CN104263155A - Environmental-friendly waterborne coating for building inner wall decoration and preparation process of environmental-friendly waterborne coating - Google Patents
Environmental-friendly waterborne coating for building inner wall decoration and preparation process of environmental-friendly waterborne coating Download PDFInfo
- Publication number
- CN104263155A CN104263155A CN201410501632.6A CN201410501632A CN104263155A CN 104263155 A CN104263155 A CN 104263155A CN 201410501632 A CN201410501632 A CN 201410501632A CN 104263155 A CN104263155 A CN 104263155A
- Authority
- CN
- China
- Prior art keywords
- parts
- water
- environmental
- calcium carbonate
- kaolin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an environmental-friendly waterborne coating for building inner wall decoration. The environmental-friendly waterborne coating is prepared from the raw materials in parts by weight: 20-40 parts of deionized water, 0.3-0.5 part of cellulose, 0.5-1.0 part of a wetting dispersant, 0.1-0.3 part of a defoamer, 0.1-0.2 part of a pH regulator, 2-8 parts of titanium dioxide, 5-8 parts of kaolin, 10-15 parts of light calcium carbonate, 5-10 parts of talc, 15-25 parts of heavy calcium carbonate, 8-12 parts of acrylic emulsion, 0.1-0.5 part of a fungicide, 1-2 parts of propanediol, 0.5-1.0 part of a film-forming additive and 0.3-0.5 part of a thickener. The environmental-friendly waterborne coating has the characteristics of good coating effect, low harmful matter content, soft smell, low production cost, good stability and long service life.
Description
?
Technical field
The invention belongs to building material field, relate to a kind of water-borne coatings, specifically a kind of environment-friendly type building thing inner wall surface decorative water coating and preparation technology thereof.
Background technology
The time in all one's life about 70% ~ 90% of people is spent in indoor, if objectionable impurities is too much in room, just likely cause the various diseases of human body, a host of facts prove, the numerous disease of current people, as felt dizzy, fatiguability, tuberculosis, diarrhoea, allergy, air conditioning disease, obesity etc., all relevant with living conditions.Even more serious as degradation under leukemia, cancer and newborn teratogenesis, children's intelligence, also too much there is direct relation with the obnoxious flavour in residence, objectionable impurities.Various environmental protection paint, health lacquer, clean taste paint etc. are almost difficult to accomplish no pollution on the market, be often turned on purify air, anion releasing, decomposing formaldehyde etc. cannot see impalpable camouflage and mask coating itself and may to volatilize the defect of objectionable impurities.From formulation optimization, raw material screening, powder dispersing apparatus, production technique, smear the links such as construction and set about ensureing no pollution.
Enhancing along with people's environmental consciousness and the concern to HUMAN HEALTH, required interior wall coating is not only rest on protection body of wall, decorated wall surface functionally, prior environmental protection and health.Therefore develop that a kind of interior wall water-based can either purify air, the obnoxious flavour decomposed in air, the health of protection people, bring convenience can to again the life of people, make to live at home more easy cleaning, more attractive in appearance.
Summary of the invention
The object of the invention is to the defect overcoming prior art, a kind of environment-friendly type building thing inner wall surface decorative water coating and preparation technology thereof are provided.
Object of the present invention can be achieved through the following technical solutions:
Environment-friendly type building thing inner wall surface decorative water coating, this water-borne coatings is made up of the raw material of following weight part: deionized water 20-40 part, Mierocrystalline cellulose 0.3-0.5 part, wetting dispersing agent 0.5-1.0 part, defoamer 0.1-0.3 part, PH conditioning agent 0.1-0.2 part, titanium dioxide 2-8 part, kaolin 5-8 part, light calcium carbonate 10-15 part, talcum powder 5-10 part, water-ground limestone 15-25 part, modified acrylic acid emulsion 8-12 part, sterilant 0.1-0.5 part, propylene glycol 1-2 part, film coalescence aid 0.5-1.0 part, thickening material 0.3-0.5 part.
