CN104974601A - Sodium carboxymethyl cellulose multicolor paint - Google Patents
Sodium carboxymethyl cellulose multicolor paint Download PDFInfo
- Publication number
- CN104974601A CN104974601A CN201510465510.0A CN201510465510A CN104974601A CN 104974601 A CN104974601 A CN 104974601A CN 201510465510 A CN201510465510 A CN 201510465510A CN 104974601 A CN104974601 A CN 104974601A
- Authority
- CN
- China
- Prior art keywords
- parts
- mucine
- multicolor finish
- xylo
- pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a sodium carboxymethyl cellulose multicolor paint which is prepared from distilled water, a pigment, calcium carbonate, ammonium hydroxide, n-octanol, sodium naphthalene sulfonate, silicon dioxide, titanium white, sodium pyrophosphate and nonaphenyl polyethylene hexanediol ether. The product has the advantages of bright color, high smoothness and favorable dispersity. The solid content is 10-50%, and the coating weight is 0.15-0.35. The drying time is 7-13 hours, the storage time is 8-12 months, and the paint can be widely produced and continuously substituted for the existing materials.
Description
Technical field
The present invention relates to technical field of coatings, particularly relate to a kind of Xylo-Mucine multicolor finish.
Background technology
Multicolor finish is mainly used in copys stone material effect, so also known as liquid stone, is also local horizon exterior coating.Be made up of inconsistent two phase compositions, wherein a phase dispersion medium is external phase, and another is disperse phase mutually, during application, by disposable spray finishing, just can obtain luxurious, attractive in appearance, colorful pattern.Water-water colorful marble paint rich color is colorful, and special color can be provided on request and emulation property high, it is unrestricted in designer, can change shape arbitrarily according to the intention of Designers.
Multicolor finish is mainly used in copys stone material effect, so also known as liquid stone, is also local horizon exterior coating.Be made up of inconsistent two phase compositions, wherein a phase dispersion medium is external phase, and another is disperse phase mutually, during application, by disposable spray finishing, just can obtain luxurious, attractive in appearance, colorful pattern.This pattern formed by disposable spray finishing is completely different from the method being completed the multicolour pattern that could be formed by multiple working procedure successively.
Granite is a kind of natural stone material, belongs to magmatite, is widely used in the outdoor facing of building.But granite cost is very expensive, and have public danger at external wall as facing, not easily big area or external wall of high-rise building are shown consideration for and are established use.Therefore, in order to buildings can reach the luxurious effect of granitic outward appearance, imitated granitic material is constantly gushed out, due to granitic color many opposite sex, that imitating technology is brought is very complicated, people need a kind of imitated easy coating to simplify the complicacy of imitating technology, in this context, multicolor finish arises at the historic moment.
After coating, due to uneven, there is dispersion and multiple color decorative pattern can be obtained, stereoscopic sensation is strong, gloss is graceful, appearance tactile impression is good relief-type coating.The characteristic such as it has acid and alkali-resistance, water-fastness, anti-pollution, wear-resisting, bonding strength is high, can be applied to plaster, cement, asbestos, brick, wood, metallic surface.Which field is does water-water multicolor finish mainly used in? its range of application that a lot of people can feel not is very wide, actually this is not so, lithotome is long at the applicating history in building decoration field, firmly getting architect and user's favor with its noble, natural, simple and unsophisticated, luxurious style, is also one of important symbol of high-end buildings external image.
Oil-in-water-type, water-in-oil-type, oily oil-in and water-in-water type four class can be divided into by its medium condition, best with water-in-oil-type package stability, and most widely used, water-in-water type environmental protection multicolor finish is being developed in practicality.The colorful marble paint of water-water is water-based coating, meet environmental requirement, non-harmful product during construction, because containing supra polymer element, construct after complete drying, have wear-resistant, wash away the characteristic changed with uviolizing, antistatic, high temperature resistant, acid rain resistant, waterproof, anti-be full of cracks, high strength, resistance to long-term multiple weather condition, property retention is constant, is easy to maintenance and cleaning, self-cleaning is excellent, multicolour once sprays, constructs easily, is a kind of excellent water tolerance, weathering resistance, a coating material.
