CN105239413A - Application of ecological auxiliary in finishing of cashmere sweater - Google Patents
Application of ecological auxiliary in finishing of cashmere sweater Download PDFInfo
- Publication number
- CN105239413A CN105239413A CN201510772308.2A CN201510772308A CN105239413A CN 105239413 A CN105239413 A CN 105239413A CN 201510772308 A CN201510772308 A CN 201510772308A CN 105239413 A CN105239413 A CN 105239413A
- Authority
- CN
- China
- Prior art keywords
- cashmere sweater
- agent
- weight
- cashmere
- oven dry
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses application of an ecological auxiliary in finishing of a cashmere sweater. The ecological auxiliary is prepared; firstly, an agent B is evenly sprayed on the cashmere sweater, the spraying weight is 0.2 time that of the cashmere sweater, and then the cashmere sweater is sealed for 7-9 hours at 25-28 EDG C and then dried for use; secondly, an agent A is evenly sprayed on the dried cashmere sweater, the spraying weight is 0.05-0.08 time that of the cashmere sweater, and then the cashmere sweater is subjected to still standing for 320-380 min at 38 DEG C and then dried at 30 DEG C, wherein the constant temperature and ventilation are maintained in the still standing process; residues on the surface of fabric are removed through deionized water, and the cashmere sweater is baked for 5 s at 60 DEG C and then dried at 30 DEG C.
Description
Technical field
The present invention relates to the application of a kind of ecological auxiliary agent on cashmere sweater arranges, belong to textile technology field.
Background technology
Cashmere sweater take goat cashmere as the knitting clothes of raw material.Be divided into slubbing knitting and spinning knitting two kinds according to yarn classification, pure cashmere and cashmere blending two kinds can be divided into according to material rate.Popular style mostly is " v " V-neck V pullover, cardigan, crew neck blouse etc.There is the natural colour such as white, blue or green, purple of goat cashmere itself, also can dye.Feel is soft, soft and smooth, glossy, and warmth retention property is good, comfortable and easy to wear, but intensity is poor, and anti-microbial property is also poor.
Afterfinish method is the key factor affecting cashmere pin performance.Along with the raising day by day of living standard, the health care consciousness of people to textile garment strengthens day by day, has the knitwear wide market next to the skin of anti-microbial property.Antibacterial fabric processing is main adopts 2 kinds of technological approaches: one is add antiseptic before fibre spinning is shaped, and carries out modification and obtains anti-bacterial fibre; Two is use antiseptic, by padding, flood, coating, the method finish fabric such as spraying, and acquisition antibacterial effect.Direct its durable antibacterial effect of employing anti-bacterial fibre, but be only applicable to synthetic fiber and regenerated fiber, technical requirement is high, complicated operation, and cost is higher.Use antibacterial finishing agent is simple and convenient, and be applicable to most of fiber textile, cost is low, but whether the persistence of anti-microbial property can be guaranteed, and whether affects the wearability of fabric, has become the problem of insider's primary study.
The present invention aims to provide the application of a kind of ecological auxiliary agent on cashmere sweater arranges, and described ecological auxiliary agent comprises compound live bacteria agent, native protein, natural polysaccharide etc., not containing any chemical reagent, use simple, the cashmere sweater after arrangement has good antibacterial effect, and can also ANTIPILLING, make the feel of cashmere sweater finer and smoother, have gloss, mechanical strength strengthens, upper dye, on whiteness then without any impact.
Summary of the invention
Based on the technical problem that background technology exists, the invention provides the application of a kind of ecological auxiliary agent on cashmere sweater arranges, described ecological auxiliary agent comprises compound live bacteria agent, native protein, natural polysaccharides etc., not containing any chemical reagent, use simple, cashmere sweater after arrangement has good antibacterial effect, and can also ANTIPILLING, makes the feel of cashmere sweater finer and smoother, there is gloss, mechanical strength strengthens, upper dye, on whiteness then without any impact.
Technical scheme of the present invention is as follows:
The application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:0.3:0.5 is mixed with 1-1.5*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.0-1.5%, pigskin collagen 0.6=0.9%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 25-28 DEG C puts 7-9 hour, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.05-0.08 times of the weight of cashmere sweater, leaves standstill 320-380min at being then placed in 38 DEG C, dries in the processes of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
Usefulness of the present invention is:
The invention provides the application of a kind of ecological auxiliary agent on cashmere sweater arranges, described ecological auxiliary agent comprises compound live bacteria agent, native protein, natural polysaccharide etc., not containing any chemical reagent, use simple, the cashmere sweater after arrangement has good antibacterial effect, and can also ANTIPILLING, allow the finer and smoother softness of the feel of cashmere sweater, have gloss, mechanical strength strengthens, upper dye, on whiteness then without any impact.
Detailed description of the invention
Embodiment 1:
The application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:0.3:0.5 is mixed with 1*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.5%, pigskin collagen 0.6%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 28 DEG C puts 7 hours, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.08 times of the weight of cashmere sweater, leaves standstill 320min at being then placed in 38 DEG C, dries in the process of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
Embodiment 2:
The application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:0.3:0.5 is mixed with 1.5*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.0%, pigskin collagen 0.9%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 25 DEG C puts 9 hours, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.05 times of the weight of cashmere sweater, leaves standstill 380min at being then placed in 38 DEG C, dries in the process of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
Embodiment 3:
The application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:0.3:0.5 is mixed with 1.1*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.4%, pigskin collagen 0.7%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 27 DEG C puts 8 hours, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.07 times of the weight of cashmere sweater, leaves standstill 330min at being then placed in 38 DEG C, dries in the process of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
Embodiment 4:
The application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:0.3:0.5 is mixed with 1.4*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.2%, pigskin collagen 0.8%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 26 DEG C puts 7 hours, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.06 times of the weight of cashmere sweater, leaves standstill 370min at being then placed in 38 DEG C, dries in the process of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
Embodiment 5 contrast test:
In the present invention, the collocation of preliminary treatment and microbial inoculum is all extremely important, if the ratio of not carrying out preliminary treatment or microbial inoculum is not right, all can have a strong impact on effect, infers and serves certain synergy between each parameter.
