conclusion the invention has the advantages that：Be conducive to improve glue coated in TAC patches by web plate gluing
Uniformity coefficient on film, so as to effectively improve yield rate during eyeglass pad pasting.
Specific embodiment
With reference to embodiment, the present invention is described in more detail.
A kind of gluing method for adhering film of eyeglass, includes following steps：
1）, select flat-shaped TAC pad pastings, the thickness of the TAC pad pastings is between 0.08-0.5mm, and TAC pad pastings
The preferred 0.3mm of thickness.
2）, on TAC pad pastings nerve of a covering plate, the mesh specification on web plate is between 100-1000 mesh；Mesh on web plate
Specification preferably 200 mesh.
3）, glue is poured on web plate, the viscosity of the glue is between 1000-10000cps；The viscosity of glue is preferred
6000-8000cps。
4）, after web plate and TAC attachment films using the promotion glue of scraper at the uniform velocity, glue will be made to pass through mesh and uniformly applied
It overlays on TAC pad pastings；
5）, semi-solid preparation drying will be carried out coated in the glue on TAC pad pastings, drying temperature is between 40-80 DEG C, during drying
Between be not more than 10 minutes；For the semi-solid preparation drying temperature of glue preferably between 60-80 DEG C, drying time is preferably 5 minutes；
6）, TAC pad pastings are dried curved, the another side of glue is coated with the backform top TAC pad pastings of heating, the top of backform is
Arcwall face, and the arcwall face of backform is adapted with the arcwall face of eyeglass, and the heating temperature of backform is dried between 100-120 DEG C
Process control is bent through at 4-10 minutes；The heating temperature of backform is preferably 110 DEG C, and baking bends through journey and is preferably controlled in 5 minutes.
7）, curved TAC pad pastings will be dried be bonded with eyeglass.
Numberical range in said program is defined by following purpose：
In step 1, the thickness size of TAC pad pastings affects later stage TAC pad pasting and dries curved processing, and TAC pad pastings are thinner, heating
Backform is easier to burn TAC pad pastings, therefore the phase dries curved processing after an action of the bowels for TAC pad pasting Yue Hou Vietnamese side；However TAC pad pastings and eyeglass are equal
Belong to light transmission medium, and refraction can be generated, therefore TAC pad pastings are thicker after different light transmission medium fittings, the refractive effect of light transmission
It is bigger, need choose facilitate molding and do not interfere with have an X-rayed this basic function size range, that is, 0.08-0.5mm it
Between.In addition the preferred 0.3mm of the thickness of TAC pad pastings is through being 0.3mm in the thickness of TAC pad pastings obtained by practical experience
When, not only ratio of briquetting is high, while the perspective of eyeglass is influenced also relatively controllable.
In step 2, when the mesh of web plate is less than 100 mesh, glue is poured on web plate and easily will directly be flowed down, and can not be controlled
Glue water coat uniformity coefficient, and the mesh of web plate be more than 1000 mesh when, the stickiness that glue carries makes it difficult to be pushed through by scraper
Mesh, therefore working efficiency is low.It is preferred that the mesh specification on web plate is 200 mesh, so as to be conducive to viscosity as 6000-8000cps
Glue be pushed on TAC pad pastings by scraper.
In step 3, when the viscosity of glue is less than 1000cps, glue is diluter, is easily directly flowed down from the mesh on web plate
It goes, is unable to control glue coating uniformity coefficient, when the viscosity of glue is more than 10000cps, glue stickiness makes it difficult to by force very much be scraped
Knife pushes through mesh, therefore working efficiency is low.Preferred viscosities are the glue of 6000-8000cps, so as to be conducive to use mesh specification
Web plate for 200 mesh is pushed to by scraper on TAC pad pastings.
In step 4, scraper pushes glue to have to remain a constant speed, and is protected so as to be conducive to the glue being coated on TAC pad pastings
It holds uniformly, and needs that TAC pad pastings is kept to be under horizontality during step 4 to step 5, can avoid because of TAC in this way
The inclination of pad pasting and make be coated in TAC pad pastings on glue slide downward, influence glue coating uniformity coefficient.
In step 5, drying temperature needs glue to reach semi-solid preparation when being less than 40 DEG C needs the time longer, and efficiency is low, and warm
Again easily by drying adhesive when degree is higher than 80 DEG C, manipulation is inconvenient, therefore between its preferred drying temperature is arranged on 60-80 DEG C,
Drying time is 5 minutes, plays the optimization manipulation of glue semi-solid preparation.
In step 6, since TAC pad pastings need to carry out web plate gluing in a flat state, and eyeglass is arcwall face, therefore
Need to be dried curved, curved operation is dried in the heating the prior art mainly adopts backform, it is noted that backform can not one in which
TAC pad pastings top to anticipated shape is needed to separate repeatedly top TAC pad pastings by secondary property, while when backform is tentative can not retract, after rollback
TAC pad pastings is easily enabled to form gauffer, are that heating backform heads on TAC pad pastings and moves a certain distance so as to scrap, therefore during normal operation
After suspend, then backform continues to move to, then suspends, until the deformation of TAC pad pastings is to anticipated shape.And the temperature of backform is less than 100
DEG C when, the temperature of backform is inadequate, and TAC pad pastings are easily pulled or even damaged, high rejection rate；When the temperature of backform is higher than 120 DEG C,
Backform easily burns relatively thin AC pad pastings, causes high rejection rate.Therefore the heating temperature of backform is preferably set as 110 DEG C,
Baking bent through process control at 5 minutes, was conducive to improve the yield rate of AC pad pastings.