Preferably, this water-borne coatings is made up of the raw material of following weight part: deionized water 30 parts, Mierocrystalline cellulose 0.4 part, wetting dispersing agent 0.75 part, defoamer 0.2 part, PH conditioning agent 0.15 part, titanium dioxide 5 parts, kaolin 6.5 parts, light calcium carbonate 12.5 parts, talcum powder 8 parts, water-ground limestone 20 parts, modified acrylic acid emulsion 10 parts, 0.3 part, sterilant, propylene glycol 1.5 parts, film coalescence aid 0.7 part, thickening material 0.4 part.
Preferably, described kaolin particle diameter is 4000 orders, and light calcium carbonate particle diameter is 1250 orders, talcum powder particle diameter is 1250 orders, and water-ground limestone particle diameter is 800 orders.
Present invention also offers a kind of technique preparing water-borne coatings, comprise following concrete steps:
In the deionized water of half amount, add wetting dispersing agent, defoamer, mixed with propylene glycol, form premixed liquid; In premixed liquid, add titanium dioxide, kaolin, light calcium carbonate, talcum powder and water-ground limestone, after dispersion, grind to form pigment slurry;
After the deionized water of sterilant, film coalescence aid, PH conditioning agent, Mierocrystalline cellulose residual content is mixed, join together with pigment slurry in modified acrylic acid emulsion;
Add thickening material adjustment viscosity to 95-105KU, obtained finished product coating.
Titanium dioxide belongs to inert pigment, has rutile-type and anatase titanium dioxide two kinds of structures, and rutile crystalline structure is fine and close, and more stable, optical activity is little, good weatherability, has higher opacifying power, reducing power simultaneously.
Light calcium carbonate can make coating not sedimentation, easily disperses, good luster, and particle diameter is 800-1250 order.
The main component of water-ground limestone is CaCO
3, the features such as whiteness is high, and purity is good, the soft and chemical composition stability of form and aspect, play increase small product size, and reduce the effect of production cost, particle diameter is within the scope of 1-10 μm.
Beneficial effect of the present invention: water-borne coatings painting effect of the present invention is good, harmful substance contents is low, smell is soft, production cost is low, good stability, long service life, be that base-material makes coating various interior wall basal plane have fabulous sticking power with ACRYLIC EMULSION, have good workability, water-resistance property of coating is good, brushing area is large, reduces application holistic cost.
Embodiment
For the ease of it will be appreciated by those skilled in the art that the present invention is further illustrated below in conjunction with specific embodiment.The raw material used in the present embodiment all commercially can be bought and obtain.The present embodiment Raw kaolin particle diameter is 4000 orders, and light calcium carbonate particle diameter is 1250 orders, and talcum powder particle diameter is 1250 orders, and water-ground limestone particle diameter is 800 orders.
Embodiment 1
Wetting dispersing agent 0.75 part, defoamer 0.2 part, propylene glycol 1.5 parts are joined in the deionized water of 15 parts, mixes, form premixed liquid; In premixed liquid, add titanium dioxide 5 parts, kaolin 6.5 parts, light calcium carbonate 12.5 parts, talcum powder 8 parts, water-ground limestone 20 parts, after dispersion, grind to form pigment slurry;
After the deionized water of 0.3 part of sterilant, 0.7 part of film coalescence aid, 0.15 part of PH conditioning agent, 0.4 part of Mierocrystalline cellulose residue 15 parts is mixed, join in 10 parts of modified acrylic acid emulsions together with pigment slurry;
Finally, 0.4 part of thickening material adjustment viscosity is added to 100KU, obtained finished product coating.
