CN106381034A - Active cutting edge used for wire rod mill - Google Patents
Active cutting edge used for wire rod mill Download PDFInfo
- Publication number
- CN106381034A CN106381034A CN201610780072.1A CN201610780072A CN106381034A CN 106381034 A CN106381034 A CN 106381034A CN 201610780072 A CN201610780072 A CN 201610780072A CN 106381034 A CN106381034 A CN 106381034A
- Authority
- CN
- China
- Prior art keywords
- weight
- weight portion
- parts
- protective paint
- weight parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an active cutting edge used for a wire rod mill, and the surface of a metal main body is coated with a protection paint. The protection paint is prepared by the following steps: 1) placing 1-2 weight parts of powdered steatile, 0.5 weight parts of mica iron oxide, 1.2 weight parts of alpha-olefin sulfonate, 2.6 weight parts of polyacrylic acid, 13 weight parts of polycarbonate in 20 weight parts of deionized water, and uniformly stirring the materials; and 2) placing 6 weight parts of silicone resin, 1.8 weight parts of methyl salicylate, 2.3 weight parts of alkyl glycoside, 1.9 weight parts of polyoxyethylene octylphenol ether, and 2.3 weight parts of sodium acetate, and continuously stirring the materials until the materials are fully and uniformly mixed to obtain the protection paint. According to the active cutting edge used for the wire rod mill, the surface of a metal main body is coated with the protection paint, and the protection paint can guarantee long-term usage of the active cutting edge used for the wire rod mill.
Description
Technical field
The present invention relates to a kind of rod-rolling mill activity cutting edge.
Background technology
With movable cutting edge, the heat-resisting, antioxidation of its metal master, antirust, decay resistance need to be changed for existing rod-rolling mill
Enter, the impact rod-rolling mill life-time service of movable cutting edge.
Content of the invention
It is an object of the invention to provide a kind of rod-rolling mill is with movable cutting edge, its metal body surface is coated with protection
Paint, makes metal master have excellent heat-resisting, antioxidation, antirust, decay resistance, thus ensureing rod-rolling mill activity cutting edge
Can life-time service.
For achieving the above object, the technical scheme is that a kind of design rod-rolling mill activity cutting edge, including metal
Main body, this metal body surface is covered with protective paint, and described protective paint is made by the steps：
1) by 1～2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weights
Amount part polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, rod-rolling mill activity cutting edge, including metal master, this metal body surface is covered with protective paint, institute
State protective paint to be made by the steps：
1) by 1 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions
Polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, rod-rolling mill activity cutting edge, including metal master, this metal body surface is covered with protective paint, institute
State protective paint to be made by the steps：
1) by 2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions
Polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Preferably, rod-rolling mill activity cutting edge, including metal master, this metal body surface is covered with protective paint, institute
State protective paint to be made by the steps：
1) by 1.2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight
Part polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Advantages of the present invention and having the beneficial effects that：A kind of rod-rolling mill activity cutting edge, its metal body surface are provided
Being coated with protective paint, making metal master have excellent heat-resisting, antioxidation, antirust, decay resistance, thus ensureing rod-rolling mill
With movable cutting edge energy life-time service.
The performance of " protective paint " and purposes are determined by its component and proportioning, and the different component meeting in " protective paint "
Influence each other, component and its proportioning can determine the final performance of " protective paint ", such as fruit component and its proportioning be not mutually coordinated, single
The beneficial effect that component is brought, even can be eliminated by other components abatement, when serious, different component is mutually conflicted, and rises
Less than whole synthesis effect, produce negative interaction and substandard products.The present invention passes through a large amount of creative works, repeatedly verifies, obtains " protection
The optimal component of paint " and proportioning so that multiple component combine, mutually coordinated and produce positive comprehensive effect.
Specific embodiment
With reference to embodiment, the specific embodiment of the present invention is further described.Following examples are only used for more
Plus clearly demonstrate technical scheme, and can not be limited the scope of the invention with this.
The technical scheme that the present invention is embodied as is：
Embodiment 1
Rod-rolling mill activity cutting edge, including metal master, this metal body surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 1～2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weights
Amount part polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 2
Rod-rolling mill activity cutting edge, including metal master, this metal body surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 1 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions
Polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 3
Rod-rolling mill activity cutting edge, including metal master, this metal body surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions
Polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
Embodiment 4
Rod-rolling mill activity cutting edge, including metal master, this metal body surface is covered with protective paint, described protective paint
It is made by the steps：
1) by 1.2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight
Part polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weights are put into again successively
Amount part OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
The rod-rolling mill of the various embodiments described above is coated with protective paint, is made metal master with movable cutting edge, its metal body surface
Body has excellent heat-resisting, antioxidation, antirust, decay resistance, thus ensureing rod-rolling mill activity cutting edge energy life-time service.
The above is only the preferred embodiment of the present invention it is noted that ordinary skill people for the art
For member, on the premise of without departing from the technology of the present invention principle, some improvements and modifications can also be made, these improvements and modifications
Also should be regarded as protection scope of the present invention.
Claims (4)
1. with movable cutting edge it is characterised in that including metal master, this metal body surface is covered with protection to a kind of rod-rolling mill
Paint, described protective paint is made by the steps：
1) by 1～2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions
Polyacrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weight portions are put into again successively
OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
2. rod-rolling mill according to claim 1 uses movable cutting edge it is characterised in that including metal master, this metal master
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) by 1 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions poly- third
Olefin(e) acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weight portions are put into again successively
OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
3. rod-rolling mill according to claim 1 uses movable cutting edge it is characterised in that including metal master, this metal master
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) by 2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions poly- third
Olefin(e) acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weight portions are put into again successively
OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.
4. rod-rolling mill according to claim 1 uses movable cutting edge it is characterised in that including metal master, this metal master
Body surface face is covered with protective paint, and described protective paint is made by the steps：
1) 1.2 weight portion Pulvis Talci, 0.5 parts by weight mica ferrum oxide, 1.2 weight portion α-sodium olefin sulfonate, 2.6 weight portions are gathered
Acrylic acid, 13 weight portion polycarbonate put in 20 parts by weight of deionized water successively, stir；
2) 6 weight portion silicones, 1.8 weight portion cresotic acids, 2.3 part by weight of alkylglycoside, 1.9 weight portions are put into again successively
OPEO, 2.3 parts by weight acetic acid sodium, continue stirring, uniform to being sufficiently mixed, prepared protective paint.