CN104119070B - A kind of organic jade material and preparation method thereof - Google Patents
A kind of organic jade material and preparation method thereof Download PDFInfo
- Publication number
- CN104119070B CN104119070B CN201410351727.4A CN201410351727A CN104119070B CN 104119070 B CN104119070 B CN 104119070B CN 201410351727 A CN201410351727 A CN 201410351727A CN 104119070 B CN104119070 B CN 104119070B
- Authority
- CN
- China
- Prior art keywords
- organic
- jade material
- raw material
- preparation
- carries out
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The invention discloses a kind of organic jade material, be prepared from by following raw material by weight: silicon-dioxide 40-45 part, aluminium sesquioxide 20-25 part, sodium oxide 15-20 part, silicon carbide 10-15 part, organic carbon source 5-10 part, magnesium oxide 0.05-0.1 part, cupric oxide 0.05-0.1 part, ferric oxide 0.05-0.1 part, selenium oxide 0.05-0.1 part, zinc oxide 0.05-0.1 part, manganese oxide 0.05-0.1 part, titanium dioxide 0.05-0.1 part.The invention also discloses a kind of preparation method of organic jade material.The present invention has quality densification, exquisiteness, and outward appearance is gentle smooth, thermostability and chemical stability high, have the performance of beautiful texture, there is good toughness, the feature that shock-resistant and plasticity-is strong simultaneously.
Description
Technical field
The invention belongs to the synthetic technical field of jade, be specifically related to a kind of organic jade material and preparation method thereof.
Background technology
Jade refers to hardness more than 3 degree less than 7 degree, the natural crystal that quality is fine and close, tough and tensile.Jade, through being processed into various artwork, has and very high to view and admire, use and reserve value, but jade being natural mineral, resource-constrained, and it is expensive is difficult to for masses accept.
In recent years, artificial jade's product commercially constantly occurs in recent years, and artificial jade's product commercially constantly occurs, mostly be bonded to add stone flour in resin, its main drawback is that hardness is low, and thermostability and poor chemical stability feel still have the vestige of plastics.In addition, the patent of invention that Chinese Patent Application No. is " ZL201010197098.6 " discloses a kind of manufacture method of artificial jade, the method adopts Inorganic Chemicals to manufacture artificial jade completely, the chemical constitution of this series products is inorganics, the fragility of product is higher, toughness is lower, easily chipping transporting, when being subject to External Force Acting in use procedure.
Summary of the invention
For the deficiencies in the prior art, an object of the present invention aims to provide a kind of organic jade material, and it has quality densification, exquisiteness, outward appearance is gentle smooth, thermostability and chemical stability high, have the performance of beautiful texture, there is good toughness, the feature that shock-resistant and plasticity-is strong simultaneously.
Two of object of the present invention aims to provide a kind of preparation method of organic jade material.
Realize an object of the present invention to reach by taking following technical scheme:
A kind of organic jade material, is characterized in that, be prepared from by following raw material by weight:
Preferably, described organic carbon source is the one in sucrose, glucose, starch.
Realize object of the present invention two can reach by taking following technical scheme:
A preparation method for organic jade material, is characterized in that, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block stock fragmentation, be ground to less than 5 millimeters, various raw material put into container and stirs, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 20-100MPa high pressure, Heating temperature, to 1450-1500 DEG C, makes compound melting, and insulation 3-4 hour, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 0 DEG C-20 DEG C carries out crystallisation by cooling, obtains xln;
4) by after xln scour without sediment motion, organic jade material is obtained.
Preferably, also comprising through step 4) organic jade material of obtaining after process carries out chiseling and carving, polishes, the technique of polishing.
Beneficial effect of the present invention is:
1, the present invention adopts the main component of natural jade: silicon-dioxide, aluminium sesquioxide, sodium oxide, silicon carbide etc., by adding organic carbon source, adds overall stability.The technique such as simultaneously carry out melting, subcooling crystallization in conjunction with High Temperature High Pressure and wash away, the organic jade material obtained is made to have quality densification, exquisiteness, outward appearance is gentle smooth, thermostability and chemical stability high, there is the performance of beautiful texture, there is good toughness, the advantage that shock-resistant and plasticity-is strong simultaneously.Compensate for natural jade scarcity of resources, expensive, fragile, flaw is many, aberration is large, be not easy the defects such as moulding, high-end furnishing fields can be widely used in.
