CN106398493A - Container - Google Patents
Container Download PDFInfo
- Publication number
- CN106398493A CN106398493A CN201610783925.7A CN201610783925A CN106398493A CN 106398493 A CN106398493 A CN 106398493A CN 201610783925 A CN201610783925 A CN 201610783925A CN 106398493 A CN106398493 A CN 106398493A
- Authority
- CN
- China
- Prior art keywords
- weight portion
- parts
- weight
- protective paint
- metal cabinet
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a container. The surface of a metal box body of the container is coated with protective paint, and the protective paint is prepared through the following steps: 1) sequentially adding 1-2 parts of benzotriazole, 1.5 parts of maleic anhydride, 1.6 parts of fatty alcohol polyoxyethylene polyoxypropylene ether, 2.1 parts of polyethylene glycol and 9 parts of white latex into 26 parts of deionized water, and uniformly stirring; 2) then sequentially adding 13 parts of water-based alkyd resin, 1.3 parts of diethylenetriamine, 0.8 part of dodecyl trimethyl ammonium sulfate, 0.8 part of sodium benzoate, 2.6 parts of acrylic acid, continuing stirring till sufficient and uniform mixing to obtain the protective paint. The surface of the metal box body of the container is coated with the protective paint, so that long-time use of the container can be guaranteed.
Description
Technical field
The present invention relates to a kind of container.
Background technology
Existing container, antirust, corrosion-resistant, antioxidation, the weather resistance of its metal cabinet have much room for improvement, and affect container
Life-time service.
Content of the invention
It is an object of the invention to provide a kind of container, its metal cabinet surface-coated has protective paint, makes metal cabinet
There is excellent antirust, corrosion-resistant, antioxidation, weather resistance, thus ensureing container energy life-time service.
For achieving the above object, the technical scheme is that a kind of container of design, including metal cabinet, this metal box
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) by 1～2 weight portion BTA, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxies third
Alkene ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Preferably, container, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 1 weight portion BTA, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Preferably, container, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 2 weight portion BTAs, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Preferably, container, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint passes through
Prepared by following steps：
1) by 1.2 weight portion BTAs, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Advantages of the present invention and having the beneficial effects that：There is provided a kind of container, its metal cabinet surface-coated has protective paint,
Metal cabinet is made to have excellent antirust, corrosion-resistant, antioxidation, weather resistance, thus ensureing container energy life-time service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is：
Embodiment 1
Container, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 1～2 weight portion BTA, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxies third
Alkene ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Embodiment 2
Container, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 1 weight portion BTA, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Embodiment 3
Container, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 2 weight portion BTAs, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
Embodiment 4
Container, including metal cabinet, this metal cabinet surface is covered with protective paint, and described protective paint is as follows
Preparation：
1) by 1.2 weight portion BTAs, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion aliphatic alcohol polyethenoxy polyoxypropylenes
Ether, 2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecane are put into again successively
Base trimethyl ammonium sulfate, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, are obtained
Protective paint.
The container of the various embodiments described above, its metal cabinet surface-coated has protective paint, so that metal cabinet is had excellent
Antirust, corrosion-resistant, antioxidation, weather resistance, thus ensure container energy life-time service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. it is characterised in that including metal cabinet, this metal cabinet surface is covered with protective paint to a kind of container, described protection
Paint is made by the steps：
1) by 1～2 weight portion BTA, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether,
2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecyl three are put into again successively
Methylsulfuric acid ammonium, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
2. container according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with
Protective paint, described protective paint is made by the steps：
1) by 1 weight portion BTA, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether, 2.1
Weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecyl three are put into again successively
Methylsulfuric acid ammonium, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
3. container according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with
Protective paint, described protective paint is made by the steps：
1) by 2 weight portion BTAs, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether, 2.1
Weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecyl three are put into again successively
Methylsulfuric acid ammonium, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.
4. container according to claim 1 is it is characterised in that include metal cabinet, this metal cabinet surface is covered with
Protective paint, described protective paint is made by the steps：
1) by 1.2 weight portion BTAs, 1.5 weight portion cis-butenedioic anhydrides, 1.6 weight portion Fatty alcohol polyoxyethylene polyoxypropylene ether,
2.1 weight portion Polyethylene Glycol, 9 weight portion white glue with vinyl put in 26 parts by weight of deionized water successively, stir；
2) 13 weight portion aqueous alkide resins, 1.3 weight portion diethylenetriamines, 0.8 weight portion dodecyl three are put into again successively
Methylsulfuric acid ammonium, 0.8 parts by weight sodium, 2.6 parts by weight of acrylic acid, continue stirring, to being sufficiently mixed uniformly, protection are obtained
Paint.