CN104446611A - 一种绝热吸声加气砖及其制备方法 - Google Patents
一种绝热吸声加气砖及其制备方法 Download PDFInfo
- Publication number
- CN104446611A CN104446611A CN201410633982.8A CN201410633982A CN104446611A CN 104446611 A CN104446611 A CN 104446611A CN 201410633982 A CN201410633982 A CN 201410633982A CN 104446611 A CN104446611 A CN 104446611A
- Authority
- CN
- China
- Prior art keywords
- parts
- powder
- water
- steam
- flyash
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种绝热吸声加气砖,由下列重量份的原料制成：铝矾土熟料3-5、硅酸钙6-7、膨胀珍珠岩粉3-5、石膏6-7、粉煤灰40-50、加气铝粉7-8、水泥9-11、生石灰11-13、废旧泡沫颗粒2-3、改性煤灰7-9、偏硅酸1-2、碳酸钙粉2-4、矿渣棉5-6、水适量；本发明加气砖通过使用矿渣棉、膨胀珍珠岩粉，增加了加气砖的绝热、吸音效果，同时提高了强度、耐磨性、耐火性、保温性和尺寸稳定性，节能环保，发展前景好；通过使用改性煤灰，增强了隔热效果，耐水性好，减少了环境污染，同时减水效果好。
Description
技术领域
本发明属于砖领域，尤其涉及一种绝热吸声加气砖及其制备方法。
背景技术
加气砖也叫做加气混凝土砌块，应用非常的广泛，主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和周围的填充围墙。
目前加气砖已成为建筑材料行业的主导产品，国家已经逐步禁止使用粘土实心砖，逐渐取而代之的就是加气混凝土砌块，蒸压砖。
加气砖具有重量轻、保温隔热性能好、抗震能力强、加工性能好、具有一定的耐高温性、隔音性能好、适应性强的特点，可根据当地不同原材料，不同条件来量身定造，原材料来源广泛，可选择河沙、粉煤灰、矿砂等，因地制宜，可以废物利用，有利环保，真正变废为宝。
但是随着建筑行业的发展，建筑物越来越高、造型越来越奇特，对加气砖的强度、密度、收缩值、抗冻性等要求都有所提高，另外随着人们生活水平的不断提高，对环境的要求也越来越高，对建筑物的保温性能、吸音性能、放射性都有更高的要求，甚至要求建筑物具有有益身体健康的性能，因此根据需要，研制更加性能优异的加气砖势在必行。
发明内容
本发明的目的在于提供一种绝热吸声加气砖及其制备方法，该加气砖具有绝热、吸音效果好、强度高、耐磨性好、耐火、保温性好、尺寸稳定性好、节能环保的优点。
本发明的技术方案如下：
一种绝热吸声加气砖,其特征在于由下列重量份的原料制成：铝矾土熟料3-5、硅酸钙6-7、膨胀珍珠岩粉3-5、石膏6-7、粉煤灰40-50、加气铝粉7-8、水泥9-11、生石灰11-13、废旧泡沫颗粒2-3、改性煤灰7-9、偏硅酸1-2、碳酸钙粉2-4、矿渣棉5-6、水适量；
所述改性煤灰由下列重量份的原料制成：煤灰13-15、硅酸锂0.5-0.7、氟硅酸镁1-2、硬脂酸铝0.5-0.7、糖钙0.5-0.8、甲基丙烯酸缩水甘油酯0.5-0.7、偶氮二异丁腈0.1-0.2、丙烯酸酯1-1.3、茶籽饼1-2、泡沫玻璃粉1-2、聚羧酸高效减水剂2-3、双戊烯0.4-0.7、粉煤灰2-4、亚硫酸钙0.5-0.7、废机油2-3；制作方法为：将煤灰、茶籽饼粉碎成100-200目颗粒，边搅拌边喷入双戊烯、废机油、硬脂酸铝，混合均匀后放置5-7个小时，再与其他剩余成分混合，加热至75-80℃，分散研磨30-40分钟，即得。
所述的绝热吸声加气砖的制备方法，其特征在于包括以下步骤：
（1）将水泥、铝矾土熟料、硅酸钙、碳酸钙粉、膨胀珍珠岩粉、生石灰、石膏、粉煤灰混合，送入球磨机中研磨成100-200目颗粒，再与除加气铝粉之外的成分混合，按水料比为0.57-0.58加入水，搅拌均匀，再加入加气铝粉，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖胚体；
