CN103709652A - 聚对苯二甲酸乙二醇酯用色母粒及其制备方法 - Google Patents
聚对苯二甲酸乙二醇酯用色母粒及其制备方法 Download PDFInfo
- Publication number
- CN103709652A CN103709652A CN201210372836.5A CN201210372836A CN103709652A CN 103709652 A CN103709652 A CN 103709652A CN 201210372836 A CN201210372836 A CN 201210372836A CN 103709652 A CN103709652 A CN 103709652A
- Authority
- CN
- China
- Prior art keywords
- polyethylene terephthalate
- pigment
- masterbatch
- preparation
- polyethylene glycol
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种聚对苯二甲酸乙二醇酯用色母粒及其制备方法。本发明的聚对苯二甲酸乙二醇酯用色母粒，其组分按质量百分数配比为：载体20%～70%、颜料20%～70%、分散剂0.1%～5%、抗氧剂0.1%～1%。本发明的有益效果是，采用三元共聚树脂作为载体，与聚对苯二甲酸乙二醇酯具有良好的相容性，而且还可以减小结晶度，降低熔点和黏度，增加流动性等，同时，本发明通过研磨在颜料表面包覆一层高聚物保护层，使颜料间失去吸附成团聚体和凝聚体的能力，从而保证了该色母粒的分散性。
Description
技术领域
本发明涉及塑料着色领域，具体地说是一种聚对苯二甲酸乙二醇酯用色母粒及其制备方法。
背景技术
聚对苯二甲酸乙二醇酯（PET）是一种结晶性聚合物，由于它具有优异的机械强度、电绝缘性、耐热性和耐化学品性，因而它主要应用于合成纤维、电器绝缘材料和胶片等领域。作为工程塑料应用时，PET材料耐蠕变性、耐疲劳性及耐摩擦与磨损性极为突出，其综合性能优于聚酰胺和聚碳酸酯。然而，PET一般情况下很难着色，目前国内外采用PET、蜡、三元共聚物等作为PET着色母料的载体，虽然得到广泛的应用，却表现出一些局限性或缺陷，例如，对母料的要求尤为严格的透明制品生产中，一个气泡、漩纹线、色痕都会是透明制品的致命缺陷；目前PET的着色剂、色母一般都是直接加入原料内一起烘料，因而这些粉末着色剂、低温熔融母料很容易存在下列缺点：低温熔融着色母料在下料口提前熔融，影响喂料；液体着色剂很容易粘在下料口死角、螺杆，长时间受热后，烧焦形成黑点等。
发明内容
本发明的目的在于提供一种分散性好、着色性强和使用方便的聚对苯二甲酸乙二醇酯用色母粒及其制备方法。
本发明解决其技术问题所采用的技术方案是：聚对苯二甲酸乙二醇酯用色母粒，其组分按质量百分数配比为：载体20%～70%、颜料20%～70%、分散剂0.1%～5%、抗氧剂0.1%～1%。
所述的载体为三元共聚树脂，是由对苯二甲酸二元醇酯、间苯二甲酸二元醇酯、对苯二甲酸多元醇酯的三种单体混合的共缩聚合物。
所述的颜料为粉状和耐热温度不小于300℃的无机颜料或有机颜料，所述的无机颜料为钛白粉（二氧化钛）、炭黑、铬黄、氧化铁红和铁蓝中的一种，所述的有机颜料为偶氮颜料、酞菁颜料和杂环颜料中的一种。
所述的分散剂为聚乙二醇、三羟甲基乙烷、硬脂酸金属盐、聚乙烯吡咯烷酮或铝钛复合偶联剂中的一种。
所述的抗氧剂为受阻酚抗氧剂1010或1076与亚磷酸酯类抗氧剂168的复配物。
上述的聚对苯二甲酸乙二醇酯用色母粒的制备方法为：将各组分按重量比例配料，然后加入以二氧六环为溶剂、在70℃～80℃温度下研磨15～20小时，使其粒度最大不超过2μm，再通过减压过滤、沉淀、过滤、洗涤滤饼的一系列工序以除去溶剂，然后进行干燥、浓缩并粉碎、造粒后包装即得聚对苯二甲酸乙二醇酯用色母粒。
