CN103242796B - 一种紫外光固化液态光学胶及其制备方法 - Google Patents
一种紫外光固化液态光学胶及其制备方法 Download PDFInfo
- Publication number
- CN103242796B CN103242796B CN201310196382.5A CN201310196382A CN103242796B CN 103242796 B CN103242796 B CN 103242796B CN 201310196382 A CN201310196382 A CN 201310196382A CN 103242796 B CN103242796 B CN 103242796B
- Authority
- CN
- China
- Prior art keywords
- acrylate
- methyl
- optical cement
- grams
- ultraviolet light
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
一种紫外光固化液态光学胶，其特征在于由下述重量配比的组分组成：聚氨酯丙烯酸酯低聚物40－70份，（甲基）丙烯酸酯20－40份，光引发剂0.1－5份，硅烷偶联剂1－10份，助剂0－10份。本发明还提供上述紫外光固化液态光学胶的一种制备方法。本发明的紫外光固化液态光学胶除了具有外观透明、粘度稳定、固化需要能量低、固化速度快、折射率高等特性外，还具有下述优良特性：粘结强度大，固化后硬度低且柔韧性好，耐候性极佳。
Description
技术领域
本发明涉及胶粘剂，具体涉及一种用于触摸屏贴装的紫外光固化液态光学胶，以及这种紫外光固化液态光学胶的制备方法。
背景技术
触摸屏由于将良好的视觉呈现与便利的直觉系统操作相结合，近年来在手机、平板电脑、电视机、车用导航系统等电子产品中得到越来越广泛的应用。
目前，在触摸屏制造中，大多使用液态光学胶（Liquid Optical Clear Adhesive，LOCA）作为各基材间粘接的胶粘剂，现有的液态光学胶能够满足一些基本要求，如：无色透明，特定光波波段内透过率为90%以上，固化后折射率与被粘基材的折射率相近等。但是，现有的液态光学胶普遍存在粘结强度弱、固化后硬脆、柔韧性差、耐候性差等问题，极大地降低了触摸屏产品自身的质量稳定期限。
发明内容
本发明所要解决的技术问题是提供一种用于触摸屏贴装的紫外光固化液态光学胶以及这种紫外光固化液态光学胶的制备方法，这种紫外光固化液态光学胶粘结强度大，固化后硬度低且柔韧性好，耐候性极佳。采用的技术方案如下：
一种紫外光固化液态光学胶，其特征在于由下述重量配比的组分组成：聚氨酯丙烯酸酯低聚物40－70份，（甲基）丙烯酸酯20－40份，光引发剂0.1－5份，硅烷偶联剂1－10份，助剂0－10份。
优选上述聚氨酯丙烯酸酯低聚物是平均粘度为20000－70000cps、平均分子量为10000－50000、官能度为1－3的聚氨酯丙烯酸酯。上述聚氨酯丙烯酸酯低聚物由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成。低的官能度使得交联度降低，从而降低了硬度；超长链段的多元醇结构，提高了胶体的柔韧性，从而降低了硬度；异腈酸酯基的作用，使聚氨酯丙烯酸酯本身具有较强的内聚力，从而提高胶体的粘结强度。
上述（甲基）丙烯酸酯是丙烯酸酯和甲基丙烯酸酯的合称。优选上述（甲基）丙烯酸酯是含长链段的（甲基）丙烯酸酯，或带羟基结构的（甲基）丙烯酸酯，或带杂环结构的（甲基）丙烯酸酯，或带多环苯的（甲基）丙烯酸酯。长链段的存在，能提高胶体的柔韧性；羟基的存在，因能生成氢键，从而提高胶体对玻璃的粘结力；杂环（包括但不限于环烷烃、苯环、环氧等）的存在，有助于提高胶体的强度及粘结力；多环苯的结构可提高胶体的折射率；长链段或脂环结构还能提高胶体的疏水性、耐水煮性能、耐高温高湿性能。