（3）将砖胚体放入蒸养釜进行抽真空，然后在1.7-1.9小时内均匀地通入蒸汽，使蒸养室内的温度升至170-180℃，压力达到11-13MPa，保持恒定9-12小时；
（4）在1.7-1.9小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃以下，出釜，放置28-30天即得。
本发明的有益效果
本发明加气砖通过使用矿渣棉、膨胀珍珠岩粉，增加了加气砖的绝热、吸音效果，同时提高了强度、耐磨性、耐火性、保温性和尺寸稳定性，节能环保，发展前景好；通过使用改性煤灰，增强了隔热效果，耐水性好，减少了环境污染，同时减水效果好。
具体实施方式
一种绝热吸声加气砖,由下列重量份（公斤）的原料制成：铝矾土熟料4、硅酸钙6.5、膨胀珍珠岩粉4、石膏6.5、粉煤灰45、加气铝粉7.5、水泥10、生石灰12、废旧泡沫颗粒2.4、改性煤灰8、偏硅酸1.5、碳酸钙粉3、矿渣棉5.5、水适量；
所述改性煤灰由下列重量份(公斤)的原料制成：煤灰14、硅酸锂0.6、氟硅酸镁1.5、硬脂酸铝0.6、糖钙0.6、甲基丙烯酸缩水甘油酯0.6、偶氮二异丁腈0.1、丙烯酸酯1.2、茶籽饼1.5、泡沫玻璃粉1.5、聚羧酸高效减水剂2.5、双戊烯0.6、粉煤灰3、亚硫酸钙0.6、废机油2.6；制作方法为：将煤灰、茶籽饼粉碎成160目颗粒，边搅拌边喷入双戊烯、废机油、硬脂酸铝，混合均匀后放置6个小时，再与其他剩余成分混合，加热至78℃，分散研磨36分钟，即得。
所述的绝热吸声加气砖的制备方法，包括以下步骤：
（1）将水泥、铝矾土熟料、硅酸钙、碳酸钙粉、膨胀珍珠岩粉、生石灰、石膏、粉煤灰混合，送入球磨机中研磨成150目颗粒，再与除加气铝粉之外的成分混合，按水料比为0.57加入水，搅拌均匀，再加入加气铝粉，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖胚体；
（3）将砖胚体放入蒸养釜进行抽真空，然后在1.8小时内均匀地通入蒸汽，使蒸养室内的温度升至176℃，压力达到11MPa，保持恒定11小时；
（4）在1.8小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃，出釜，放置28天即得。
实验数据：
该加气砖的密度为590kg/m3，耐火温度为730℃，导热系数为0.12W /(m·℃），采用淋浴喷头分别向240mm厚的粘土砖墙和加气砖墙喷淋，粘土砖墙12小时后全部浸透，加气砖墙喷淋72小时后渗水深度为70mm，抗压强度为 7.4Mpa，吸声系数0.47。
Claims (2)
1.一种绝热吸声加气砖,其特征在于由下列重量份的原料制成：铝矾土熟料3-5、硅酸钙6-7、膨胀珍珠岩粉3-5、石膏6-7、粉煤灰40-50、加气铝粉7-8、水泥9-11、生石灰11-13、废旧泡沫颗粒2-3、改性煤灰7-9、偏硅酸1-2、碳酸钙粉2-4、矿渣棉5-6、水适量；
所述改性煤灰由下列重量份的原料制成：煤灰13-15、硅酸锂0.5-0.7、氟硅酸镁1-2、硬脂酸铝0.5-0.7、糖钙0.5-0.8、甲基丙烯酸缩水甘油酯0.5-0.7、偶氮二异丁腈0.1-0.2、丙烯酸酯1-1.3、茶籽饼1-2、泡沫玻璃粉1-2、聚羧酸高效减水剂2-3、双戊烯0.4-0.7、粉煤灰2-4、亚硫酸钙0.5-0.7、废机油2-3；制作方法为：将煤灰、茶籽饼粉碎成100-200目颗粒，边搅拌边喷入双戊烯、废机油、硬脂酸铝，混合均匀后放置5-7个小时，再与其他剩余成分混合，加热至75-80℃，分散研磨30-40分钟，即得。
2.根据权利要求1所述的绝热吸声加气砖的制备方法，其特征在于包括以下步骤：
（1）将水泥、铝矾土熟料、硅酸钙、碳酸钙粉、膨胀珍珠岩粉、生石灰、石膏、粉煤灰混合，送入球磨机中研磨成100-200目颗粒，再与除加气铝粉之外的成分混合，按水料比为0.57-0.58加入水，搅拌均匀，再加入加气铝粉，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖胚体；
（3）将砖胚体放入蒸养釜进行抽真空，然后在1.7-1.9小时内均匀地通入蒸汽，使蒸养室内的温度升至170-180℃，压力达到11-13MPa，保持恒定9-12小时；
（4）在1.7-1.9小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃以下，出釜，放置28-30天即得。