CN106186693A - A kind of ceramic glaze - Google Patents
A kind of ceramic glaze Download PDFInfo
- Publication number
- CN106186693A CN106186693A CN201610531231.4A CN201610531231A CN106186693A CN 106186693 A CN106186693 A CN 106186693A CN 201610531231 A CN201610531231 A CN 201610531231A CN 106186693 A CN106186693 A CN 106186693A
- Authority
- CN
- China
- Prior art keywords
- parts
- glaze
- ceramic glaze
- ceramic
- modified
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A kind of ceramic glaze, it is made up of the raw material of following parts by weight: ultrawhite Zirconium orthosilicate. 6 11 parts, calcined alumina 47 parts, albite 6 12 parts, organic-silicon-modified resin 8 15 parts, aqueous auxiliary rheological agents 3.5 6 parts, calcium carbonate 24 parts, strontium carbonate 6 11 parts, 9 14 parts of quartz, aluminium sesquioxide 6 10 parts, zinc oxide 79 parts, 3.5 5 parts of modified verdelite powder, cellulose ether 3.5 4.6 parts, water reducer 69 parts, ultra fine sand 7 12 parts, calcined kaolin 8 12 parts, magnesium oxide 1.5 2.6 parts.The invention has the beneficial effects as follows: the ceramic glaze of the present invention, improving the heat insulation and preservation effect of pottery, clear color, and anti-wear performance preferable, temperature adaptation scope is wide.
Description
Technical field
The present invention relates to a kind of ceramic glaze.
Background technology
Construction sanitary ceramic industry focuses on using advanced glaze technology very much, domestic occurred large quantities of professional very
Strong ceramic glaze and preparing ceramic clinker, colorant company.Glaze used in construction sanitary ceramic product is more and more rich and varied, mesh
The glaze product that front most pottery enterprise uses.Existing ceramic glaze can be as follows with rough classification with purposes according to classification: 1, lead glaze
And leadless glaze；2, raw glaze and fritted glaze；3, once-firing or twice firing glaze；4, ceramic tile, tableware, sanitary ceramics with
Electroceramics glaze；5, by leaching glaze, the glaze spraying of enameling method division, glaze is watered；6, high-temperature glaze and low temperature glaze；7, highly expanded glaze and low
Expand glaze；8, firing atmosphere oxidizing flame, neutral flame and reducing flame；9, coloured glaze and colourless glaze；10, clear frit and opaque glaze
；11, bright glaze, mat glaze, semi-mat glaze or figure glaze etc..Along with the development of society, people are for the requirement of ceramic glaze
More and more higher, need existing glaze is further improved, improve its properties of product.
Summary of the invention
For the deficiencies in the prior art, the problem to be solved in the present invention is to provide a kind of ceramic glaze, improve pottery every
Hot heat insulation effect, clear color, and anti-wear performance are preferable, and temperature adaptation scope is wide.
For solving prior art problem, the technical scheme that the present invention provides is, a kind of ceramic glaze, it is by following weight portion
The raw material of number is made:
Ultrawhite Zirconium orthosilicate. 6-11 part, calcined alumina 4-7 part, albite 6-12 part, organic-silicon-modified resin 8-15 part, aqueous flow
Become auxiliary agent 3.5-6 part, calcium carbonate 2-4 part, strontium carbonate 6-11 part, quartz 9-14 part, aluminium sesquioxide 6-10 part, zinc oxide 7-9
Part, modified verdelite powder 3.5-5 part, cellulose ether 3.5-4.6 part, water reducer 6-9 part, ultra fine sand 7-12 part, calcined kaolin
8-12 part, magnesium oxide 1.5-2.6 part.
The invention has the beneficial effects as follows: the ceramic glaze of the present invention, the heat insulation and preservation effect of raising pottery, clear color,
And anti-wear performance is preferable, temperature adaptation scope is wide.
Detailed description of the invention
Embodiment 1
A kind of ceramic glaze, it is made up of the raw material of following parts by weight:
Ultrawhite Zirconium orthosilicate. 6 parts, calcined alumina 4 parts, albite 6 parts, organic-silicon-modified resin 8 parts, aqueous auxiliary rheological agents 3.5
Part, calcium carbonate 2 parts, strontium carbonate 6 parts, 9 parts of quartz, aluminium sesquioxide 6 parts, zinc oxide 7 parts, 3.5 parts of modified verdelite powder, fiber
3.5 parts of ether of element, water reducer 6 parts, ultra fine sand 7 parts, calcined kaolin 8 parts, magnesium oxide 1.5 parts.
Embodiment 2
A kind of ceramic glaze, it is made up of the raw material of following parts by weight:
Ultrawhite Zirconium orthosilicate. 11 parts, calcined alumina 7 parts, albite 12 parts, organic-silicon-modified resin 15 parts, aqueous auxiliary rheological agents 6
Part, calcium carbonate 4 parts, strontium carbonate 11 parts, 14 parts of quartz, aluminium sesquioxide 10 parts, zinc oxide 9 parts, 5 parts of modified verdelite powder, fine
Dimension 4.6 parts of ether of element, water reducer 9 parts, ultra fine sand 12 parts, calcined kaolin 12 parts, magnesium oxide 2.6 parts.
Claims (1)
1. a ceramic glaze, it is characterised in that: it is made up of the raw material of following parts by weight:
Ultrawhite Zirconium orthosilicate. 6-11 part, calcined alumina 4-7 part, albite 6-12 part, organic-silicon-modified resin 8-15 part, aqueous flow
Become auxiliary agent 3.5-6 part, calcium carbonate 2-4 part, strontium carbonate 6-11 part, quartz 9-14 part, aluminium sesquioxide 6-10 part, zinc oxide 7-9
Part, modified verdelite powder 3.5-5 part, cellulose ether 3.5-4.6 part, water reducer 6-9 part, ultra fine sand 7-12 part, calcined kaolin
8-12 part, magnesium oxide 1.5-2.6 part.