更优选方案中，上述（甲基）丙烯酸酯是丙烯酸羟乙酯、甲基丙烯酸羟乙酯、4-羟基丁基丙烯酸酯、丙烯酸-2-羟丙酯、甲基丙烯酸羟丙酯、2-羟基-2-丙烯酸丁基酯、1,4-环己烷二甲醇单丙烯酸酯、1,4-环己烷二甲醇甲基丙烯酸酯、1-氯-2-羟丙基丙烯酸酯、1-氯-2-羟丙基甲基丙烯酸酯、二乙二醇单丙烯酸酯、二甘醇丙烯酸甲酯、1,6-己二醇单丙烯酸酯、1,6-己二醇二丙烯酸酯、季戊四醇三丙烯酸酯、聚二季戊四醇五丙烯酸酯、三羟甲基丙烷二甲基丙烯酸酯、丙烯酸异冰片酯、甲基丙烯酸异冰片酯、环戊基丙烯酸酯、环戊基丙烯酸甲酯、2-丙烯酸环己基酯、2-甲基丙烯酸环己酯、双环苯氧乙基丙烯酸酯、丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸乙酯、丙烯酸丙酯、丙基-2-甲基-2-丙烯酸酯、丙烯酸异丙酯、甲基丙烯酸正丁酯、丙烯酸正丁酯、甲基丙烯酸叔丁酯、丙烯酸异丁酯、甲基丙烯酸异丁酯、丙烯酸正戊酯、甲基丙烯酸戊酯、丙烯酸正辛酯、丙烯酸异辛酯、甲基丙烯酸异辛酯、丙烯酸癸酯、甲基丙烯酸癸酯、甲基丙烯酸十一烷基酯、2-丙烯酸十二烷基酯、丙烯酸月桂酯和甲基丙烯酸月桂酯中的一种或其中多种的组合。
上述光引发剂主要起到吸收紫外光，从而激发以提供自由基，使反应顺利进行的作用。光引发剂的有效官能团包括但不限于苯偶姻类、苯乙酮类、a-羟基酮类、酰基膦氧化物、a-氨基酮类等。优选上述光引发剂是四乙基米氏酮、苯甲酮、1-羟基环己基苯基甲酮、丙烯酸酯苯甲酮、苯基二苯甲酮、羟基二苯甲酮、4,4'-二(N,N-二甲氨基)二苯甲酮、2,2'-二乙氧基苯乙酮、2-羟基-2-苯基苯乙酮、2-羟基-2-甲基-1-苯基-1-丙酮、2,4,6-三甲基苯甲酰-二苯基氧化膦、双（2,4,6-三甲基苯甲酰基）苯基氧化膦、安息香甲醚、安息香乙醚和三聚氯氰中的一种或其中多种的组合。
上述硅烷偶联剂的可水解基团水解生成硅醇，与无机物质（如玻璃）结合形成硅氧烷；另外，硅烷偶联剂的有机官能团与丙烯酸单体共聚，在无机物质和有机物质之间架起“分子桥”，使紫外光固化液态光学胶具有优异的粘结力。优选上述硅烷偶联剂是三甲氧基甲硅烷、乙烯基三乙氧基硅烷、3-三甲氧基硅烷丙烯酸丙脂、3-甲基丙烯酰氧丙基三甲氧基硅烷、3-(2,3-环氧丙氧)丙基三甲氧基硅烷、3-[(2,3)-环氧丙氧]丙基甲基二甲氧基硅烷、三甲氧基[2-(7-氧杂二环[4.1.0]庚-3-基)乙基]硅烷、3-氨基丙基三甲氧基硅烷（即偶联剂KH-540）和3-氯丙基三甲氧基硅烷中的一种或其中多种的组合。
上述助剂可以是增塑剂、消泡剂和光稳定剂中的一种或其多种的组合。
上述增塑剂用来增加聚合物的柔软性，其折射率一般要求1.48以上。优选上述增塑剂是邻苯二甲酸酯、磷酸酯（如磷酸三苯酯）、烷基磺酸酯、脂肪族二元酸酯（如己二酸二（2-乙基）己酯、癸二酸二正己酯）、苯多酸酯和环氧化合物中的一种或其中多种的组合。
上述消泡剂用来抑制、降低或消除聚合物中的气泡。优选上述消泡剂是磷酸三丁酯、聚二甲基硅氧烷、聚丙烯酸酯和聚醚中的一种或其中多种的组合。
上述光稳定剂用来抑制或减缓聚合物光氧老化过程。优选上述光稳定剂是双(1,2,2,6,6-五甲基-4-哌啶)癸二酸酯、1-甲基-8-(1,2,2,6,6-五甲基-4-哌啶)癸二酸酯、4-羟基-2,2,6,6-四甲基-1-哌啶醇、双（3,5-二叔丁基-4-羟基苄基磷酸单乙酯）镍、2-（2’-羟基-3’,5-二叔丁基苯基）苯并三唑和2-羟基-4-正辛氧基二本甲酮中的一种或其中多种的组合。
本发明还提供上述紫外光固化液态光学胶的一种制备方法，其特征在于依次包括下述步骤：
（1）按重量计，取40－70份聚氨酯丙烯酸酯低聚物、20－40份（甲基）丙烯酸酯、0.1－5份光引发剂、1－10份硅烷偶联剂和0－10份助剂，并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1000－1500转/分钟的条件下搅拌至混合均匀（优选搅拌时间为30－60分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（优选脱泡时间为20－30分钟），得到紫外光固化液态光学胶。
为确保紫外光固化液态光学胶的纯净度，在步骤（2）进行脱泡之前，对步骤（1）得到的胶料进行过滤，除去其中的杂质（杂质是来自环境中和沾染在生产设备上的灰尘等物质）。优选用于过滤的滤膜孔径为1－20um。
本发明的紫外光固化液态光学胶除了具有外观透明、粘度稳定、固化需要能量低、固化速度快、折射率高等特性外，还具有下述优良特性：粘结强度大，固化后硬度低且柔韧性好，耐候性极佳。
具体实施方式
实施例1