It should be noted that, when the arcwall face of backform in step 6 is adapted with the arc-shaped concave of eyeglass, TAC is pasted in step 7
The arcwall face of film deformation is adapted with the arc-shaped concave of eyeglass, thus in step 7 be by TAC pad pastings be coated with the one side of glue with
The arc-shaped concave of eyeglass is bonded；And in step 6 when the arcwall face of backform is adapted with the arc convex of eyeglass, TAC pad pastings
The arcwall face of deformation is adapted with the arc convex of eyeglass, therefore is needed will first to dry curved TAC pad pastings in step 7 and done anti-folding,
It is exactly the glue one side being originally coated on the outside of arc TAC pad pastings, by way of breaking folding manually, by soft TAC pad pastings
It turns, so as to the one side coated with glue be made to become the inside of arc TAC pad pastings, then by arc TAC pad pastings coated with glue
The medial surface of water is bonded with the arc convex of eyeglass.
Control is additionally needed, is terminated since step 3 to step 7, all times need to control in 30 minutes, keep away
Exempt from glue to expose overlong time in air and reduce its stickiness, influence to bind effect.
And TAC pad pastings need to wipe the coated side of TAC pad pastings using acetone or alcohol before glue is coated
It washes, effect is for removing the impurity in the coated side of TAC pad pastings, spot even grease, is conducive to improve glue coating
In the stickiness of TAC pad pastings, avoid because of the yield rate of impurity effect eyeglass pad pasting.
Eyeglass with TAC pad pastings before being bonded simultaneously, it is also desirable to which the binding face of eyeglass is carried out using acetone or alcohol
It cleans, effect is equally for removing the impurity on the binding face of eyeglass, spot even grease, when being conducive to improve pad pasting
With the firmness of eyeglass bonding, avoid because of the yield rate of impurity effect eyeglass pad pasting.
The above is only the preferred embodiment of the present invention, and protection scope of the present invention is not limited merely to above-mentioned implementation
Example, all technical solutions belonged under thinking of the present invention all belong to the scope of protection of the present invention.It should be pointed out that for the art
Those of ordinary skill for, several improvements and modifications without departing from the principles of the present invention, these improvements and modifications
It should be regarded as protection scope of the present invention.
Claims (9)
1. a kind of gluing method for adhering film of eyeglass, it is characterized in that：Include following steps：
1）, select flat-shaped TAC pad pastings, the thickness of the TAC pad pastings is between 0.08-0.5mm；
2）, on TAC pad pastings nerve of a covering plate, the mesh specification on web plate is between 100-1000 mesh；
3）, glue is poured on web plate, the viscosity of the glue is between 1000-10000cps；
4）, after web plate and TAC attachment films using the promotion glue of scraper at the uniform velocity, glue will be made to pass through mesh and be uniformly coated in
On TAC pad pastings；
5）, will coated on TAC pad pastings glue carry out semi-solid preparation drying, drying temperature is between 40-80 DEG C, and drying time is not
More than 10 minutes；
6）, TAC pad pastings are dried curved, the another side of glue is coated with the backform top TAC pad pastings of heating, the top of backform is arc
Face, and the arcwall face of backform is adapted with the arcwall face of eyeglass, and between 100-120 DEG C, baking is bent through the heating temperature of backform
Process control was at 4-10 minutes；
7）, curved TAC pad pastings will be dried be bonded with eyeglass；
Step 3 started to step 7 finishing control in 30 minutes.
2. the gluing method for adhering film of eyeglass according to claim 1, it is characterized in that：In step 1, the thickness gauge of TAC pad pastings
Very little selection 0.3mm.
3. the gluing method for adhering film of eyeglass according to claim 1, it is characterized in that：In step 2, the mesh specification on web plate
Select 200 mesh.
4. the gluing method for adhering film of eyeglass according to claim 1, it is characterized in that：In step 3, the viscosity of glue is selected
6000-8000cps。
5. the gluing method for adhering film of eyeglass according to claim 1, it is characterized in that：It is kept during step 4 to step 5
TAC pad pastings are under horizontality.
6. the gluing method for adhering film of eyeglass according to claim 1, it is characterized in that：In step 5, the semi-solid preparation drying of glue
For temperature between 60-80 DEG C, drying time is 5 minutes.
7. the gluing method for adhering film of eyeglass according to claim 1, it is characterized in that：In step 6, the heating temperature of backform is
110 DEG C, baking bent through process control at 5 minutes.
8. the gluing method for adhering film of the eyeglass according to any one in claim 1-7, it is characterized in that：Work as top in step 6
When the arcwall face of mould is adapted with the arc-shaped concave of eyeglass, TAC pad pastings are bonded with the arc-shaped concave of eyeglass in step 7；And
In step 6 when the arcwall face of backform is adapted with the arc convex of eyeglass, curved TAC pad pastings will first be dried by, which being needed in step 7, does
Anti- folding, then TAC pad pastings are bonded with the arc convex of eyeglass.
9. the gluing method for adhering film of the eyeglass according to any one in claim 1-7, it is characterized in that：TAC pad pastings are applying
Before covering glue, the coated side of TAC pad pastings is cleaned using acetone or alcohol；Eyeglass before being bonded with TAC pad pastings,
The binding face of eyeglass is cleaned using acetone or alcohol.