CN104099007B - 一种多镁基铝合金表面处理剂 - Google Patents
一种多镁基铝合金表面处理剂 Download PDFInfo
- Publication number
- CN104099007B CN104099007B CN201410275665.3A CN201410275665A CN104099007B CN 104099007 B CN104099007 B CN 104099007B CN 201410275665 A CN201410275665 A CN 201410275665A CN 104099007 B CN104099007 B CN 104099007B
- Authority
- CN
- China
- Prior art keywords
- stirring
- conditioning agent
- deionized water
- raw material
- minutes
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种多镁基铝合金表面处理剂，它是由下述重量份的原料组成的：苯扎溴铵1.2-2、氯化镁0.4-1、溴化苄0.2-0.4、二甲基甲酰胺0.8-1、硫酸镁0.4-2、二硫化钼0.1-0.2、1,3-二甲基-2-咪唑啉酮0.4-1、硫酸亚铁0.8-1、锑酸钠0.5-1、二烷基二硫代磷酸锌0.5-1、钼酸铵1-2、成膜助剂2-3、硅烷偶联剂KH550 10-12、硅烷偶联剂KH560 10-12、去离子水130-150，本发明的表面处理剂形成的涂膜均匀致密无气泡，工件表面干净，附着力强，防锈效果明显，沉渣产生少，耐候性强。
Description
技术领域
本发明主要涉及表面处理领域，尤其涉及一种多镁基铝合金表面处理剂。
背景技术
铝合金的表面处理方法有很多，如物理法、化学法、物理化学法和综合法。现在常用的方法是阳极氧化法，通过电化学方法在铝合金表面形成转化膜，这种方法虽然可提高铝合金的多镁基性能，但是其适应环境的能力差，转化膜层不够均匀、易脱落，耐磨性能没有得到改善，而传统的磷酸盐转化和铬酸盐钝化表面处理技术虽然可以获得良好的效果，但处理过程中排出的废液中含有锌、锰、镍、铬等重金属离子和亚多镁基等致癌物质，对环境污染非常严重，而金属表面硅烷化处理技术由于不涉及危害环境的物质，生产工艺能耗低、技术应用领域广泛，被认为有望取代磷酸盐转化处理和铬酸盐钝化处理，是金属表面单独防护最新发展方向。
发明内容
本发明目的就是提供一种多镁基铝合金表面处理剂。
本发明是通过以下技术方案实现的：
一种多镁基铝合金表面处理剂，它是由下述重量份的原料组成的：
苯扎溴铵1.2-2、氯化镁0.4-1、溴化苄0.2-0.4、二甲基甲酰胺0.8-1、硫酸镁0.4-2、二硫化钼0.1-0.2、1,3-二甲基-2-咪唑啉酮0.4-1、硫酸亚铁0.8-1、锑酸钠0.5-1、二烷基二硫代磷酸锌0.5-1、钼酸铵1-2、成膜助剂2-3、硅烷偶联剂KH55010-12、硅烷偶联剂KH56010-12、去离子水130-150；
所述的成膜助剂是由下述重量份的原料组成的：
聚乙二醇100020-26、氟硅酸钠1-2、乙酰丙酮钙0.2-0.3、钼酸铵0.5-1、甘草酸二钾1-2、沙蒿胶1-2、聚山梨酯801-2、硅烷偶联剂kh5600.3-0.5、去离子水70-80；
将氟硅酸钠、钼酸铵、硅烷偶联剂kh560混合球磨均匀，加入上述去离子水重量的20-30%，600-800转/分搅拌分散3-7分钟，得分散液；
将聚乙二醇1000与沙蒿胶混合，搅拌均匀后升高温度为55-60℃，加入甘草酸二钾，保温搅拌2-4分钟，加入到剩余的去离子水中，100-200转/分搅拌分散4-6分钟，加入上述分散液和剩余各原料，400-600转/分搅拌分散10-15分钟，即得所述成膜助剂。
一种多镁基铝合金表面处理剂的制备方法，包括以下步骤：
将氯化镁、硫酸镁混合，搅拌均匀后加入二烷基二硫代磷酸锌，60-70℃下搅拌混合3-5分钟；
将钼酸铵、硫酸亚铁混合加入到去离子水中，搅拌混合后加入1,3-二甲基-2-咪唑啉酮，60-70转/分搅拌分散10-20分钟；