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取67克聚氨酯丙烯酸酯低聚物（均为平均粘度为50000cps、平均分子量为50000、官能度为2的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、20克（甲基）丙烯酸酯（均为1,4-环己烷二甲醇甲基丙烯酸酯）、5克光引发剂（均为苯基二苯甲酮）、6克硅烷偶联剂（均为乙烯基三乙氧基硅烷）和2克助剂（均为增塑剂己二酸二（2-乙基）己酯），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1200转/分钟的条件下搅拌至混合均匀（搅拌时间为50分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为25分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物67克（均为平均粘度为50000cps、平均分子量为50000、官能度为2的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、（甲基）丙烯酸酯20克（均为1,4-环己烷二甲醇甲基丙烯酸酯）、光引发剂5克（均为苯基二苯甲酮）、硅烷偶联剂6克（均为乙烯基三乙氧基硅烷）和助剂2克（均为增塑剂己二酸二（2-乙基）己酯）。
批量生产时按上述比例配备原料即可。
实施例2
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取55克聚氨酯丙烯酸酯低聚物（均为平均粘度为40000cps、平均分子量为35000、官能度为1的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、32克（甲基）丙烯酸酯（均为甲基丙烯酸异冰片酯）、2克光引发剂（均为2,2’-二乙氧基苯乙酮）、1克硅烷偶联剂（均为3-甲基丙烯酰氧丙基三甲氧基硅烷）和10克助剂（均为增塑剂癸二酸二正己酯），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1500转/分钟的条件下搅拌至混合均匀（搅拌时间为30分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为20分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物55克（均为平均粘度为40000cps、平均分子量为35000、官能度为1的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、（甲基）丙烯酸酯32克（均为甲基丙烯酸异冰片酯）、光引发剂2克（均为2,2’-二乙氧基苯乙酮）、硅烷偶联剂1克（均为3-甲基丙烯酰氧丙基三甲氧基硅烷）和助剂10克（均为增塑剂癸二酸二正己酯）。
批量生产时按上述比例配备原料即可。
实施例3
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取60克聚氨酯丙烯酸酯低聚物（均为平均粘度为45000cps、平均分子量为40000、官能度为1.5的聚氨酯甲基丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、33克（甲基）丙烯酸酯（其中甲基丙烯酸异辛酯20克、甲基丙烯酸异冰片酯13克）、0.2克光引发剂（均为2-羟基-2-苯基苯乙酮）、3克硅烷偶联剂（均为3-(2,3-环氧丙氧)丙基三甲氧基硅烷）和3.8克助剂（其中光稳定剂双（3,5-二叔丁基-4-羟基苄基磷酸单乙酯）镍0.3克，增塑剂磷酸三苯酯3.5克），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1000转/分钟的条件下搅拌至混合均匀（搅拌时间为60分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为30分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物60克（均为平均粘度为45000cps、平均分子量为40000、官能度为1.5的聚氨酯甲基丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、（甲基）丙烯酸酯33克（其中甲基丙烯酸异辛酯20克、甲基丙烯酸异冰片酯13克）、光引发剂0.2克（均为2-羟基-2-苯基苯乙酮）、硅烷偶联剂3克（均为3-(2,3-环氧丙氧)丙基三甲氧基硅烷）和助剂3.8克（其中光稳定剂双（3,5-二叔丁基-4-羟基苄基磷酸单乙酯）镍0.3克，增塑剂磷酸三苯酯3.5克）。