本发明的有益效果是，采用三元共聚树脂作为载体，与聚对苯二甲酸乙二醇酯具有良好的相容性，而且还可以减小结晶度，降低熔点和黏度，增加流动性等，同时，本发明通过研磨在颜料表面包覆一层高聚物保护层，使颜料间失去吸附成团聚体和凝聚体的能力，从而保证了该色母粒的分散性。
具体实施方式
下面结合具体实施例来进一步说明本发明的技术方案。
实施例1：
一种聚对苯二甲酸乙二醇酯用色母粒，其组分按质量百分数配比为：三元共聚树脂48%、钛白粉（二氧化钛）48%、聚乙二醇3.5%、受阻酚抗氧剂1010与亚磷酸酯类抗氧剂168的复配物0.5%，其中，三元共聚树脂是由对苯二甲酸二元醇酯、间苯二甲酸二元醇酯、对苯二甲酸多元醇酯的三种单体混合的共缩聚合物。
制备方法：将各组分按重量比例配料，然后加入以二氧六环为溶剂、在70℃～80℃温度下研磨15～20小时，使其粒度最大不超过2μm，再通过减压过滤、沉淀、过滤、洗涤滤饼的一系列工序以除去溶剂，然后进行干燥、浓缩并粉碎、造粒后包装即得聚对苯二甲酸乙二醇酯用色母粒。
实施例2：
一种聚对苯二甲酸乙二醇酯用色母粒，其组分按质量百分数配比为：三元共聚树脂25%、炭黑70%、硬脂酸金属盐4%、受阻酚抗氧剂1010与亚磷酸酯类抗氧剂168的复配物1%，其中，三元共聚树脂是由对苯二甲酸二元醇酯、间苯二甲酸二元醇酯、对苯二甲酸多元醇酯的三种单体混合的共缩聚合物。
制备方法：将各组分按重量比例配料，然后加入以二氧六环为溶剂、在70℃～80℃温度下研磨15～20小时，使其粒度最大不超过2μm，再通过减压过滤、沉淀、过滤、洗涤滤饼的一系列工序以除去溶剂，然后进行干燥、浓缩并粉碎、造粒后包装即得聚对苯二甲酸乙二醇酯用色母粒。
实施例3：
一种聚对苯二甲酸乙二醇酯用色母粒，其组分按质量百分数配比为：三元共聚树脂70%、酞菁颜料28%、铝钛复合偶联剂1.5%、受阻酚抗氧剂1076与亚磷酸酯类抗氧剂168的复配物0.5%，其中，三元共聚树脂是由对苯二甲酸二元醇酯、间苯二甲酸二元醇酯、对苯二甲酸多元醇酯的三种单体混合的共缩聚合物，酞菁颜料为粉状和耐热温度不小于300℃。
制备方法：将各组分按重量比例配料，然后加入以二氧六环为溶剂、在70℃～80℃温度下研磨15～20小时，使其粒度最大不超过2μm，再通过减压过滤、沉淀、过滤、洗涤滤饼的一系列工序以除去溶剂，然后进行干燥、浓缩并粉碎、造粒后包装即得聚对苯二甲酸乙二醇酯用色母粒。
Claims (6)
1.一种聚对苯二甲酸乙二醇酯用色母粒，其特征在于，其组分按质量百分数配比为：载体20%～70%、颜料20%～70%、分散剂0.1%～5%、抗氧剂0.1%～1%。
2.根据权利要求1所述的聚对苯二甲酸乙二醇酯用色母粒，其特征在于，所述的载体为三元共聚树脂，是由对苯二甲酸二元醇酯、间苯二甲酸二元醇酯、对苯二甲酸多元醇酯的三种单体混合的共缩聚合物。
3.根据权利要求1所述的聚对苯二甲酸乙二醇酯用色母粒，其特征在于，所述的颜料为粉状和耐热温度不小于300℃的无机颜料或有机颜料，所述的无机颜料为钛白粉（二氧化钛）、炭黑、铬黄、氧化铁红和铁蓝中的一种，所述的有机颜料为偶氮颜料、酞菁颜料和杂环颜料中的一种。
4.根据权利要求1所述的聚对苯二甲酸乙二醇酯用色母粒，其特征在于，所述的分散剂为聚乙二醇、三羟甲基乙烷、硬脂酸金属盐、聚乙烯吡咯烷酮或铝钛复合偶联剂中的一种。
5.根据权利要求1所述的聚对苯二甲酸乙二醇酯用色母粒，其特征在于，所述的抗氧剂为受阻酚抗氧剂1010或1076与亚磷酸酯类抗氧剂168的复配物。
6.根据权利要求1所述的聚对苯二甲酸乙二醇酯用色母粒的制备方法，其特征在于，包括以下步骤：将各组分按重量比例配料，然后加入以二氧六环为溶剂、在70℃～80℃温度下研磨15～20小时，使其粒度最大不超过2μm，再通过减压过滤、沉淀、过滤、洗涤滤饼的一系列工序以除去溶剂，然后进行干燥、浓缩并粉碎、造粒后包装即得聚对苯二甲酸乙二醇酯用色母粒。