Comparative example 1: carry out preliminary treatment without B agent
The application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:0.3:0.5 is mixed with 1.2*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.3%, pigskin collagen 0.9%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 25 DEG C puts 8 hours, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.05 times of the weight of cashmere sweater, leaves standstill 340min at being then placed in 38 DEG C, dries in the process of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
Comparative example 2: the ratio of bacterial strain is not right
The application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:1:1 is mixed with 1.3*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.1%, pigskin collagen 0.6%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 28 DEG C puts 9 hours, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.07 times of the weight of cashmere sweater, leaves standstill 360min at being then placed in 38 DEG C, dries in the process of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
Embodiment 6: index is tested and assessed
The index of the cashmere sweater that embodiment 1-5 obtains is tested, as follows:
Cashmere weight-loss ratio measures:
According to fabric regain, calculate the treated front constant dry mass w0 of sample; The constant dry mass w1 of fabric after precise process, is calculated as follows the weight-loss ratio before and after fabric ferment treatment:
Weight-loss ratio=(w0-w1)/w0 × 100%
The pilling resistance of cashmere knit goods detects and adopts GB/T4802.3-2008 balling-up case method.
Evaluate the persistence of antibacterial fabric performance, mainly antibiotic fabric is carried out to the wash durability test of anti-microbial property.Antibiotic fabric decantation test with reference to the simplification wash conditions of appendix C in " FZ/T73023-2006 antibiosis knitting product " and program, to fabric washing to be measured 50 times.
Antibiotic fabric performance test methods is with reference to the succusion of Appendix D in " FZ/T73023-2006 antibiosis knitting product ".Succusion be imitate human body wear condition, make bacterium under oscillating condition with anti-microbial agent in clothes, by calculate bacterial reduction, determine a kind of method of anti-microbial property size.Succusion testing procedure is: put into by sample to be tested containing certain density bacterium (staphylococcus aureus bacterial classification) nutrient solution, then sample is placed on reciprocating oscillator, at (24 ± 1) DEG C, with the velocity fluctuation 18h of 150r/min, sample fabric is fully contacted by vibration with bacterium liquid after, 24h is cultivated in (37 ± 1) DEG C biochemical cultivation case, measure the clump count of bacterium before and after vibration, carry out quantitative assessment antibacterial effect by method for counting colonies.
The calculating of succusion test anti-microbial property:
Bacteriostasis rate (%)=(A-B)/A × 100%
In formula (1): A is clump count after standard blank sample vibration 18h; B is clump count after sample to be tested vibration 18h.
Table 1 detects for producing to embodiment 1-5 the cashmere sweater obtained the result obtained.
Table 1 performance measurement
This detects data only for above-mentioned detection sample.
As can be seen here, the invention provides the application of a kind of ecological auxiliary agent on cashmere sweater arranges, described ecological auxiliary agent comprises compound live bacteria agent, native protein, natural polysaccharides etc., not containing any chemical reagent, use simple, cashmere sweater after arrangement has good antibacterial effect, and can also ANTIPILLING, makes the feel of cashmere sweater finer and smoother, there is gloss. in addition, the mechanical strength also observing cashmere sweater after arranging strengthens, upper dye, on whiteness then without any impact.
The above; be only the present invention's preferably detailed description of the invention; but protection scope of the present invention is not limited thereto; anyly be familiar with those skilled in the art in the technical scope that the present invention discloses; be equal to according to technical scheme of the present invention and inventive concept thereof and replace or change, all should be encompassed within protection scope of the present invention.
Claims (2)
1. the application of ecological auxiliary agent on cashmere sweater arranges, its step is as follows:
(1) ecological auxiliary agent is prepared:
A agent: will addicted to sour micrococcus, bacillus subtilis, Candida is that 1:0.3:0.5 is mixed with 1-1.5*10 according to bacterial strain number ratio
5bacteria suspension, described bacteria suspension also contains, according to mass percent, the trehalose of 0.3%, the stachyose of 0.2%, the nano titanium oxide of 0.05%;
B agent: according to mass percent, fibroin albumen 1.0-1.5%, pigskin collagen 0.6=0.9%, water soluble chitosan 0.2%, 0.08% nano titanium oxide;
(2) arrange:
First B agent be evenly sprayed on cashmere sweater, the weight of sprinkling is 0.2 times of the weight of cashmere sweater, vexedly at being then placed in 25-28 DEG C puts 7-9 hour, 30 DEG C of oven dry, for subsequent use;
Then A agent be evenly sprayed on the cashmere sweater of oven dry, the weight of sprinkling is 0.05-0.08 times of the weight of cashmere sweater, leaves standstill 320-380min at being then placed in 38 DEG C, dries in the processes of leaving standstill for 30 DEG C and keeps constant temperature and ventilation;
(3) with washed with de-ionized water fabric face residue, 60 DEG C cure 5s after, 30 DEG C of oven dry.
2. the application of ecological auxiliary agent according to claim 1 on cashmere sweater arranges, is characterized in that:
The molecular weight of described nano titanium oxide is 50-100nm.