将上述处理后的各原料与剩余各原料混合，200-300转/分搅拌分散1-2小时，即得所述多镁基铝合金表面处理剂。
本发明的优点是：
本发明的表面处理剂形成的涂膜均匀致密无气泡，工件表面干净，附着力强，防锈效果明显，沉渣产生少，耐候性强。
具体实施方式
实施例1
一种多镁基铝合金表面处理剂，它是由下述重量份的原料组成的：
苯扎溴铵1.2、氯化镁0.4、溴化苄0.2、二甲基甲酰胺0.8、硫酸镁0.4-2、二硫化钼0.1、1,3-二甲基-2-咪唑啉酮0.4、硫酸亚铁0.8、锑酸钠0.5-1、二烷基二硫代磷酸锌0.5、钼酸铵1-2、成膜助剂3、硅烷偶联剂KH55012、硅烷偶联剂KH56012、去离子水150；
所述的成膜助剂是由下述重量份的原料组成的：
聚乙二醇100026、氟硅酸钠2、乙酰丙酮钙0.3、钼酸铵0.5、甘草酸二钾1、沙蒿胶1、聚山梨酯802、硅烷偶联剂kh5600.5、去离子水80；
将氟硅酸钠、钼酸铵、硅烷偶联剂kh560混合球磨均匀，加入上述去离子水重量的30%，800转/分搅拌分散7分钟，得分散液；
将聚乙二醇1000与沙蒿胶混合，搅拌均匀后升高温度为60℃，加入甘草酸二钾，保温搅拌2分钟，加入到剩余的去离子水中，200转/分搅拌分散4分钟，加入上述分散液和剩余各原料，600转/分搅拌分散15分钟，即得所述成膜助剂。
一种多镁基铝合金表面处理剂的制备方法，包括以下步骤：
将氯化镁、硫酸镁混合，搅拌均匀后加入二烷基二硫代磷酸锌，70℃下搅拌混合3分钟；
将钼酸铵、硫酸亚铁混合加入到去离子水中，搅拌混合后加入1,3-二甲基-2-咪唑啉酮，70转/分搅拌分散20分钟；
将上述处理后的各原料与剩余各原料混合，300转/分搅拌分散1小时，即得所述多镁基铝合金表面处理剂。
使用方法：
将进行脱脂、水洗后的铝合金工件置于本发明的表面处理剂中进行浸渍，工作温度20-40℃，工作时间0.5-1min。
性能测试：
取本发明的表面处理剂处理的铝合金板材做实验，该板材的规格为80mm×100mm×4mm，将该板材横向切开，进行喷洒试验，所用试剂为浓度为5%的氯化钠溶液，试验时间300小时，测量在切割线一侧形成的鼓泡宽度，结果鼓泡宽度为0；
耐盐性：
将该板材浸泡在浓度为5%的氯化钠溶液中，浸泡300小时，材料表面基本无变化，浸泡300小时，无锈斑出现；
耐酸性：
将该板材用温度为23℃的0.05mol/l硫酸进行喷淋实验，实验时间20小时，用清水洗净，在室内放置2小时，漆膜表面无变化，无起泡、无脱落、无破损；
抗剥离性：
将该板材表面涂上一层2-3mm的浆糊，放到温度为50℃，相对湿度为90-96%的密封箱中，实验时间24小时，取出后用清水洗净，漆膜表面无起泡、无脱落、无破损。
Claims (2)
1.一种多镁基铝合金表面处理剂，其特征在于它是由下述重量份的原料组成的：苯扎溴铵1.2、氯化镁0.4、溴化苄0.2、二甲基甲酰胺0.8、硫酸镁0.4-2、二硫化钼0.1、1,3-二甲基-2-咪唑啉酮0.4、硫酸亚铁0.8、锑酸钠0.5-1、二烷基二硫代磷酸锌0.5、钼酸铵1-2、成膜助剂3、硅烷偶联剂KH55012、硅烷偶联剂KH56012、去离子水150；
所述的成膜助剂是由下述重量份的原料组成的：
聚乙二醇100026、氟硅酸钠2、乙酰丙酮钙0.3、钼酸铵0.5、甘草酸二钾1、沙蒿胶1、聚山梨酯802、硅烷偶联剂KH5600.5、去离子水80；
将氟硅酸钠、钼酸铵、硅烷偶联剂KH560混合球磨均匀，加入上述去离子水重量的30%，800转/分搅拌分散7分钟，得分散液；
将聚乙二醇1000与沙蒿胶混合，搅拌均匀后升高温度为60℃，加入甘草酸二钾，保温搅拌2分钟，加入到剩余的去离子水中，200转/分搅拌分散4分钟，加入上述分散液和剩余各原料，600转/分搅拌分散15分钟，即得所述成膜助剂。
2.一种如权利要求1所述的多镁基铝合金表面处理剂的制备方法，其特征在于包括以下步骤：将氯化镁、硫酸镁混合，搅拌均匀后加入二烷基二硫代磷酸锌，70℃下搅拌混合3分钟；
将钼酸铵、硫酸亚铁混合加入到去离子水中，搅拌混合后加入1,3-二甲基-2-咪唑啉酮，70转/分搅拌分散20分钟；
将上述处理后的各原料与剩余各原料混合，300转/分搅拌分散1小时，即得所述多镁基铝合金表面处理剂。