CN103290681A - Resin finishing technology of fabrics - Google Patents
Resin finishing technology of fabrics Download PDFInfo
- Publication number
- CN103290681A CN103290681A CN 201310247310 CN201310247310A CN103290681A CN 103290681 A CN103290681 A CN 103290681A CN 201310247310 CN201310247310 CN 201310247310 CN 201310247310 A CN201310247310 A CN 201310247310A CN 103290681 A CN103290681 A CN 103290681A
- Authority
- CN
- China
- Prior art keywords
- fabric
- fabrics
- technology
- resin finish
- resin
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a resin finishing technology of fabrics. The fabrics comprise unpigmented viscose fiber fabrics, cotton fiber fabrics, and blended fabrics of cotton fibers and chemical fibers. The technology comprises the following steps: padding the fabrics in a resin finishing liquid; taking out the padded fabrics, allowing the padded fabrics to stand at normal temperature for 24-48h, and pre-drying at 95-105DEG C for 1-3min until the water content of the fabrics is 10-12%; allowing the fabrics to enter a stenter, and curing at 130-150DEG C for 5-10min; and completely cleaning with normal temperature water. By adopting the above mode, the technology can improve all performances of the fabrics, makes the fabrics have good wrinkle and shrink resistance, a good wear resistance, a good breaking strength and a good tearing strength, and has the advantages of operation saving, energy consumption reduction and cost saving.
Description
Technical field
The present invention relates to the weaving face fabric processing technology field, particularly relate to a kind of RESIN FINISH technology of fabric.
Background technology
RESIN FINISH is that a kind of synthetic resin that utilizes is handled fabric, makes fabric obtain the processing method of special finishing effect.Adopt the resin of different performance, can get different finishing effects, as wrinkle resistant, shrinkproof, waterproof, fire prevention etc.In recent years, along with science and technology development, the RESIN FINISH technology of fabric has been mentioned development greatly, is mainly used in the wrinkle resistant shrinkproof and durable crease-proof finishing of fabric.
Existing finishing technique is complicated, has certain defective in the allotment of resin finishing agent, makes energy consumption height in the whole arrangement process, and the loss of finishing agent is big, and every performance of fabric is wayward, causes the ABRASION RESISTANCE of fabric and fracture strength to descend easily.
Summary of the invention
The technical problem that the present invention mainly solves provides a kind of RESIN FINISH technology of fabric, can improve every performance of fabric, make fabric have good wrinkle resistant shrinkproof performance, anti-wear performance, ultimate strength and tearing brute force etc., and can save operation, cut down the consumption of energy, save cost.
For solving the problems of the technologies described above, the technical scheme that the present invention adopts is: the RESIN FINISH technology that a kind of fabric is provided, described fabric comprises the BLENDED FABRIC of viscose fiber fabric, cotton fabric, cotton fiber and chemical fiber before the dyeing, may further comprise the steps: earlier described fabric is padded in RESIN FINISH liquid; Fabric after then will padding takes out, and leaves standstill under the normal temperature 24-48 hour, and under 95-105 ℃ of temperature preliminary drying 1-3 minute then is 10%-12% with fabric drying to moisture; Then described fabric is entered stenter, under 130-150 ℃ of temperature, baked 5-10 minute; Then rinse well with normal-temperature water at last.
In a preferred embodiment of the present invention, contain resin finishing agent 55-60g/L, catalyst 13-15 g/L, softener 10-15 g/L, protective agent 8-12g/L and bleeding agent 1-2 g/L in the described RESIN FINISH liquid.
In a preferred embodiment of the present invention, the described pick-up that pads is 68%-72%.
In a preferred embodiment of the present invention, described catalyst comprises magnesium chloride and citric acid.
The invention has the beneficial effects as follows: by the moisture of fabric behind the control pick-up of fabric and the preliminary drying, and adopt the tentering oven dry, reduce the time of curing, and saved finishing process, reduced energy consumption, saved cost; Adopt the various auxiliary agents of reasonable distribution to dispose the RESIN FINISH liquid that forms, can improve every performance of fabric, make fabric have good wrinkle resistant shrinkproof performance, anti-wear performance, ultimate strength and tearing brute force etc.
The specific embodiment
Below preferred embodiment of the present invention is described in detail, thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
The embodiment of the invention comprises:
A kind of RESIN FINISH technology of fabric, described fabric comprise the BLENDED FABRIC of viscose fiber fabric, cotton fabric, cotton fiber and chemical fiber before the dyeing, may further comprise the steps: earlier described fabric is padded in RESIN FINISH liquid; Fabric after then will padding takes out, and leaves standstill under the normal temperature 24-48 hour, and under 95-105 ℃ of temperature preliminary drying 1-3 minute then is 10%-12% with fabric drying to moisture; Then described fabric is entered stenter, under 130-150 ℃ of temperature, baked 5-10 minute; Then rinse well with normal-temperature water at last.
