CN104277722B - Timber floor binding agent - Google Patents
Timber floor binding agent Download PDFInfo
- Publication number
- CN104277722B CN104277722B CN201410552485.5A CN201410552485A CN104277722B CN 104277722 B CN104277722 B CN 104277722B CN 201410552485 A CN201410552485 A CN 201410552485A CN 104277722 B CN104277722 B CN 104277722B
- Authority
- CN
- China
- Prior art keywords
- parts
- binding agent
- timber floor
- isomery
- poly
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of timber floor binding agent, consist of the following composition by weight: 65 parts of deionized waters, 2 ~ 3 parts of ethyl trimethoxy silanes, 2 ~ 3 parts of N hydroxymethyl acrylamides, 1 ~ 2 part of vinylformic acid, 1 ~ 2 part of maleic anhydride modified polyethylene, 2 ~ 3 parts of isomery ten polyoxyethylenated alcohol, 1 ~ 2 part of sodium bicarbonate, 1 ~ 2 part of Potassium Persulphate, 2 ~ 3 parts of polyvinyl alcohol, 1 ~ 2 part of locust tree glue etherate, 7 ~ 8 parts of methyl acrylates, 3 ~ 4 parts of poly-hexanodioic acid hexylene glycol esters.Timber floor binding agent of the present invention, its cohesive force is strong, good weatherability.
Description
Technical field
The present invention relates to timber floor binding agent.
Background technology
Timber floor needs the splicing of polylith timber floor to be bonded together to carry out constructing and then using, and in order to make bonding between neighboring trees board tight, and the time length is long, needs to select a kind of binding agent preferably.
Summary of the invention
The object of the present invention is to provide a kind of timber floor binding agent, its cohesive force is strong, good weatherability.
For achieving the above object, technical scheme of the present invention is a kind of timber floor binding agent of design, consists of the following composition by weight:
65 parts of deionized waters,
2 ~ 3 parts of ethyl trimethoxy silanes,
2 ~ 3 parts of N hydroxymethyl acrylamides,
1 ~ 2 part of vinylformic acid,
1 ~ 2 part of maleic anhydride modified polyethylene,
2 ~ 3 parts of isomery ten polyoxyethylenated alcohol,
1 ~ 2 part of sodium bicarbonate,
1 ~ 2 part of Potassium Persulphate,
2 ~ 3 parts of polyvinyl alcohol,
1 ~ 2 part of locust tree glue etherate,
7 ~ 8 parts of methyl acrylates,
3 ~ 4 parts of poly-hexanodioic acid hexylene glycol esters.
Preferably, timber floor binding agent, consists of the following composition by weight:
65 parts of deionized waters,
2.3 parts of ethyl trimethoxy silanes,
2.3 parts of N hydroxymethyl acrylamides,
1.2 parts of vinylformic acid,
1.2 parts of maleic anhydride modified polyethylene,
2.3 parts of isomery ten polyoxyethylenated alcohol,
1.2 parts of sodium bicarbonates,
1.2 parts of Potassium Persulphates,
2.3 parts of polyvinyl alcohol,
1.2 parts of locust tree glue etherates,
7.8 parts of methyl acrylates,
3.4 parts of poly-hexanodioic acid hexylene glycol esters.
Preferably, timber floor binding agent, consists of the following composition by weight:
65 parts of deionized waters,
2 parts of ethyl trimethoxy silanes,
2 parts of N hydroxymethyl acrylamides,
1 part of vinylformic acid,
1 part of maleic anhydride modified polyethylene,
2 parts of isomery ten polyoxyethylenated alcohol,
1 part of sodium bicarbonate,
1 part of Potassium Persulphate,
2 parts of polyvinyl alcohol,
1 part of locust tree glue etherate,
7 parts of methyl acrylates,
3 parts of poly-hexanodioic acid hexylene glycol esters.
Preferably, timber floor binding agent, consists of the following composition by weight:
65 parts of deionized waters,
3 parts of ethyl trimethoxy silanes,
3 parts of N hydroxymethyl acrylamides,
2 parts of vinylformic acid,
2 parts of maleic anhydride modified polyethylene,
3 parts of isomery ten polyoxyethylenated alcohol,
2 parts of sodium bicarbonates,
2 parts of Potassium Persulphates,
3 parts of polyvinyl alcohol,
2 parts of locust tree glue etherates,
8 parts of methyl acrylates,
4 parts of poly-hexanodioic acid hexylene glycol esters.
Advantage of the present invention and beneficial effect are: provide a kind of timber floor binding agent, and its cohesive force is strong, good weatherability.
Embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples only for technical scheme of the present invention is clearly described, and can not limit the scope of the invention with this.
