CN104327750A - Single-component plate alignment adhesive - Google Patents
Single-component plate alignment adhesive Download PDFInfo
- Publication number
- CN104327750A CN104327750A CN201410552513.3A CN201410552513A CN104327750A CN 104327750 A CN104327750 A CN 104327750A CN 201410552513 A CN201410552513 A CN 201410552513A CN 104327750 A CN104327750 A CN 104327750A
- Authority
- CN
- China
- Prior art keywords
- parts
- lauric acid
- weight
- kf88s
- rongalites
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a single-component plate alignment adhesive which is composed of the following ingredients in parts by weight: 250 parts of deionized water, 1-2 parts of lauric acid, 8-9 parts of butyl acrylate, 2-3 parts of tert-butyl hydroperoxide, 1-2 parts of polyvinylpyrrolidone, 3-4 parts of triethylamine, 1-2 parts of polyglycerol monostearate, 1-2 parts of ammonium persulfate, 3-4 parts of sodium formaldehyde sulfoxylate, 7-8 parts of triethanolamine, 2-3 parts of Kathon and 1-2 parts of methyltrimethoxy silane. The single-component plate alignment adhesive has the advantages of high heat resistance (the heat resistance of the adhesive film can reach 400 DEG C), long storage time and long open period.
Description
Technical field
The present invention relates to Single-component puzzle glue.
Background technology
Splicing adhesive refers to the tackiness agent for splicing the woodworks such as integrated timber, is suitable for the jigsaw bonding of non-structural material and structural wood integrated timber etc.
Summary of the invention
The object of the present invention is to provide a kind of Single-component puzzle glue, its resistance toheat is strong, and the thermotolerance of glued membrane can reach 400 DEG C, and preservation period and open season long.
For achieving the above object, technical scheme of the present invention is a kind of Single-component puzzle glue of design, consists of the following composition by weight:
250 parts of deionized waters,
1 ~ 2 part of lauric acid,
8 ~ 9 parts of butyl acrylates,
2 ~ 3 parts of tertbutyl peroxides,
1 ~ 2 part of polyvinylpyrrolidone,
3 ~ 4 parts of triethylamines,
1 ~ 2 part of Polyglycerine monostearate,
1 ~ 2 part of ammonium persulphate,
3 ~ 4 parts of rongalites,
7 ~ 8 parts of trolamines,
2 ~ 3 parts of KF88s,
1 ~ 2 part of methyltrimethoxy silane.
Preferably, Single-component puzzle glue, consists of the following composition by weight:
250 parts of deionized waters,
1.2 parts of lauric acid,
8.9 parts of butyl acrylates,
2.3 parts of tertbutyl peroxides,
1.2 parts of polyvinylpyrrolidones,
3.4 parts of triethylamines,
1.2 parts of Polyglycerine monostearates,
1.2 parts of ammonium persulphates,
3.4 parts of rongalites,
7.8 parts of trolamines,
2.3 parts of KF88s,
1.2 parts of methyltrimethoxy silanes.
Preferably, Single-component puzzle glue, consists of the following composition by weight:
250 parts of deionized waters,
1 part of lauric acid,
8 parts of butyl acrylates,
2 parts of tertbutyl peroxides,
1 part of polyvinylpyrrolidone,
3 parts of triethylamines,
1 part of Polyglycerine monostearate,
1 part of ammonium persulphate,
3 parts of rongalites,
7 parts of trolamines,
2 parts of KF88s,
1 part of methyltrimethoxy silane.
Preferably, Single-component puzzle glue, consists of the following composition by weight:
250 parts of deionized waters,
2 parts of lauric acid,
9 parts of butyl acrylates,
3 parts of tertbutyl peroxides,
2 parts of polyvinylpyrrolidones,
4 parts of triethylamines,
2 parts of Polyglycerine monostearates,
2 parts of ammonium persulphates,
4 parts of rongalites,
8 parts of trolamines,
3 parts of KF88s,
2 parts of methyltrimethoxy silanes.
