CN104419372A - Adhesive - Google Patents
Adhesive Download PDFInfo
- Publication number
- CN104419372A CN104419372A CN201310410313.XA CN201310410313A CN104419372A CN 104419372 A CN104419372 A CN 104419372A CN 201310410313 A CN201310410313 A CN 201310410313A CN 104419372 A CN104419372 A CN 104419372A
- Authority
- CN
- China
- Prior art keywords
- tackiness agent
- paraffin
- polyvinyl alcohol
- oleic acid
- fire retardant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides an adhesive, comprising the following raw materials by weight: 1-3kg of a fire retardant, 60-90kg of paraffin, 10-25kg of oleic acid, 25-60kg of polyvinyl alcohol, 10-30kg of ammonium hydroxide and 120-450kg of water. According to the adhesive and a method for preparing the adhesive provided by the invention, the preparation process is simple; the raw materials are non-toxic and free of pollution; and the environmentally-friendly requirements are met.
Description
Technical field
The present invention relates to technical field of adhesive, particularly relate to a kind of tackiness agent for wooden form.
Background technology
The existing binder materials for the preparation of wooden form is mostly containing the toxic substance such as formaldehyde, Precondensed UreaFormaldehyde Resin, and expensive raw material price, and preparation is complicated.Product is made to reach environment protection requirement.
Summary of the invention
The object of the invention is to the defect solving the existence of above-mentioned prior art, provide a kind of technique simple, cheap, not containing the environmental protection tackiness agent of formaldehyde, Precondensed UreaFormaldehyde Resin.
For achieving the above object, the present invention adopts following technical scheme:
A kind of tackiness agent, its raw material by weight, comprising:
Fire retardant: 1-3kg, paraffin: 60-90kg, oleic acid: 10-25kg, polyvinyl alcohol 25-60kg, ammoniacal liquor 10-30kg, water 120-450kg.
Further, tackiness agent as above, its raw material by weight, comprising:
Fire retardant: 2kg, paraffin: 80kg, oleic acid: 16kg, polyvinyl alcohol 40kg, ammoniacal liquor 20kg surplus: 370kg water.
Further, described fire retardant is specially antimonous oxide, magnesium hydroxide, aluminium hydroxide one wherein.
Prepare a method for tackiness agent described above, comprise the following steps:
(1), as described above proportioning paraffin is added water and heats after emulsification, then drop into fire retardant, oleic acid, polyvinyl alcohol, ammoniacal liquor respectively by as above proportioning;
(2) be, under the condition of 60 °-90 °, the mixture of step (1) is fully stirred, obtains tackiness agent of the present invention in temperature.
Tackiness agent provided by the invention and prepare the method for tackiness agent, preparation technology is simple, and advantages of nontoxic raw materials is pollution-free, makes the present invention reach the requirement of environmental protection.
Embodiment
For making object of the present invention.Technical scheme and advantage clearly, are clearly and completely described the technical scheme in the present invention below, and obviously, described embodiment is the present invention's part embodiment, instead of whole embodiments.Based on the embodiment in the present invention, those of ordinary skill in the art, not making the every other embodiment obtained under creative work prerequisite, belong to the scope of protection of the invention.
Embodiment 1:
Antimonous oxide: 2kg, paraffin: 80kg, oleic acid: 16kg, polyvinyl alcohol 40kg, ammoniacal liquor 20kg surplus: 370kg water.
Prepare the method for tackiness agent described above, comprise the following steps:
(1), as described above proportioning paraffin is added water and heats after emulsification, then drop into fire retardant, oleic acid, polyvinyl alcohol, ammoniacal liquor respectively by as above proportioning;
(2) be, under the condition of 60 °-90 °, the mixture of step (1) is fully stirred, obtains tackiness agent of the present invention in temperature.
Embodiment 2:
Magnesium hydroxide: 1kg, paraffin: 85kg, oleic acid: 16kg, polyvinyl alcohol 60kg, ammoniacal liquor 20kg surplus: 150kg water.
