CN103937337A - Paint for vehicle tarpaulin - Google Patents
Paint for vehicle tarpaulin Download PDFInfo
- Publication number
- CN103937337A CN103937337A CN201410113603.2A CN201410113603A CN103937337A CN 103937337 A CN103937337 A CN 103937337A CN 201410113603 A CN201410113603 A CN 201410113603A CN 103937337 A CN103937337 A CN 103937337A
- Authority
- CN
- China
- Prior art keywords
- parts
- add
- raw material
- mix
- coating
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses paint for a vehicle tarpaulin. Raw materials of the paint for the vehicle tarpaulin comprises, by weight, 73-80 parts of polypropylene, 0.6-1 part of benzyl triphenyl phosphonium chloride, 1-2 parts of 8-hydroxyquinoline, 2-3 parts of bamboo fiber, 0.8-1.3 parts of bis(i-octyl thioacetate)tin-di-n-octyl, 1-2 parts of hydroxyethyl cellulose, 10-13 parts of heavy calcium carbonate, 1-2 parts of (3-aminopropyl)trimethoxy silane, 12-14 parts of dicapryl phthalate, 1-2 parts of 1H-Benzotriazole, 3-5 parts of anhydrous calcium chloride and 14-18 parts of composite filling material. The tarpaulin coated with the paint is great in wear resistance, is portable, is strong in waterproof performance, is low in price, is especially suitable for the vehicle tarpaulin and can be widely applied to various occasions.
Description
Technical field
The present invention relates generally to a kind of coating, relates in particular to a kind of top fabric coating.
Background technology
Object is exposed among atmosphere, is subject to the erosion of oxygen, moisture etc., causes the breakoff phenomenons such as corrosion of metal, foxy, cement weathering.At article surface, be coated with coating, form layer protecting film, can stop or postpone generation and the development of these breakoff phenomenons; extended the work-ing life of various materials; therefore a kind of efficient coating can play good protection effect, reduces the wastage rate of object, economizes on resources.
Development along with coating industry; take acrylate, PVC polymkeric substance etc. as the product of coating also a lot; but some coatings have slight corrodibility, dust suction, thermotolerance, weathering resistance poor; and the stable chemical performance of PE, good weatherability; nontoxic, pollution-free, density is low; the application of various materials can be widely used in, good protection effect can be played.
Summary of the invention
The object of the invention is just to provide a kind of top fabric coating.
The present invention is achieved by the following technical solutions:
A top fabric coating, it is comprised of the raw material of following weight parts:
Polypropylene 73-80, benzyl triphenyl phosphonium chloride phosphine 0.6-1, oxine 1-2, bamboo fibers 2-3, Imarcaptoacetate dioctyltin 0.8-1.3, Natvosol 1-2, water-ground limestone 10-13,3-aminopropyl trimethoxysilane 1-2, dioctyl phthalate (DOP) 12-14, phenylpropyl alcohol triazole 1-2, Calcium Chloride Powder Anhydrous 3-5, compounded mix 14-18;
Described compounded mix is comprised of the raw material of following weight parts:
Agalmatolite 25-30, fine hair powder 10-13, methylisothiazolinone 2-3, linear low density polyethylene 15-25, Xylo-Mucine 1-2, tricresyl phosphate (butoxyethyl group) ester 1-2, Terpineol 350 1-2;
Above-mentioned agalmatolite is calcined to 1-2 hour at 600-700 ℃, after discharging is cooling, add methylisothiazolinone, linear low density polyethylene, pulverize, Xylo-Mucine is joined in 6-10 times of water, after stirring, add fine hair powder, at 60-70 ℃, be uniformly mixed 4-6 minute, mix with powder obtained above, add each raw material of residue, fully grind, dry, cross 60-80 mesh sieve, obtain described compounded mix.
A preparation method for coating for top fabric, comprises the following steps:
Above-mentioned Natvosol, bamboo fibers, water-ground limestone are mixed, add 3-aminopropyl trimethoxysilane, at 50-60 ℃, 200-300 rev/min of dispersed with stirring 4-6 minute, adds phenylpropyl alcohol triazole, is stirred to normal temperature, add each raw material of residue, mix, send into twin screw extruder, carry out melting, extrude, cross 60-100 mesh sieve, obtain described top fabric coating.