Multicolor finish is the new decorative material for building of beautifying hotel, movie theatre, entertainment place, shop, office building, house etc.Water-water multicolor finish is a kind of series product of Environmental Protective Water-paint system, is born for meeting the building external paint market of development now.That the pigment of modified resin and the good stability obtained with High-tech Research And Development is made, full water-based, the colorful granite coating of disposable spray finishing, the color produced is more true to nature, more durable, by the granite sample that Designers provides, emulator can reach 99%, is the best product of alternative exterior wall grouan, therefore also known as liquid stone.
Multicolor finish is mixed into the two or more different colours of liquid or gel, size and different band look particulate in basic coating, the suspended dispersion coating of a kind of compound of composition.Water-water multicolor finish is a kind of series product of Environmental Protective Water-paint system, is born for meeting the building external paint market of development now.That the pigment of modified resin and the good stability obtained with High-tech Research And Development is made, full water-based, the colorful granite coating of disposable spray finishing, the color produced is more true to nature, more durable, by the granite sample that Designers provides, emulator can reach 99%, is the best product of alternative exterior wall grouan.
Summary of the invention
The invention provides the multicolor finish that a kind of fast drying and period of storage are long, solve the technical problems such as the dry slow and period of storage of existing multicolor finish is short.
The present invention is by the following technical solutions: a kind of Xylo-Mucine multicolor finish, it is as follows that mass fraction proportioning pressed by its raw material: distilled water 100 parts, pigment 1-5 part, calcium carbonate 8-12 part, ammonium hydroxide 0.8-1.2 part, n-Octanol 1-5 part, sodium naphthalene sulfonate 0.5-2.5 part, silicon-dioxide 8-12 part, titanium dioxide 10-30 part, trisodium phosphate 6-10 part, nonyl phenyl polyethylene hexanediol ether 0.2-0.8 part.
As a preferred technical solution of the present invention: it is as follows that mass fraction proportioning pressed by the raw material of described Xylo-Mucine multicolor finish: distilled water 100 parts, pigment 2-4 part, calcium carbonate 9-11 part, ammonium hydroxide 0.9-1.1 part, n-Octanol 2-4 part, sodium naphthalene sulfonate 1-2 part, silicon-dioxide 9-11 part, titanium dioxide 15-25 part, trisodium phosphate 7-9 part, nonyl phenyl polyethylene hexanediol ether 0.4-0.6 part.
As a preferred technical solution of the present invention: it is as follows that mass fraction proportioning pressed by the raw material of described Xylo-Mucine multicolor finish: distilled water 100 parts, pigment 3 parts, 10 parts, calcium carbonate, 1 part, ammonium hydroxide, n-Octanol 3 parts, sodium naphthalene sulfonate 1.5 parts, silica 10 part, titanium dioxide 20 parts, trisodium phosphate 8 parts, nonyl phenyl polyethylene hexanediol ether 0.5 part.
As a preferred technical solution of the present invention: described pigment adopts red iron oxide or phthalocyanine blue.
Beneficial effect: a kind of Xylo-Mucine multicolor finish of the present invention adopts above technical scheme compared with prior art, has following technique effect: 1, product colour is bright-coloured, smooth, good dispersity; 2, solid divides 10-50%, and 0.15-0.35 is measured in coating; 3, time of drying 7-13h, 8-12 month storage period, can the widespread production not division of history into periods for current material.
Embodiment
Below in conjunction with example, the invention will be further described, and embodiment, only for the present invention will be described, does not form the restriction to right, and other alternative means that it may occur to persons skilled in the art that, all within the scope of the claims in the present invention.
Embodiment 1:
Distilled water 100 parts is taken according to mass fraction proportioning, red iron oxide 1 part, 8 parts, calcium carbonate, 0.8 part, ammonium hydroxide, n-Octanol 1 part, sodium naphthalene sulfonate 0.5 part, silicon-dioxide 8 parts, titanium dioxide 10 parts, trisodium phosphate 6 parts, nonyl phenyl polyethylene hexanediol ether 0.2 part, is uniformly mixed in a kettle..
Product colour is bright-coloured, smooth, good dispersity; Solid divides 10%, and coating measures 0.15; Time of drying 13h, 8 months storage periods.