2, be also added with the trace element of the useful HUMAN HEALTH such as magnesium, copper, iron, selenium, zinc, manganese, titanium in formula of the present invention, thus create the effect of " jade supports people ".
Embodiment
Below in conjunction with embodiment, the present invention is illustrated
Embodiment 1:
A kind of organic jade material, is prepared from by following raw material by weight:
Described organic carbon source is sucrose.
A preparation method for organic jade material, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block stock fragmentation, be ground to less than 5 millimeters, various raw material put into container and stirs, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 20MPa high pressure, Heating temperature to 1450 DEG C, makes compound melting, is incubated 3 hours, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 0 DEG C carries out crystallisation by cooling, is tied
4) by after xln scour without sediment motion, organic jade material is obtained.
5) by through step 4) organic jade material of obtaining after process carries out chiseling and carving, polishes, the technique of polishing, obtains finished product.
Embodiment 2:
A kind of organic jade material, is prepared from by following raw material by weight:
Described organic carbon source is glucose.
A preparation method for organic jade material, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block stock fragmentation, be ground to less than 5 millimeters, various raw material put into container and stirs, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 100MPa high pressure, Heating temperature to 1500 DEG C, makes compound melting, is incubated 4 hours, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 20 DEG C carries out crystallisation by cooling, obtains xln;
4) by after xln scour without sediment motion, organic jade material is obtained.
5) by through step 4) organic jade material of obtaining after process carries out chiseling and carving, polishes, the technique of polishing, obtains finished product.
Embodiment 3:
A kind of organic jade material, is prepared from by following raw material by weight:
Described organic carbon source is starch.
A preparation method for organic jade material, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block stock fragmentation, be ground to less than 5 millimeters, various raw material put into container and stirs, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 50MPa high pressure, Heating temperature to 1480 DEG C, makes compound melting, is incubated 3.5 hours, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 10 DEG C carries out crystallisation by cooling, obtains xln;
4) by after xln scour without sediment motion, organic jade material is obtained.
5) by through step 4) organic jade material of obtaining after process carries out chiseling and carving, polishes, the technique of polishing, obtains finished product.
Carry out Performance Detection to embodiment 1-3 products obtained therefrom, detected result is in table 1.
Table 1 performance perameter table
Above-described embodiment is only the preferred case study on implementation of the present invention, can not limit the present invention's scope required for protection with this, any unsubstantiality that those skilled in the art does on basis of the present invention and replace all belong to the scope of protection of present invention.
Claims (4)
1. an organic jade material, is characterized in that, is prepared from by following raw material by weight:
The preparation method of described organic jade material, carries out according to the following steps:
1) take raw material by the proportioning in formula described in claim 1, by block stock fragmentation, be ground to less than 5 millimeters, various raw material put into container and stirs, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 20-100MPa high pressure, Heating temperature, to 1450-1500 DEG C, makes compound melting, and insulation 3-4 hour, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 0 DEG C-20 DEG C carries out crystallisation by cooling, obtains xln;
4) by after xln scour without sediment motion, organic jade material is obtained.
2. organic jade material according to claim 1, is characterized in that: described organic carbon source is the one in sucrose, glucose, starch.
3. according to the preparation method of the organic jade material in claim 1-2 described in any one, it is characterized in that, carry out according to the following steps:
1) take raw material by the proportioning in formula described in claim 1, by block stock fragmentation, be ground to less than 5 millimeters, various raw material put into container and stirs, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 20-100MPa high pressure, Heating temperature, to 1450-1500 DEG C, makes compound melting, and insulation 3-4 hour, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 0 DEG C-20 DEG C carries out crystallisation by cooling, obtains xln;
4) by after xln scour without sediment motion, organic jade material is obtained.
4. the preparation method of organic jade material according to claim 1, is characterized in that: also comprise through step 4) organic jade material of obtaining after process carries out chiseling and carving, polishes, the technique of polishing.