Using method:
By paint heating melting, then coating piece is infiltrated, can to coating, exert pressure to control by rubber rollers the thickness of glue-line, then through plasticizing, cooling.
Advantage of the present invention is:
After coating of the present invention applies, the wear resistance of product is good, lighter, and waterproof ability is strong, cheap, is specially adapted to, as hood for motor car drop cloth, be widely used in various occasions.
Embodiment
Embodiment 1
A top fabric coating, it by following weight parts (kilogram) raw material form:
Polypropylene 80, benzyl triphenyl phosphonium chloride phosphine 0.6, oxine 2, bamboo fibers 3, Imarcaptoacetate dioctyltin 1.3, Natvosol 1, water-ground limestone 13,3-aminopropyl trimethoxysilane 1, dioctyl phthalate (DOP) 14, phenylpropyl alcohol triazole 2, Calcium Chloride Powder Anhydrous 3, compounded mix 18;
Described compounded mix is comprised of the raw material of following weight parts:
Agalmatolite 30, fine hair powder 13, methylisothiazolinone 3, linear low density polyethylene 25, Xylo-Mucine 2, tricresyl phosphate (butoxyethyl group) ester 2, Terpineol 350 2;
Above-mentioned agalmatolite is calcined 2 hours at 700 ℃, after discharging is cooling, add methylisothiazolinone, linear low density polyethylene, pulverize, Xylo-Mucine is joined in 10 times of water, after stirring, add fine hair powder, at 70 ℃, be uniformly mixed 4 minutes, mix with powder obtained above, add each raw material of residue, fully grind, dry, cross 80 mesh sieves, obtain described compounded mix.
A preparation method for coating for top fabric, comprises the following steps:
Above-mentioned Natvosol, bamboo fibers, water-ground limestone are mixed, add 3-aminopropyl trimethoxysilane, at 60 ℃, 300 revs/min of dispersed with stirring are 6 minutes, add phenylpropyl alcohol triazole, are stirred to normal temperature, add each raw material of residue, mix, send into twin screw extruder, carry out melting, extrude, cross 100 mesh sieves, obtain described top fabric coating.
Performance test:
Shock resistance: >=50kg/cm;
Pencil hardness test: 2H is without scuffing.
Claims (2)
1. a top fabric coating, is characterized in that what it was comprised of the raw material of following weight parts:
Polypropylene 73-80, benzyl triphenyl phosphonium chloride phosphine 0.6-1, oxine 1-2, bamboo fibers 2-3, Imarcaptoacetate dioctyltin 0.8-1.3, Natvosol 1-2, water-ground limestone 10-13,3-aminopropyl trimethoxysilane 1-2, dioctyl phthalate (DOP) 12-14, phenylpropyl alcohol triazole 1-2, Calcium Chloride Powder Anhydrous 3-5, compounded mix 14-18;
Described compounded mix is comprised of the raw material of following weight parts:
Agalmatolite 25-30, fine hair powder 10-13, methylisothiazolinone 2-3, linear low density polyethylene 15-25, Xylo-Mucine 1-2, tricresyl phosphate (butoxyethyl group) ester 1-2, Terpineol 350 1-2;
Above-mentioned agalmatolite is calcined to 1-2 hour at 600-700 ℃, after discharging is cooling, add methylisothiazolinone, linear low density polyethylene, pulverize, Xylo-Mucine is joined in 6-10 times of water, after stirring, add fine hair powder, at 60-70 ℃, be uniformly mixed 4-6 minute, mix with powder obtained above, add each raw material of residue, fully grind, dry, cross 60-80 mesh sieve, obtain described compounded mix.
2. a preparation method for coating for top fabric as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned Natvosol, bamboo fibers, water-ground limestone are mixed, add 3-aminopropyl trimethoxysilane, at 50-60 ℃, 200-300 rev/min of dispersed with stirring 4-6 minute, adds phenylpropyl alcohol triazole, is stirred to normal temperature, add each raw material of residue, mix, send into twin screw extruder, carry out melting, extrude, cross 60-100 mesh sieve, obtain described top fabric coating.