CN104119070A - Organic jade material and preparation method thereof - Google Patents
Organic jade material and preparation method thereof Download PDFInfo
- Publication number
- CN104119070A CN104119070A CN201410351727.4A CN201410351727A CN104119070A CN 104119070 A CN104119070 A CN 104119070A CN 201410351727 A CN201410351727 A CN 201410351727A CN 104119070 A CN104119070 A CN 104119070A
- Authority
- CN
- China
- Prior art keywords
- organic
- jade material
- oxide
- jade
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses an organic jade material, which is prepared from the following raw materials in parts by weight: 40-45 parts of silica, 20-25 parts of aluminum oxide, 15-20 parts of sodium oxide, 10-15 parts of silicon carbide, 5-10 parts of organic carbon source, 0.05-0.1 part of magnesium oxide, 0.05-0.1 part of copper oxide, 0.05-0.1 part of ferric oxide, 0.05-0.1 part of selenium oxide, 0.05-0.1 part of zinc oxide, 0.05-0.1 part of manganese oxide, and 0.05-0.1 part of titanium oxide. The invention further discloses a preparation method of the organic jade material. The organic jade material is compact and fine in texture, mild and smooth in appearance, high in thermal stability and chemical stability, and has jade-feeling performance, as well as the characteristics of being good in toughness, impact-resistant and strong in plasticity.
Description
Technical field
The synthetic technical field that the invention belongs to jade, is specifically related to a kind of organic jade material and preparation method thereof.
Background technology
Jade refers to that hardness is more than 3 degree below 7 degree, quality densification, tough and tensile natural crystal.Jade is through being processed into various artworks, have very high view and admire, use and reserve value, but jade is natural mineral, resource-constrained, its expensive being difficult to is accepted for masses.
In recent years, artificial jade's product is continuous appearance in recent years on market, and artificial jade's product constantly occurs on market, mostly to add stone flour to be bonded in resin, its main drawback is that hardness is low, and thermostability and poor chemical stability still have the vestige of plastics in feel.In addition, the patent of invention that Chinese Patent Application No. is " ZL201010197098.6 " discloses a kind of manufacture method of artificial jade, the method adopts Inorganic Chemicals to manufacture artificial jade completely, the chemical constitution of this series products is inorganics, the fragility of product is higher, toughness is lower, easily chipping be subject to External Force Acting in transport, use procedure time.
Summary of the invention
For the deficiencies in the prior art, one of object of the present invention aims to provide a kind of organic jade material, and it has quality densification, exquisiteness, outward appearance is gentle smooth, thermostability and chemical stability are high, have the performance of beautiful texture, have good toughness, the feature that shock-resistant and plasticity-is strong simultaneously.
Two of object of the present invention aims to provide a kind of preparation method of organic jade material.
Realizing one of object of the present invention can be by taking following technical scheme to reach:
A kind of organic jade material, is characterized in that, is prepared from by following raw material by weight:
Preferably, described organic carbon source is the one in sucrose, glucose, starch.
Realizing two of object of the present invention can be by taking following technical scheme to reach:
A preparation method for organic jade material, is characterized in that, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block raw material crushing, be ground to below 5 millimeters, various raw materials are put into container and stir, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 20-100MPa high pressure, Heating temperature, to 1450-1500 DEG C, makes compound melting, and insulation 3-4 hour, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 0 DEG C-20 DEG C carries out crystallisation by cooling, obtains xln;
4) by xln with after scour without sediment motion, obtain organic jade material.
Preferably, also comprising through step 4) organic jade material of obtaining after processing is chiseled and carved, the technique of polishing, polishing.
Beneficial effect of the present invention is:
1, the present invention adopts the main component of natural jade: silicon-dioxide, aluminium sesquioxide, sodium oxide, silicon carbide etc., by adding organic carbon source, increased overall stability.The technique such as simultaneously carry out melting, subcooling crystallization in conjunction with High Temperature High Pressure and wash away, make the organic jade material obtaining there is quality densification, exquisiteness, outward appearance is gentle smooth, thermostability and chemical stability are high, there is the performance of beautiful texture, there is good toughness, shock-resistant and plasticity-is strong simultaneously.Made up natural jade scarcity of resources, expensive, fragile, flaw is many, aberration is large, be not easy the defects such as moulding, can be widely used in high-end decoration field.