Advantage of the present invention and beneficial effect are: provide a kind of Single-component puzzle glue, and its resistance toheat is strong, and the thermotolerance of glued membrane can reach 400 DEG C, and preservation period and open season long.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Single-component puzzle glue, consists of the following composition by weight:
250 parts of deionized waters,
1.2 parts of lauric acid,
8.9 parts of butyl acrylates,
2.3 parts of tertbutyl peroxides,
1.2 parts of polyvinylpyrrolidones,
3.4 parts of triethylamines,
1.2 parts of Polyglycerine monostearates,
1.2 parts of ammonium persulphates,
3.4 parts of rongalites,
7.8 parts of trolamines,
2.3 parts of KF88s,
1.2 parts of methyltrimethoxy silanes.
Embodiment 2
Single-component puzzle glue, consists of the following composition by weight:
250 parts of deionized waters,
1 part of lauric acid,
8 parts of butyl acrylates,
2 parts of tertbutyl peroxides,
1 part of polyvinylpyrrolidone,
3 parts of triethylamines,
1 part of Polyglycerine monostearate,
1 part of ammonium persulphate,
3 parts of rongalites,
7 parts of trolamines,
2 parts of KF88s,
1 part of methyltrimethoxy silane.
Embodiment 3
Single-component puzzle glue, consists of the following composition by weight:
250 parts of deionized waters,
2 parts of lauric acid,
9 parts of butyl acrylates,
3 parts of tertbutyl peroxides,
2 parts of polyvinylpyrrolidones,
4 parts of triethylamines,
2 parts of Polyglycerine monostearates,
2 parts of ammonium persulphates,
4 parts of rongalites,
8 parts of trolamines,
3 parts of KF88s,
2 parts of methyltrimethoxy silanes.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. Single-component puzzle glue, is characterized in that, consists of the following composition by weight:
250 parts of deionized waters,
1 ~ 2 part of lauric acid,
8 ~ 9 parts of butyl acrylates,
2 ~ 3 parts of tertbutyl peroxides,
1 ~ 2 part of polyvinylpyrrolidone,
3 ~ 4 parts of triethylamines,
1 ~ 2 part of Polyglycerine monostearate,
1 ~ 2 part of ammonium persulphate,
3 ~ 4 parts of rongalites,
7 ~ 8 parts of trolamines,
2 ~ 3 parts of KF88s,
1 ~ 2 part of methyltrimethoxy silane.
2. Single-component puzzle glue according to claim 1, is characterized in that, consists of the following composition by weight:
250 parts of deionized waters,
1.2 parts of lauric acid,
8.9 parts of butyl acrylates,
2.3 parts of tertbutyl peroxides,
1.2 parts of polyvinylpyrrolidones,
3.4 parts of triethylamines,
1.2 parts of Polyglycerine monostearates,
1.2 parts of ammonium persulphates,
3.4 parts of rongalites,
7.8 parts of trolamines,
2.3 parts of KF88s,
1.2 parts of methyltrimethoxy silanes.
3. Single-component puzzle glue according to claim 1, is characterized in that, consists of the following composition by weight:
250 parts of deionized waters,
1 part of lauric acid,
8 parts of butyl acrylates,
2 parts of tertbutyl peroxides,
1 part of polyvinylpyrrolidone,
3 parts of triethylamines,
1 part of Polyglycerine monostearate,
1 part of ammonium persulphate,
3 parts of rongalites,
7 parts of trolamines,
2 parts of KF88s,
1 part of methyltrimethoxy silane.
4. Single-component puzzle glue according to claim 1, is characterized in that, consists of the following composition by weight:
250 parts of deionized waters,
2 parts of lauric acid,
9 parts of butyl acrylates,
3 parts of tertbutyl peroxides,
2 parts of polyvinylpyrrolidones,
4 parts of triethylamines,
2 parts of Polyglycerine monostearates,
2 parts of ammonium persulphates,
4 parts of rongalites,
8 parts of trolamines,
3 parts of KF88s,
2 parts of methyltrimethoxy silanes.