CN104193387B - 一种吸波加气砖及其制备方法 - Google Patents
一种吸波加气砖及其制备方法 Download PDFInfo
- Publication number
- CN104193387B CN104193387B CN201410370193.XA CN201410370193A CN104193387B CN 104193387 B CN104193387 B CN 104193387B CN 201410370193 A CN201410370193 A CN 201410370193A CN 104193387 B CN104193387 B CN 104193387B
- Authority
- CN
- China
- Prior art keywords
- aerated bricks
- water
- rice husk
- steam
- hour
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种吸波加气砖，由下列重量份的原料制成：水泥11-14、生石灰12-15、改性稻壳8-11、石膏4-7、粉煤灰60-70、聚磷酸铵3-5、苯丙乳液0.3-0.6、山嵛醇0.2-0.4、引气剂K12？0.01-0.015、高钙硫铝熟料0.3-0.4、硬脂酸钠0.3-0.5、煅烧菱镁矿4-7、加气铝粉5-6、淀粉0.4-0.6、导电石墨0.9-1.4、水适量；本发明加气砖通过使用导电石墨，使得加气砖具有一定的吸波性能，防止电磁干扰辐射，而且该加气砖气泡不连续，均匀，因此加气砖强度高，耐磨性好，耐水性好，而且阻燃性好；通过使用改性稻壳，增强了隔热效果，减轻了重量，增加了抗震性能，同时减水效果好。
Description
技术领域
本发明属于砖领域，尤其涉及一种吸波加气砖及其制备方法。
背景技术
加气砖也叫做加气混凝土砌块，应用非常的广泛，主要用在机械厂房和民用建筑中的墙体材料、填充墙、楼板和屋面板等承重墙材以及非承重材料和周围的填充围墙。
目前加气砖已成为建筑材料行业的主导产品，国家已经逐步禁止使用粘土实心砖，逐渐取而代之的就是加气混凝土砌块，蒸压砖。
加气砖具有重量轻、保温隔热性能好、抗震能力强、加工性能好、具有一定的耐高温性、隔音性能好、适应性强的特点，可根据当地不同原材料，不同条件来量身定造，原材料来源广泛，可选择河沙、粉煤灰、矿砂等，因地制宜，可以废物利用，有利环保，真正变废为宝。
但是随着建筑行业的发展，建筑物越来越高、造型越来越奇特，对加气砖的强度、密度、收缩值、抗冻性等要求都有所提高，另外随着人们生活水平的不断提高，对环境的要求也越来越高，对建筑物的保温性能、吸音性能、放射性都有更高的要求，甚至要求建筑物具有有益身体健康的性能，因此根据需要，研制更加性能优异的加气砖势在必行。
发明内容
本发明的目的在于提供一种吸波加气砖及其制备方法，该加气砖具有一定的吸波性能，防止电磁干扰辐射，强度高，耐磨性好，耐水性好，阻燃性好。
本发明的技术方案如下：
一种吸波加气砖,其特征在于由下列重量份的原料制成：水泥11-14、生石灰12-15、改性稻壳8-11、石膏4-7、粉煤灰60-70、聚磷酸铵3-5、苯丙乳液0.3-0.6、山嵛醇0.2-0.4、引气剂K120.01-0.015、高钙硫铝熟料0.3-0.4、硬脂酸钠0.3-0.5、煅烧菱镁矿4-7、加气铝粉5-6、淀粉0.4-0.6、导电石墨0.9-1.4、水适量；
所述改性稻壳由下列重量份的原料制成：稻壳13-15、亚硫酸钠0.5-0.7、远红外陶瓷粉1-2、庚酸烯丙酯0.5-0.7、2-甲基咪唑0.1-0.2、芳香族聚氨酯丙烯酸酯1-2、丙烯酸羟乙酯1-2、聚羧酸高效减水剂1-2、玻璃粉1-2、过硫酸铵0.01-0.02、海藻酸钙0.4-0.7、霞石粉1-2、三丹油0.5-0.7、地沟油2-3；制作方法为：将稻壳粉碎成50-100目颗粒，边搅拌边喷入三丹油、地沟油，混合均匀后放置5-7个小时，再与其他剩余成分混合，加热至75-80℃，分散研磨30-40分钟，即得。
所述的吸波加气砖的制备方法，其特征在于包括以下步骤：
（1）将水泥、生石灰、石膏、煅烧菱镁矿、粉煤灰混合，送入球磨机中研磨成50-100目颗粒，再与除加气铝粉之外的成分混合，按水料比为0.57-0.58加入水，搅拌均匀，再加入加气铝粉，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖坯体；