2, in formula of the present invention, be also added with the trace element of the useful HUMAN HEALTH such as magnesium, copper, iron, selenium, zinc, manganese, titanium, thereby brought up the effect of " jade is supported people ".
Embodiment
Below in conjunction with embodiment, the present invention is illustrated
Embodiment 1:
A kind of organic jade material, is prepared from by following raw material by weight:
Described organic carbon source is sucrose.
A preparation method for organic jade material, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block raw material crushing, be ground to below 5 millimeters, various raw materials are put into container and stir, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 20MPa high pressure, Heating temperature to 1450 DEG C, makes compound melting, is incubated 3 hours, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 0 DEG C carries out crystallisation by cooling, is tied
4) by xln with after scour without sediment motion, obtain organic jade material.
5) by through step 4) organic jade material of obtaining after processing is chiseled and carved, the technique of polishing, polishing, obtains finished product.
Embodiment 2:
A kind of organic jade material, is prepared from by following raw material by weight:
Described organic carbon source is glucose.
A preparation method for organic jade material, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block raw material crushing, be ground to below 5 millimeters, various raw materials are put into container and stir, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 100MPa high pressure, Heating temperature to 1500 DEG C, makes compound melting, is incubated 4 hours, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 20 DEG C carries out crystallisation by cooling, obtains xln;
4) by xln with after scour without sediment motion, obtain organic jade material.
5) by through step 4) organic jade material of obtaining after processing is chiseled and carved, the technique of polishing, polishing, obtains finished product.
Embodiment 3:
A kind of organic jade material, is prepared from by following raw material by weight:
Described organic carbon source is starch.
A preparation method for organic jade material, carries out according to the following steps:
1) take raw material by the proportioning in above-mentioned formula, by block raw material crushing, be ground to below 5 millimeters, various raw materials are put into container and stir, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 50MPa high pressure, Heating temperature to 1480 DEG C, makes compound melting, is incubated 3.5 hours, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 10 DEG C carries out crystallisation by cooling, obtains xln;
4) by xln with after scour without sediment motion, obtain organic jade material.
5) by through step 4) organic jade material of obtaining after processing is chiseled and carved, the technique of polishing, polishing, obtains finished product.
Embodiment 1-3 products obtained therefrom is carried out to Performance Detection, and detected result is in table 1.
Table 1 performance perameter table
Above-described embodiment, only for the preferred case study on implementation of the present invention, can not limit the present invention's scope required for protection with this, any unsubstantiality that those skilled in the art does on basis of the present invention and replace and all belong to the scope of protection of present invention.
Claims (4)
1. an organic jade material, is characterized in that, is prepared from by following raw material by weight:
2. organic jade material according to claim 1, is characterized in that: described organic carbon source is the one in sucrose, glucose, starch.
3. according to the preparation method of the organic jade material described in any one in claim 1-2, it is characterized in that, carry out according to the following steps:
1) take raw material by the proportioning in formula described in claim 1, by block raw material crushing, be ground to below 5 millimeters, various raw materials are put into container and stir, obtain compound;
2) above-mentioned compound is put into smelting furnace, under 20-100MPa high pressure, Heating temperature, to 1450-1500 DEG C, makes compound melting, and insulation 3-4 hour, obtains melting charge;
3) melting charge being put into temperature is that the water coolant of 0 DEG C-20 DEG C carries out crystallisation by cooling, obtains xln;
4) by xln with after scour without sediment motion, obtain organic jade material.
4. the preparation method of organic jade material according to claim 1, is characterized in that: also comprise through step 4) organic jade material of obtaining after processing is chiseled and carved, the technique of polishing, polishing.