CN104127113A - Shade curtain shell fabric - Google Patents
Shade curtain shell fabric Download PDFInfo
- Publication number
- CN104127113A CN104127113A CN201410382803.8A CN201410382803A CN104127113A CN 104127113 A CN104127113 A CN 104127113A CN 201410382803 A CN201410382803 A CN 201410382803A CN 104127113 A CN104127113 A CN 104127113A
- Authority
- CN
- China
- Prior art keywords
- grey cloth
- dry
- cloth
- polyester particle
- dried
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a shade curtain shell fabric. The preparation method of the shade curtain shell fabric comprises the following steps of (1) silk making, (2) weaving, (3) dosing, (4) one immersion and one rolling, (5) drying, (6) baking, (7) washing and (8) secondary drying. According to the shade curtain shell fabric, the functions of inflaming retarding and full light shading are achieved through change of the raw materials and organization structure.
Description
Technical field
The present invention relates to a kind of shade curtain fabric.
Background technology
Fire service law regulation, the decorative textile product of the public buildings such as each large hotel, office, meeting room adopts inflaming retarding fabric without exception.Along with the raising of people's living standard and the enhancing of fire-fighting consciousness, fire-retardant requirement to family decoration fabric is also more and more higher, in bedroom, the place that light is had relatively high expectations such as cinema, multimedia chamber, darkroom, usually need a kind of window curtain fabric of full shading, full shade fabric is in the market passed through coating processing mostly, but through its draping property of fabric and the gas permeability variation of coating, and coating easily comes off, and affects shaded effect.
Summary of the invention
Technical problem to be solved by this invention is to provide a kind of shade curtain fabric, realizes fire-retardant and full shade function by the variation of raw material and institutional framework.
For solving above-mentioned existing technical problem, the present invention adopts following scheme: shade curtain fabric, comprise the following steps: 1), throwing: first by flame retardant polyester particle, antibacterial polyester particle, uvioresistant polyester particle, antistatic polyester particle, anion polyester granulate and far-infrared polyester particle are pressed the mixed hybrid particles of 1:1:1:1:1:1 pre-crystallized 62～65min at the temperature of 150 DEG C, then the dry moisture content≤15ppm that makes dried hybrid particles at the temperature of 158～160 DEG C, again by dry Masterbatch 2～2.5h, then dry Masterbatch is fully mixed to rear spinning with dry hybrid particles, then after entering after winding falling-barrel, processing obtains terylene color silk, 2), weave cotton cloth: adopt one group of warp thread and one group of weft yarn to be woven into grey cloth according to warp backed weave structure on water-jet loom, grey cloth be organized as two-sided tissue, form reversible cloth, 3), dosing: first add a small amount of water, then add sol-type flame retardant, emulsifying agent, protecting colloid, silicone softening agent and bleeding agent to carry out abundant stirring and dissolving, then to regulate pH value with alkali be 5.5～5.8, be diluted with water and obtain fire retarding treating liquid, 4), one soaks one and rolls: grey cloth is padded to fire retarding treating liquid by padding machine, and the speed of a motor vehicle of padding grey cloth in process is 28～30m/min, and the liquid carrying rate that pads rear grey cloth is 72～75%, 5), dry: at 120～125 DEG C, grey cloth is dried to 3min, 6), bake: at 180～185 DEG C, grey cloth is baked to 2～2.5min, 7), washing: the grey cloth after baking is washed 3～4 times, 8), dry for the second time: finally at 135～140 DEG C, the grey cloth after washing is dried to 2.5～3min and obtain flame-retarded sun-shading curtain cloth.
Beneficial effect:
The shade curtain fabric that the present invention adopts technique scheme to provide, realize fire-retardant and full shade function by the variation of raw material, institutional framework and production technology, fire-retardant, shading, antibacterial, uvioresistant etc. are functional good, coating is difficult for departing from, even if depart from, still there is good fire resistance.
Detailed description of the invention
Shade curtain fabric, comprise the following steps: 1), throwing: first by flame retardant polyester particle, antibacterial polyester particle, uvioresistant polyester particle, antistatic polyester particle, anion polyester granulate and far-infrared polyester particle are pressed the mixed hybrid particles of 1:1:1:1:1:1 pre-crystallized 62～65min at the temperature of 150 DEG C, then the dry moisture content≤15ppm that makes dried hybrid particles at the temperature of 158～160 DEG C, again by dry Masterbatch 2～2.5h, then dry Masterbatch is fully mixed to rear spinning with dry hybrid particles, then after entering after winding falling-barrel, processing obtains terylene color silk, 2), weave cotton cloth: adopt one group of warp thread and one group of weft yarn to be woven into grey cloth according to warp backed weave structure on water-jet loom, grey cloth be organized as two-sided tissue, form reversible cloth, 3), dosing: first add a small amount of water, then add sol-type flame retardant, emulsifying agent, protecting colloid, silicone softening agent and bleeding agent to carry out abundant stirring and dissolving, then to regulate pH value with alkali be 5.5～5.8, be diluted with water and obtain fire retarding treating liquid, 4), one soaks one and rolls: grey cloth is padded to fire retarding treating liquid by padding machine, and the speed of a motor vehicle of padding grey cloth in process is 28～30m/min, and the liquid carrying rate that pads rear grey cloth is 72～75%, 5), dry: at 120～125 DEG C, grey cloth is dried to 3min, 6), bake: at 180～185 DEG C, grey cloth is baked to 2～2.5min, 7), washing: the grey cloth after baking is washed 3～4 times, 8), dry for the second time: finally at 135～140 DEG C, the grey cloth after washing is dried to 2.5～3min and obtain flame-retarded sun-shading curtain cloth.
Claims (1)
1. shade curtain fabric, it is characterized in that: comprise the following steps: 1), throwing: first by flame retardant polyester particle, antibacterial polyester particle, uvioresistant polyester particle, antistatic polyester particle, anion polyester granulate and far-infrared polyester particle are pressed the mixed hybrid particles of 1:1:1:1:1:1 pre-crystallized 62～65min at the temperature of 150 DEG C, then the dry moisture content≤15ppm that makes dried hybrid particles at the temperature of 158～160 DEG C, again by dry Masterbatch 2～2.5h, then dry Masterbatch is fully mixed to rear spinning with dry hybrid particles, then after entering after winding falling-barrel, processing obtains terylene color silk, 2), weave cotton cloth: adopt one group of warp thread and one group of weft yarn to be woven into grey cloth according to warp backed weave structure on water-jet loom, grey cloth be organized as two-sided tissue, form reversible cloth, 3), dosing: first add a small amount of water, then add sol-type flame retardant, emulsifying agent, protecting colloid, silicone softening agent and bleeding agent to carry out abundant stirring and dissolving, then to regulate pH value with alkali be 5.5～5.8, be diluted with water and obtain fire retarding treating liquid, 4), one soaks one and rolls: grey cloth is padded to fire retarding treating liquid by padding machine, and the speed of a motor vehicle of padding grey cloth in process is 28～30m/min, and the liquid carrying rate that pads rear grey cloth is 72～75%, 5), dry: at 120～125 DEG C, grey cloth is dried to 3min, 6), bake: at 180～185 DEG C, grey cloth is baked to 2～2.5min, 7), washing: the grey cloth after baking is washed 3～4 times, 8), dry for the second time: finally at 135～140 DEG C, the grey cloth after washing is dried to 2.5～3min and obtain flame-retarded sun-shading curtain cloth.