（3）将砖坯体放入蒸养釜进行抽真空，然后在1.7-1.9小时内均匀地通入蒸汽，使蒸养室内的温度升至170-180℃，压力达到11-13MPa，保持恒定9-12小时；
（4）在1.7-1.9小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃以下，出釜，放置28-30天即得。
本发明的有益效果
本发明加气砖通过使用导电石墨，使得加气砖具有一定的吸波性能，防止电磁干扰辐射，而且该加气砖气泡不连续，均匀，因此加气砖强度高，耐磨性好，耐水性好，而且阻燃性好；通过使用改性稻壳，增强了隔热效果，耐水性好，减轻了重量，增加了抗震性能，同时减水效果好。
具体实施方式
一种吸波加气砖,由下列重量份(公斤)的原料制成：水泥12、生石灰14、改性稻壳10、石膏5、粉煤灰65、聚磷酸铵4、苯丙乳液0.5、山嵛醇0.3、引气剂K120.013、高钙硫铝熟料0.4、硬脂酸钠0.4、煅烧菱镁矿5、加气铝粉5.5、淀粉0.5、导电石墨1.2、水适量；
所述改性稻壳由下列重量份（公斤）的原料制成：稻壳14、亚硫酸钠0.6、远红外陶瓷粉1.6、庚酸烯丙酯0.6、2-甲基咪唑0.1、芳香族聚氨酯丙烯酸酯1.5、丙烯酸羟乙酯1.5、聚羧酸高效减水剂1.5、玻璃粉1.5、过硫酸铵0.01、海藻酸钙0.6、霞石粉1.6、三丹油0.6、地沟油2.6；制作方法为：将稻壳粉碎成80目颗粒，边搅拌边喷入三丹油、地沟油，混合均匀后放置6个小时，再与其他剩余成分混合，加热至77℃，分散研磨35分钟，即得。
所述的吸波加气砖的制备方法，包括以下步骤：
（1）将水泥、生石灰、石膏、煅烧菱镁矿、粉煤灰混合，送入球磨机中研磨成90目颗粒，再与除加气铝粉之外的成分混合，按水料比为0.58加入水，搅拌均匀，再加入加气铝粉，搅拌均匀得到浆料；
（2）将第（1）步得到的浆料倒入模具中，得到砖坯体；
（3）将砖坯体放入蒸养釜进行抽真空，然后在1.8小时内均匀地通入蒸汽，使蒸养室内的温度升至175℃，压力达到12MPa，保持恒定11小时；
（4）在1.8小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃，出釜，放置29天即得。
实验数据：
该加气砖的密度为680kg/m3，耐火温度为670℃，导热系数为0.11W/(m·℃），采用淋浴喷头分别向240mm厚的粘土砖墙和加气砖墙喷淋，粘土砖墙12小时后全部浸透，加气砖墙喷淋72小时后渗水深度为70mm，抗压强度为5.9Mpa，吸声系数0.45。
Claims (2)
1.一种吸波加气砖,其特征在于由下列重量份的原料制成：水泥11-14、生石灰12-15、改性稻壳8-11、石膏4-7、粉煤灰60-70、聚磷酸铵3-5、苯丙乳液0.3-0.6、山嵛醇0.2-0.4、引气剂K120.01-0.015、高钙硫铝熟料0.3-0.4、硬脂酸钠0.3-0.5、煅烧菱镁矿4-7、加气铝粉5-6、淀粉0.4-0.6、导电石墨0.9-1.4、水适量；所述改性稻壳由下列重量份的原料制成：稻壳13-15、亚硫酸钠0.5-0.7、远红外陶瓷粉1-2、庚酸烯丙酯0.5-0.7、2-甲基咪唑0.1-0.2、芳香族聚氨酯丙烯酸酯1-2、丙烯酸羟乙酯1-2、聚羧酸高效减水剂1-2、玻璃粉1-2、过硫酸铵0.01-0.02、海藻酸钙0.4-0.7、霞石粉1-2、三丹油0.5-0.7、地沟油2-3；所述改性稻壳的制作方法为：将稻壳粉碎成50-100目颗粒，边搅拌边喷入三丹油、地沟油，混合均匀后放置5-7个小时，再与其他剩余成分混合，加热至75-80℃，分散研磨30-40分钟，即得。
2.根据权利要求1所述的吸波加气砖的制备方法，其特征在于包括以下步骤：（1）将水泥、生石灰、石膏、煅烧菱镁矿、粉煤灰混合，送入球磨机中研磨成50-100目颗粒，再与除加气铝粉之外的成分混合，按水料比为0.57-0.58加入水，搅拌均匀，再加入加气铝粉，搅拌均匀得到浆料；（2）将第（1）步得到的浆料倒入模具中，得到砖坯体；（3）将砖坯体放入蒸养釜进行抽真空，然后在1.7-1.9小时内均匀地通入蒸汽，使蒸养室内的温度升至170-180℃，压力达到11-13MPa，保持恒定9-12小时；（4）在1.7-1.9小时内均匀地放出蒸汽，使蒸养室内的温度降至70℃以下，出釜，放置28-30天即得。