CN104292952B - 一种防火阻燃铜金粉颜料及其制备方法 - Google Patents

一种防火阻燃铜金粉颜料及其制备方法 Download PDF

Info

Publication number
CN104292952B
CN104292952B CN201410509703.7A CN201410509703A CN104292952B CN 104292952 B CN104292952 B CN 104292952B CN 201410509703 A CN201410509703 A CN 201410509703A CN 104292952 B CN104292952 B CN 104292952B
Authority
CN
China
Prior art keywords
ethanol
oil
alloy powder
component
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201410509703.7A
Other languages
English (en)
Other versions
CN104292952A (zh
Inventor
董前年
朱双单
徐瞳瞳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
HEFEI SUNRISE ALUMINIUM PIGMENTS Co Ltd
Original Assignee
HEFEI SUNRISE ALUMINIUM PIGMENTS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by HEFEI SUNRISE ALUMINIUM PIGMENTS Co Ltd filed Critical HEFEI SUNRISE ALUMINIUM PIGMENTS Co Ltd
Priority to CN201410509703.7A priority Critical patent/CN104292952B/zh
Publication of CN104292952A publication Critical patent/CN104292952A/zh
Application granted granted Critical
Publication of CN104292952B publication Critical patent/CN104292952B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种防火阻燃铜金粉颜料，其特征是由下述重量份的原料组成：微米级的片状铜金粉40-50，三氧化二锑0.5-1，正硅酸乙酯6-8，硅烷偶联剂KH-550 0.3-0.5，磷酸三乙酯0.05-0.1，生育酚0.02-0.05，乙酸乙酯4-8，妥尔油1-2，山茶油2-4，硅烷偶联剂A-151 0.1-0.2，十溴联苯醚0.2-0.4，复合助剂1-2。本发明的铜金粉颜料防火阻燃性能好，安全性高，与有机树脂的相容性好，实用性强。

Description

一种防火阻燃铜金粉颜料及其制备方法
技术领域
本发明涉及金属颜料领域，具体涉及一种防火阻燃铜金粉颜料及其制备方法。
背景技术
金属颜料是具有片状形态的金属粒子，其作用在于以装饰或特殊工艺性能为目标或特征而赋予制品以一种金属色外观。金属颜料的用途可大致分为表面涂层(涂料、油墨、粉末涂料等)和塑料。在这些用途中，利用了金属颜料共有的特性：高金属光泽、高遮盖力和能形成平滑薄层涂膜。铝粉、铜金粉和锌粉是目前应用最广泛的金属颜料。
发明内容
本发明的目的是提供一种防火阻燃铜金粉颜料。
本发明是通过以下技术方案实现的：
一种防火阻燃铜金粉颜料，其由下述重量份的原料制成：
微米级的片状铜金粉40-50，三氧化二锑0.5-1，正硅酸乙酯6-8，硅烷偶联剂KH-5500.3-0.5，磷酸三乙酯0.05-0.1，生育酚0.02-0.05，乙酸乙酯4-8，妥尔油1-2，山茶油2-4，硅烷偶联剂A-1510.1-0.2，十溴联苯醚0.2-0.4，复合助剂1-2；
复合助剂由下列重量份的原料制成：
纳米碳酸钙30-40，纳米二氧化硅5-10，钛酸酯偶联剂0.5-1，白矿油1-2，亚麻籽油1-2，太古油0.5-1，没食子酸丙酯0.5-1；
复合助剂的制备方法：
将纳米碳酸钙和纳米二氧化硅加入适量水，混合均匀后加入钛酸酯偶联剂，60-80℃充分搅拌0.5-1h，干燥后加入白矿油、亚麻籽油、没食子酸丙酯和太古油的混合液，110-130℃充分搅拌0.5-1h，即得。
一种防火阻燃铜金粉颜料的制备方法，包括以下步骤：
（1）配制氨水、蒸馏水和乙醇的混合溶剂作为A组分，用乙醇稀释正硅酸乙酯作为B组分；将微米级的片状铜金粉加入适量无水乙醇中，加入硅烷偶联剂A-151，氮气保护下搅拌0.5-1h后，以1-2滴/s的滴加速度同时分别滴加A组分和B组分，边滴加边搅拌，滴加完毕后40-45℃反应6-8h，抽滤后用无水乙醇洗涤，真空干燥，所述的A组分中氨水、蒸馏水和乙醇的重量比=1:2:5，所述的氨水浓度为25%，所述的B组分中乙醇和正硅酸乙酯的重量比=1:2；
（2）在反应容器中加入（1）中处理后的铜金粉、三氧化二锑和适量乙醇，搅拌混合均匀后加入硅烷偶联剂KH-550，60-80℃加热搅拌回流反应3-6h，用乙醇多次洗涤后干燥，再加入山茶油、生育酚和适量甲苯，30-40℃搅拌反应1-2h，离心后多次洗涤，真空干燥；
（3）与其余原料混合后50-60℃搅拌1-2h，取出后真空干燥即得。
本发明的优点是：
1.通过配方与工艺的改进，使铜金粉颜料具有良好的阻燃防火性能，降低火灾危险系数，提供高安全性；
2.通过铜金粉的表面改性，提升了铜金粉颜料的疏水性和在树脂中的分散性能，与树脂的相容性好，实用性强。
具体实施方式
本发明非限定实施例如下：
实施例1
一种防火阻燃铜金粉颜料，由下列重量(kg)的组分原料制备而成：
微米级的片状铜金粉45，三氧化二锑0.8，正硅酸乙酯7，硅烷偶联剂KH-5500.4，磷酸三乙酯0.08，生育酚0.04，乙酸乙酯6，妥尔油1.5，山茶油3，硅烷偶联剂A-1510.15，十溴联苯醚0.3，复合助剂1.5；
其中，复合助剂由下列重量（kg）的原料制成：
纳米碳酸钙35，纳米二氧化硅8，钛酸酯偶联剂0.8，白矿油1.5，亚麻籽油1.5，太古油0.8，没食子酸丙酯0.8；
复合助剂的制备方法：
将纳米碳酸钙和纳米二氧化硅加入适量水，混合均匀后加入钛酸酯偶联剂，80℃充分搅拌0.5h，干燥后加入白矿油、亚麻籽油、没食子酸丙酯和太古油的混合液，120℃充分搅拌0.5h，即得。
其制备方法包括以下步骤：
（1）配制氨水、蒸馏水和乙醇的混合溶剂作为A组分，用乙醇稀释正硅酸乙酯作为B组分；将微米级的片状铜金粉加入适量无水乙醇中，加入硅烷偶联剂A-151，氮气保护下搅拌0.5h后，以1滴/s的滴加速度同时分别滴加A组分和B组分，边滴加边搅拌，滴加完毕后40℃反应8h，抽滤后用无水乙醇洗涤，真空干燥，所述的A组分中氨水、蒸馏水和乙醇的重量比=1:2:5，所述的氨水浓度为25%，所述的B组分中乙醇和正硅酸乙酯的重量比=1:2；
（2）在反应容器中加入（1）中处理后的铜金粉、三氧化二锑和适量乙醇，搅拌混合均匀后加入硅烷偶联剂KH-550，80℃加热搅拌回流反应3h，用乙醇多次洗涤后干燥，再加入山茶油、生育酚和适量甲苯，30℃搅拌反应2h，离心后多次洗涤，真空干燥；
（3）与其余原料混合后60℃搅拌1h，取出后真空干燥即得。
经检验，本实施例的铜金粉颜料涂层表面平整光滑，光泽度良好，手感良好。