Prepare the method for tackiness agent described above, comprise the following steps:
(1), as described above proportioning paraffin is added water and heats after emulsification, then drop into fire retardant, oleic acid, polyvinyl alcohol, ammoniacal liquor respectively by as above proportioning;
(2) be, under the condition of 60 °-90 °, the mixture of step (1) is fully stirred, obtains tackiness agent of the present invention in temperature.
Embodiment 3:
Magnesium hydroxide: 3kg, paraffin: 90kg, oleic acid: 25kg, polyvinyl alcohol 55kg, ammoniacal liquor 30kg surplus: 120kg water.
Prepare the method for tackiness agent described above, comprise the following steps:
(1), as described above proportioning paraffin is added water and heats after emulsification, then drop into fire retardant, oleic acid, polyvinyl alcohol, ammoniacal liquor respectively by as above proportioning;
(2) be, under the condition of 60 °-90 °, the mixture of step (1) is fully stirred, obtains tackiness agent of the present invention in temperature.
Embodiment 4:
Aluminium hydroxide: 2.5kg, paraffin: 60kg, oleic acid: 16kg, polyvinyl alcohol 40kg, ammoniacal liquor 20kg surplus: 300kg water.
Prepare the method for tackiness agent described above, comprise the following steps:
(1), as described above proportioning paraffin is added water and heats after emulsification, then drop into fire retardant, oleic acid, polyvinyl alcohol, ammoniacal liquor respectively by as above proportioning;
(2) be, under the condition of 60 °-90 °, the mixture of step (1) is fully stirred, obtains tackiness agent of the present invention in temperature.
Embodiment 5:
Magnesium hydroxide: 3kg, paraffin: 90kg, oleic acid: 10kg, polyvinyl alcohol 25kg, ammoniacal liquor 10kg surplus: 450kg water.
Prepare the method for tackiness agent described above, comprise the following steps:
(1), as described above proportioning paraffin is added water and heats after emulsification, then drop into fire retardant, oleic acid, polyvinyl alcohol, ammoniacal liquor respectively by as above proportioning;
(2) be, under the condition of 60 °-90 °, the mixture of step (1) is fully stirred, obtains tackiness agent of the present invention in temperature.
Last it is noted that above embodiment is only in order to illustrate technical scheme of the present invention, be not intended to limit; Although with reference to previous embodiment to invention has been detailed description, those of ordinary skill in the art is to be understood that: it still can be modified to the technical scheme described in foregoing embodiments, or carries out equivalent replacement to wherein portion of techniques feature; And these amendments or replacement, do not make the essence of appropriate technical solution depart from the spirit and scope of various embodiments of the present invention technical scheme.
Claims (4)
1. a tackiness agent, is characterized in that, its raw material by weight, comprising:
Fire retardant: 1-3kg, paraffin: 60-90kg, oleic acid: 10-25kg, polyvinyl alcohol 25-60kg, ammoniacal liquor 10-30kg, water 120-450kg.
2. tackiness agent according to claim 1, is characterized in that, its raw material by weight, comprising:
Fire retardant: 2kg, paraffin: 80kg, oleic acid: 16kg, polyvinyl alcohol 40kg, ammoniacal liquor 20kg surplus: 370kg water.
3. tackiness agent according to claim 1 and 2, is characterized in that, described fire retardant is specially antimonous oxide, magnesium hydroxide, aluminium hydroxide one wherein.
4. prepare a preparation method for tackiness agent described in claim 1, it is characterized in that comprising the following steps:
(1), by proportioning according to claim 1 being added water by paraffin heats after emulsification, then drops into fire retardant, oleic acid, polyvinyl alcohol, ammoniacal liquor respectively by as above proportioning;
(2) be, under the condition of 60 °-90 °, the mixture of step (1) is fully stirred, obtains tackiness agent of the present invention in temperature.