Wherein, contain resin finishing agent 55-60g/L, catalyst 13-15 g/L, softener 10-15 g/L, protective agent 8-12g/L and bleeding agent 1-2 g/L in the described RESIN FINISH liquid.
The described pick-up that pads is 68%-72%.
Described catalyst comprises magnesium chloride and citric acid.
Embodiment one:
A kind of RESIN FINISH technology of fabric, described fabric comprise the BLENDED FABRIC of viscose fiber fabric, cotton fabric, cotton fiber and chemical fiber before the dyeing, may further comprise the steps: earlier described fabric is padded in RESIN FINISH liquid; Fabric after then will padding takes out, and leaves standstill under the normal temperature 24-48 hour, and preliminary drying 2 minutes under 95 ℃ of temperature is 12% with fabric drying to moisture then; Then described fabric is entered stenter, under 145 ℃ of temperature, baked 10 minutes; Then rinse well with normal-temperature water at last.
Wherein, contain 2D resin finishing agent 60g/L, magnesium chloride (catalyst) 13 g/L, citric acid 0.5 g/L, ester based quaternary ammonium salt softener 10 g/L, polyethylene emulsion (protective agent) 12g/L and JFC bleeding agent 1.5 g/L in the described RESIN FINISH liquid.
The described pick-up that pads is 71%.
Embodiment two:
A kind of RESIN FINISH technology of fabric, described fabric comprise the BLENDED FABRIC of viscose fiber fabric, cotton fabric, cotton fiber and chemical fiber before the dyeing, may further comprise the steps: earlier described fabric is padded in RESIN FINISH liquid; Fabric after then will padding takes out, and leaves standstill under the normal temperature 24-48 hour, and preliminary drying 1.5 minutes under 100 ℃ of temperature is 10% with fabric drying to moisture then; Then described fabric is entered stenter, under 135 ℃ of temperature, baked 8 minutes; Then rinse well with normal-temperature water at last.
Wherein, contain 2D resin finishing agent 60g/L, magnesium chloride (catalyst) 14.5 g/L, citric acid 0.3 g/L, ester based quaternary ammonium salt softener 15 g/L, polyethylene emulsion (protective agent) 10g/L and JFC bleeding agent 1 g/L in the described RESIN FINISH liquid.
The described pick-up that pads is 68%.
The present invention has disclosed a kind of RESIN FINISH technology of fabric, by the moisture of fabric behind the control pick-up of fabric and the preliminary drying, and adopts the tentering oven dry, reduces the time of curing, and has saved finishing process, has reduced energy consumption, has saved cost; Adopt the various auxiliary agents of reasonable distribution to dispose the RESIN FINISH liquid that forms, can improve every performance of fabric, make fabric have good wrinkle resistant shrinkproof performance, anti-wear performance, ultimate strength and tearing brute force etc.
The above only is embodiments of the invention; be not so limit claim of the present invention; every equivalent structure or equivalent flow process conversion that utilizes description of the present invention to do; or directly or indirectly be used in other relevant technical fields, all in like manner be included in the scope of patent protection of the present invention.
Claims (4)
1. the RESIN FINISH technology of a fabric, described fabric comprise the BLENDED FABRIC of viscose fiber fabric, cotton fabric, cotton fiber and chemical fiber before the dyeing, it is characterized in that, may further comprise the steps: earlier described fabric is padded in RESIN FINISH liquid; Fabric after then will padding takes out, and leaves standstill under the normal temperature 24-48 hour, and under 95-105 ℃ of temperature preliminary drying 1-3 minute then is 10%-12% with fabric drying to moisture; Then described fabric is entered stenter, under 130-150 ℃ of temperature, baked 5-10 minute; Then rinse well with normal-temperature water at last.
2. the RESIN FINISH technology of fabric according to claim 1 is characterized in that, contains resin finishing agent 55-60g/L, catalyst 13-15 g/L, softener 10-15 g/L, protective agent 8-12g/L and bleeding agent 1-2 g/L in the described RESIN FINISH liquid.
3. the RESIN FINISH technology of fabric according to claim 1 is characterized in that, the described pick-up that pads is 68%-72%.
4. the RESIN FINISH technology of fabric according to claim 1 is characterized in that, described catalyst comprises magnesium chloride and citric acid.