Claims (1)

1.一种防火阻燃铜金粉颜料，其特征在于其由下述重量份的原料制成：微米级的片状铜金粉40-50，三氧化二锑0.5-1，正硅酸乙酯6-8，硅烷偶联剂KH-5500.3-0.5，磷酸三乙酯0.05-0.1，生育酚0.02-0.05，乙酸乙酯4-8，妥尔油1-2，山茶油2-4，硅烷偶联剂A-1510.1-0.2，十溴联苯醚0.2-0.4，复合助剂1-2；
所述复合助剂由下列重量份的原料制成：纳米碳酸钙30-40，纳米二氧化硅5-10，钛酸酯偶联剂0.5-1，白矿油1-2，亚麻籽油1-2，太古油0.5-1，没食子酸丙酯0.5-1；
所述复合助剂的制备方法是：将纳米碳酸钙和纳米二氧化硅加入适量水，混合均匀后加入钛酸酯偶联剂，60-80℃充分搅拌0.5-1h，干燥后加入白矿油、亚麻籽油、没食子酸丙酯和太古油的混合液，110-130℃充分搅拌0.5-1h，即得；
所述的防火阻燃铜金粉颜料的制备方法，包括以下步骤：
（1）配制氨水、蒸馏水和乙醇的混合溶剂作为A组分，用乙醇稀释正硅酸乙酯作为B组分；将微米级的片状铜金粉加入适量无水乙醇中，加入硅烷偶联剂A-151，氮气保护下搅拌0.5-1h后，以1-2滴/s的滴加速度同时分别滴加A组分和B组分，边滴加边搅拌，滴加完毕后40-45℃反应6-8h，抽滤后用无水乙醇洗涤，真空干燥，所述的A组分中氨水、蒸馏水和乙醇的重量比=1:2:5，所述的氨水浓度为25%，所述的B组分中乙醇和正硅酸乙酯的重量比=1:2；
（2）在反应容器中加入（1）中处理后的铜金粉、三氧化二锑和适量乙醇，搅拌混合均匀后加入硅烷偶联剂KH-550，60-80℃加热搅拌回流反应3-6h，用乙醇多次洗涤后干燥，再加入山茶油、生育酚和适量甲苯，30-40℃搅拌反应1-2h，离心后多次洗涤，真空干燥；
（3）与其余原料混合后50-60℃搅拌1-2h，取出后真空干燥即得。
CN201410509703.7A 2014-09-29 2014-09-29 一种防火阻燃铜金粉颜料及其制备方法 Active CN104292952B (zh)