CN1041212C - 聚烯烃组合物 - Google Patents
聚烯烃组合物 Download PDFInfo
- Publication number
- CN1041212C CN1041212C CN94107610A CN94107610A CN1041212C CN 1041212 C CN1041212 C CN 1041212C CN 94107610 A CN94107610 A CN 94107610A CN 94107610 A CN94107610 A CN 94107610A CN 1041212 C CN1041212 C CN 1041212C
- Authority
- CN
- China
- Prior art keywords
- weight
- polyolefin compositions
- ethylene
- polypropylene
- propylene rubber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Lifetime
Abstract
本发明提供一种聚烯烃组合物，该组合物包含有乙烯与丁烯-1共聚物、聚丙烯、乙丙橡胶、低分子量聚乙烯或聚丙烯及抗氧剂，制成的组合物具有很好的力学性能和加工性能，尤其适用作通信电缆的绝缘材料。
Description
本发明涉及一种聚烯烃组合物，尤其涉及适用于通讯电缆的聚烯烃组合物。国际专和分类号为：C08L23/00。
目前通讯电缆用的绝缘材料多数为聚乙烯材料，包括高密度(d＝0.941～0.965g/cm3)聚乙烯(HDPE)、中密度(d＝0.926～0.940)聚乙烯(MDPE)和低密度(d＝0.910～0.925g/cm3)聚乙烯(LDPE)，其中高密度聚乙烯效果最好。适用于通讯电缆绝缘材料的高密度聚乙烯的制备方法有两种。一是由乙烯和特定的催化剂在反应釜里用特定的聚合工艺制备的；二是由不同的聚乙烯经过共混改性的方法制得的。中国专利1054851A，比利时专利BE-901028A和日本公开专利77--14647均是用两种不同的聚乙烯共混的方法制备的第一份文献仅给出了聚乙烯产品密度、熔体流动速率(MI)及加工性能；后两份文献只给出原料及产品的密度和熔体流动速率(MI)。对于产品的力学性能和电性能均未给出。而且配方中没有其它聚合物组份，加入低密度或中密度聚乙烯必然给最终产品的耐磨性及使用寿命带来不利的影响；加入的低分子又使加工中产生烟雾。本发明的目的在于以高密度聚乙烯聚丙烯等树脂为基础。加入特定数量的改性剂提高产品的力学性能，改善加工性能。
因此，本发明提供一种聚烯烃组合物，该组合物包括下述组分：
①20～95％(重量)密度为0.945～0.956g/cm3的乙烯与丁烯-1共聚物，该共聚物的熔融指数(MI)为0.1～0.8克/10分钟；
②5～90％(重量)聚丙烯，该聚丙烯的熔融指数(MI)为8～12克/10分钟；
③5～20％(重量)乙丙橡胶，该乙丙橡胶中乙烯含量为50～60％(重量)；
④0.3～2％(重量)分子量为2000～4000的聚乙烯或熔融指数(MI)为30～40克/10分钟的聚丙烯；
⑤0.2～0.6％(重量)的抗氧剂。
所述乙烯与丁烯-1共聚物中丁烯-1含量为0.2～3.0％(重量)。
所述聚丙烯是丙烯均聚物。
所述乙丙橡胶是二元或三元乙丙橡胶。
所述抗氧剂是2.6-二叔丁基对甲酚或四〔β-(3，5-二叔丁基-4-羟基苯基)丙酸〕季戊四醇。
本发明的组合物可按下述方法制备：
按1-5中所述的材料及给定的配比，分别计量后加到高速混合器里以干混法混合均匀，再将混合均匀的物料加入双螺杆挤压机于160～250℃挤压，冷却切粒，即可得到性能优异的聚烯烃组合物，该组合物尤其适用于作通讯电缆绝缘材料。
本发明的发明者提出和制备一种既适用于高速(1500-2500m/min)牵引又可满足中低速(300-1200m/min)牵引加工通讯电缆的绝缘材料，这种材料具有优异的力学性能和加工性能其拉伸强度大于21MPa，伸长率大于500。
下面给出的实施例用于说明本发明，对其范围没有任何限定
实施例 1～4
实施例1～4各组合物的各组分及用量列在表1中，在制备组合物时，分别加到高速混合器里，混合均匀再加到双螺杆里挤出冷却切粒，计量包装，即可得到通讯电缆绝缘材料，具体的操作参数列于表2
表1聚烯烃电缆料的制备配方及典型性能
表2制备组合物的操作参数
Claims (5)
1.一种聚烯烃组合物，该组合物包括下述组分：
①)20～95％(重量)乙烯与丁烯-1共聚物，该共聚物的密度为0.945～0.956g/cm3，熔融指数(MI)为0.1～0.8克/10分钟；
②5～90％(重量)聚丙烯，该聚丙烯的熔融指数(MI)为9～12克/10分钟；
③5～20％(重量)乙丙橡胶，该乙丙橡胶中乙烯含量为50～60％(重量)；
④0.3～2％(重量)分子量为2000～4000的聚乙烯或熔融指数(MI)为30～40克/10分种的聚丙烯；
⑤0.2～0.6％(重量)抗氧剂。
2.如权利要求1所述的聚烯烃组合物，其特征在于乙烯与丁烯-1共聚物中丁烯-1含量为0.2～3.0％(重量)。
3.如权利要求1所述的聚烯烃组合物，其特征在于，聚丙烯是丙烯均聚物。
4.如权利要求1所述的聚烯烃组合物，其特征在于，乙丙橡胶是二元或三元乙丙橡胶。
5.如权利要求1所述的聚烯烃组合物，其特征在于，抗氧剂是2.6-二叔丁基对甲酚或四〔β-(3，5-二叔丁基-4-羟基苯基〕季戊四醇。