Embodiment 2:
Distilled water 100 parts is taken according to mass fraction proportioning, red iron oxide 5 parts, 12 parts, calcium carbonate, 1.2 parts, ammonium hydroxide, n-Octanol 5 parts, sodium naphthalene sulfonate 2.5 parts, silica 12 parts, titanium dioxide 30 parts, trisodium phosphate 10 parts, nonyl phenyl polyethylene hexanediol ether 0.8 part, is uniformly mixed in a kettle..
Product colour is bright-coloured, smooth, good dispersity; Solid divides 10%, and coating measures 0.15; Time of drying 13h, 8 months storage periods.
Embodiment 3:
Distilled water 100 parts is taken, red iron oxide 2 parts, 9 parts, calcium carbonate, 0.9 part, ammonium hydroxide according to mass fraction proportioning, n-Octanol 2 parts, sodium naphthalene sulfonate 1 part, silicon-dioxide 9 parts, titanium dioxide 15 parts, trisodium phosphate 7 parts, nonyl phenyl polyethylene hexanediol ether 0.4 part, is uniformly mixed in a kettle..
Product colour is bright-coloured, smooth, good dispersity; Solid divides 30%, and coating measures 0.25; Time of drying 10h, 10 months storage periods.
Embodiment 4:
Distilled water 100 parts is taken, phthalocyanine blue 4 parts, 11 parts, calcium carbonate, 1.1 parts, ammonium hydroxide according to mass fraction proportioning, n-Octanol 4 parts, sodium naphthalene sulfonate 2 parts, silica 11 part, titanium dioxide 25 parts, trisodium phosphate 9 parts, nonyl phenyl polyethylene hexanediol ether 0.6 part, is uniformly mixed in a kettle..
Product colour is bright-coloured, smooth, good dispersity; Solid divides 40%, and coating measures 0.3; Time of drying 12h, 11 months storage periods.
Embodiment 5:
Distilled water 100 parts is taken, phthalocyanine blue 3 parts, 10 parts, calcium carbonate, 1 part, ammonium hydroxide according to mass fraction proportioning, n-Octanol 3 parts, sodium naphthalene sulfonate 1.5 parts, silica 10 part, titanium dioxide 20 parts, trisodium phosphate 8 parts, nonyl phenyl polyethylene hexanediol ether 0.5 part, is uniformly mixed in a kettle..
Product colour is bright-coloured, smooth, good dispersity; Solid divides 50%, and coating measures 0.35; Time of drying 7h, 12 months storage periods.
Claims (4)
1. an Xylo-Mucine multicolor finish, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described Xylo-Mucine multicolor finish: distilled water 100 parts, pigment 1-5 part, calcium carbonate 8-12 part, ammonium hydroxide 0.8-1.2 part, n-Octanol 1-5 part, sodium naphthalene sulfonate 0.5-2.5 part, silicon-dioxide 8-12 part, titanium dioxide 10-30 part, trisodium phosphate 6-10 part, nonyl phenyl polyethylene hexanediol ether 0.2-0.8 part.
2. a kind of Xylo-Mucine multicolor finish according to claim 1, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described Xylo-Mucine multicolor finish: distilled water 100 parts, pigment 2-4 part, calcium carbonate 9-11 part, ammonium hydroxide 0.9-1.1 part, n-Octanol 2-4 part, sodium naphthalene sulfonate 1-2 part, silicon-dioxide 9-11 part, titanium dioxide 15-25 part, trisodium phosphate 7-9 part, nonyl phenyl polyethylene hexanediol ether 0.4-0.6 part.
3. a kind of Xylo-Mucine multicolor finish according to claim 2, it is characterized in that, it is as follows that mass fraction proportioning pressed by the raw material of described Xylo-Mucine multicolor finish: distilled water 100 parts, pigment 3 parts, 10 parts, calcium carbonate, 1 part, ammonium hydroxide, n-Octanol 3 parts, sodium naphthalene sulfonate 1.5 parts, silica 10 part, titanium dioxide 20 parts, trisodium phosphate 8 parts, nonyl phenyl polyethylene hexanediol ether 0.5 part.
4. a kind of Xylo-Mucine multicolor finish according to claim 1, is characterized in that: described pigment adopts red iron oxide or phthalocyanine blue.