The technical scheme that the present invention specifically implements is:
Embodiment 1
Timber floor binding agent, consists of the following composition by weight:
65 parts of deionized waters,
2.3 parts of ethyl trimethoxy silanes,
2.3 parts of N hydroxymethyl acrylamides,
1.2 parts of vinylformic acid,
1.2 parts of maleic anhydride modified polyethylene,
2.3 parts of isomery ten polyoxyethylenated alcohol,
1.2 parts of sodium bicarbonates,
1.2 parts of Potassium Persulphates,
2.3 parts of polyvinyl alcohol,
1.2 parts of locust tree glue etherates,
7.8 parts of methyl acrylates,
3.4 parts of poly-hexanodioic acid hexylene glycol esters.
Embodiment 2
Timber floor binding agent, consists of the following composition by weight:
65 parts of deionized waters,
2 parts of ethyl trimethoxy silanes,
2 parts of N hydroxymethyl acrylamides,
1 part of vinylformic acid,
1 part of maleic anhydride modified polyethylene,
2 parts of isomery ten polyoxyethylenated alcohol,
1 part of sodium bicarbonate,
1 part of Potassium Persulphate,
2 parts of polyvinyl alcohol,
1 part of locust tree glue etherate,
7 parts of methyl acrylates,
3 parts of poly-hexanodioic acid hexylene glycol esters.
Embodiment 3
Timber floor binding agent, consists of the following composition by weight:
65 parts of deionized waters,
3 parts of ethyl trimethoxy silanes,
3 parts of N hydroxymethyl acrylamides,
2 parts of vinylformic acid,
2 parts of maleic anhydride modified polyethylene,
3 parts of isomery ten polyoxyethylenated alcohol,
2 parts of sodium bicarbonates,
2 parts of Potassium Persulphates,
3 parts of polyvinyl alcohol,
2 parts of locust tree glue etherates,
8 parts of methyl acrylates,
4 parts of poly-hexanodioic acid hexylene glycol esters.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, under the prerequisite not departing from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (4)
1. timber floor binding agent, is characterized in that, consists of the following composition by weight:
65 parts of deionized waters,
2 ~ 3 parts of ethyl trimethoxy silanes,
2 ~ 3 parts of N hydroxymethyl acrylamides,
1 ~ 2 part of vinylformic acid,
1 ~ 2 part of maleic anhydride modified polyethylene,
2 ~ 3 parts of isomery ten polyoxyethylenated alcohol,
1 ~ 2 part of sodium bicarbonate,
1 ~ 2 part of Potassium Persulphate,
2 ~ 3 parts of polyvinyl alcohol,
1 ~ 2 part of locust tree glue etherate,
7 ~ 8 parts of methyl acrylates,
3 ~ 4 parts of poly-hexanodioic acid hexylene glycol esters.
2. timber floor binding agent according to claim 1, is characterized in that, consist of the following composition by weight:
65 parts of deionized waters,
2.3 parts of ethyl trimethoxy silanes,
2.3 parts of N hydroxymethyl acrylamides,
1.2 parts of vinylformic acid,
1.2 parts of maleic anhydride modified polyethylene,
2.3 parts of isomery ten polyoxyethylenated alcohol,
1.2 parts of sodium bicarbonates,
1.2 parts of Potassium Persulphates,
2.3 parts of polyvinyl alcohol,
1.2 parts of locust tree glue etherates,
7.8 parts of methyl acrylates,
3.4 parts of poly-hexanodioic acid hexylene glycol esters.
3. timber floor binding agent according to claim 1, is characterized in that, consist of the following composition by weight:
65 parts of deionized waters,
2 parts of ethyl trimethoxy silanes,
2 parts of N hydroxymethyl acrylamides,
1 part of vinylformic acid,
1 part of maleic anhydride modified polyethylene,
2 parts of isomery ten polyoxyethylenated alcohol,
1 part of sodium bicarbonate,
1 part of Potassium Persulphate,
2 parts of polyvinyl alcohol,
1 part of locust tree glue etherate,
7 parts of methyl acrylates,
3 parts of poly-hexanodioic acid hexylene glycol esters.
4. timber floor binding agent according to claim 1, is characterized in that, consist of the following composition by weight:
65 parts of deionized waters,
3 parts of ethyl trimethoxy silanes,
3 parts of N hydroxymethyl acrylamides,
2 parts of vinylformic acid,
2 parts of maleic anhydride modified polyethylene,
3 parts of isomery ten polyoxyethylenated alcohol,
2 parts of sodium bicarbonates,
2 parts of Potassium Persulphates,
3 parts of polyvinyl alcohol,
2 parts of locust tree glue etherates,
8 parts of methyl acrylates,
4 parts of poly-hexanodioic acid hexylene glycol esters.