Embodiment 2
Wetting dispersing agent 1 part, defoamer 0.1 part, propylene glycol 1 part are joined in the deionized water of 10 parts, mixes, form premixed liquid; In premixed liquid, add titanium dioxide 2 parts, kaolin 5 parts, light calcium carbonate 15 parts, talcum powder 5 parts, water-ground limestone 15 parts, grind to form pigment slurry after dispersion, being ground to particle diameter is 1000-1250 order;
After the deionized water of 0.1 part of sterilant, 0.5 part of film coalescence aid, 0.5 part of PH conditioning agent, 0.3 part of Mierocrystalline cellulose residue 10 parts is mixed, join in 8 parts of modified acrylic acid emulsions together with pigment slurry;
Finally, 0.3 part of thickening material adjustment viscosity is added to 105KU, obtained finished product coating.
Embodiment 3
Wetting dispersing agent 0.5 part, defoamer 0.3 part, propylene glycol 2 parts are joined in the deionized water of 20 parts, mixes, form premixed liquid; In premixed liquid, add titanium dioxide 8 parts, kaolin 8 parts, light calcium carbonate 10 parts, talcum powder 10 parts, water-ground limestone 25 parts, grind to form pigment slurry after dispersion, being ground to particle diameter is 1000-1250 order;
After the deionized water of 0.5 part of sterilant, 1 part of film coalescence aid, 0.1 part of PH conditioning agent, 0.5 part of Mierocrystalline cellulose residue 20 parts is mixed, join in 12 parts of modified acrylic acid emulsions together with pigment slurry;
Finally, 0.5 part of thickening material adjustment viscosity is added to 95KU, obtained finished product coating.
Above content is only citing made for the present invention and explanation; affiliated those skilled in the art make various amendment to described specific embodiment or supplement or adopt similar mode to substitute; only otherwise depart from invention or surmount this scope as defined in the claims, protection scope of the present invention all should be belonged to.
Claims (4)
1. environment-friendly type building thing inner wall surface decorative water coating, it is characterized in that, this water-borne coatings is made up of the raw material of following weight part: deionized water 20-40 part, Mierocrystalline cellulose 0.3-0.5 part, wetting dispersing agent 0.5-1.0 part, defoamer 0.1-0.3 part, PH conditioning agent 0.1-0.2 part, titanium dioxide 2-8 part, kaolin 5-8 part, light calcium carbonate 10-15 part, talcum powder 5-10 part, water-ground limestone 15-25 part, modified acrylic acid emulsion 8-12 part, sterilant 0.1-0.5 part, propylene glycol 1-2 part, film coalescence aid 0.5-1.0 part, thickening material 0.3-0.5 part.
2. environment-friendly type building thing inner wall surface decorative water coating according to claim 1, it is characterized in that, this water-borne coatings is made up of the raw material of following weight part: deionized water 30 parts, Mierocrystalline cellulose 0.4 part, wetting dispersing agent 0.75 part, defoamer 0.2 part, PH conditioning agent 0.15 part, titanium dioxide 5 parts, kaolin 6.5 parts, light calcium carbonate 12.5 parts, talcum powder 8 parts, water-ground limestone 20 parts, modified acrylic acid emulsion 10 parts, 0.3 part, sterilant, propylene glycol 1.5 parts, film coalescence aid 0.7 part, thickening material 0.4 part.
3. environment-friendly type building thing inner wall surface decorative water coating according to claim 1 or 2, it is characterized in that, described kaolin particle diameter is 4000 orders, and light calcium carbonate particle diameter is 1250 orders, talcum powder particle diameter is 1250 orders, and water-ground limestone particle diameter is 800 orders.
4. prepare a technique for water-borne coatings as claimed in claim 1 or 2, it is characterized in that, comprise following concrete steps:
In the deionized water of half amount, add wetting dispersing agent, defoamer, mixed with propylene glycol, form premixed liquid; In premixed liquid, add titanium dioxide, kaolin, light calcium carbonate, talcum powder and water-ground limestone, after dispersion, grind to form pigment slurry;
After the deionized water of sterilant, film coalescence aid, PH conditioning agent, Mierocrystalline cellulose residual content is mixed, join together with pigment slurry in modified acrylic acid emulsion;
Add thickening material adjustment viscosity to 95-105KU, obtained finished product coating.