CN103921091A - Copper ware manufacturing method - Google Patents
Copper ware manufacturing method Download PDFInfo
- Publication number
- CN103921091A CN103921091A CN201410128196.2A CN201410128196A CN103921091A CN 103921091 A CN103921091 A CN 103921091A CN 201410128196 A CN201410128196 A CN 201410128196A CN 103921091 A CN103921091 A CN 103921091A
- Authority
- CN
- China
- Prior art keywords
- copper
- blank
- crucible
- ware
- forging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the technical field of metal forging, particularly relates to a copper ware manufacturing method, and mainly solves the problems that homemade metal containers in rural areas are rough in technology, poor in reproducibility, and the like. According to the technical scheme, the method includes: placing copper in a crucible, adding zinc 1% of the weight of copper in the crucible, heating the crucible on fire until both the copper and the zinc melt, pouring the molten copper and zinc into a copper ware die to obtain a copper ware blank after cooling, heating the blank on fire until the blank is red, forging the blank to achieve required thickness, then forging the blank on a stone die, welding while heating on a furnace after forging, adding borax and welding flux on the blank, and heating while pulling the thin copper bar to weld seams. The copper ware manufacturing method has the advantages that the manufactured copper ware is simple to manufacture, solid and durable, and the like.
Description
Technical field
The invention belongs to metal forging technical field, be specifically related to a kind of bronze, brass or copper ware preparation method.
Background technology
Agricultural production has advanced social development greatly, various supporting metal farm implements, cooker, apparatus be also multifarious, emerge in an endless stream.People are the exploitation situation of mineral matter as required and around, and the material of container has plastics, glass, aluminium, iron, copper etc., and different, purposes differs.
Summary of the invention
The problems such as the present invention is coarse mainly for rural area self-control canister technology, reproducibility is poor, provide a kind of simple, durable bronze, brass or copper ware preparation method of making.
The technical scheme that the present invention takes is for achieving the above object:
A kind of bronze, brass or copper ware preparation method, wherein: first copper material is put in crucible, in crucible, add again the metallic zinc of copper material weight 1%, then crucible is placed on to the copper material and the metallic zinc that on fire, are heated in crucible and is all fused into liquid water, liquid water is poured in the mould of bronze, brass or copper ware, after to be cooled, bronze, brass or copper ware blank has just been cast, after blank is cast, again blank is placed on to the red work of making of the upper burning of fire, when getting to the thickness of requirement, will be placed on Shi Mo above beats, after making into, weld again, during welding, just on stove, heat, add borax and welding agent, above being placed on, make a fire on one side, pull thin copper bar on one side, crack has just welded.
The present invention adopts technique scheme, and a kind of bronze, brass or copper ware preparation method can be provided, and by the method, can very simply make bronze, brass or copper ware by oneself, does not require elegant in appearancely, seeks only practicality, has brought enough facilities to people's life.
The specific embodiment
Embodiment 1
A kind of bronze, brass or copper ware preparation method, wherein: first copper material is put in crucible, in crucible, add again the metallic zinc of copper material weight 1%, then crucible is placed on to the copper material and the metallic zinc that on fire, are heated in crucible and is all fused into liquid water, liquid water is poured in the mould of bronze, brass or copper ware, after to be cooled, bronze, brass or copper ware blank has just been cast, after blank is cast, again blank is placed on to the red work of making of the upper burning of fire, when getting to the thickness of requirement, will be placed on Shi Mo above beats, after making into, weld again, during welding, just on stove, heat, add borax and welding agent, above being placed on, make a fire on one side, pull thin copper bar on one side, crack has just welded.
Claims (1)
1. a bronze, brass or copper ware preparation method, it is characterized in that: first copper material is put in crucible, in crucible, add again the metallic zinc of copper material weight 1%, then crucible is placed on to the copper material and the metallic zinc that on fire, are heated in crucible and is all fused into liquid water, liquid water is poured in the mould of bronze, brass or copper ware, after to be cooled, bronze, brass or copper ware blank has just been cast, after blank is cast, again blank is placed on to the red work of making of the upper burning of fire, when getting to the thickness of requirement, will be placed on Shi Mo above beats, after making into, weld again, during welding, just on stove, heat, add borax and welding agent, above being placed on, make a fire on one side, pull thin copper bar on one side, crack has just welded.