批量生产时按上述比例配备原料即可。
实施例4
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取65克聚氨酯丙烯酸酯低聚物（其中平均粘度为50000cps、平均分子量为50000、官能度为2的聚氨酯丙烯酸酯35克，平均粘度为40000cps、平均分子量为35000、官能度为1.5的聚氨酯丙烯酸酯30克，这两种聚氨酯丙烯酸酯均由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、30克（甲基）丙烯酸酯（其中双环苯氧乙基丙烯酸酯10克、甲基丙烯酸异冰片酯20克）、3克光引发剂（均为安息香乙醚）和2克硅烷偶联剂（均为乙烯基三乙氧基硅烷），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1400转/分钟的条件下搅拌至混合均匀（搅拌时间为40分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为28分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物65克（其中平均粘度为50000cps、平均分子量为50000、官能度为2的聚氨酯丙烯酸酯35克，平均粘度为40000cps、平均分子量为35000、官能度为1.5的聚氨酯丙烯酸酯30克，这两种聚氨酯丙烯酸酯均由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、（甲基）丙烯酸酯30克（其中双环苯氧乙基丙烯酸酯10克、甲基丙烯酸异冰片酯20克）、光引发剂3克（均为安息香乙醚）和硅烷偶联剂2克（均为乙烯基三乙氧基硅烷）。
批量生产时按上述比例配备原料即可。
实施例5
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取55克聚氨酯丙烯酸酯低聚物（均为平均粘度为50000cps、平均分子量为50000、官能度为1.5的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、40克（甲基）丙烯酸酯（其中双环苯氧乙基丙烯酸酯10克、甲基丙烯酸异冰片酯10克、甲基丙烯酸羟乙酯10克、甲基丙烯酸乙酯10克）、2克光引发剂（均为安息香乙醚）、2克硅烷偶联剂（均为乙烯基三乙氧基硅烷）和1克助剂（均为光稳定剂2-（2’-羟基-3’,5-二叔丁基苯基）苯并三唑），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1200转/分钟的条件下搅拌至混合均匀（搅拌时间为55分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为30分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物55克（均为平均粘度为50000cps、平均分子量为50000、官能度为1.5的聚氨酯丙烯酸酯）、（甲基）丙烯酸酯40克（其中双环苯氧乙基丙烯酸酯10克、甲基丙烯酸异冰片酯10克、甲基丙烯酸羟乙酯10克、甲基丙烯酸乙酯10克）、光引发剂2克（均为安息香乙醚）、硅烷偶联剂2克（均为乙烯基三乙氧基硅烷）和助剂1克（均为光稳定剂2-（2’-羟基-3’,5-二叔丁基苯基）苯并三唑）。
批量生产时按上述比例配备原料即可。
实施例6
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取40克聚氨酯丙烯酸酯低聚物（均为平均粘度为20000cps、平均分子量为10000、官能度为1.5的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、40克（甲基）丙烯酸酯（其中甲基丙烯酸异辛酯20克、二乙二醇单丙烯酸酯10克、丙烯酸月桂酯5克、季戊四醇三丙烯酸酯5克）、3克光引发剂（均为2,4,6-三甲基苯甲酰-二苯基氧化膦）、10克硅烷偶联剂（均为三甲氧基[2-(7-氧杂二环[4.1.0]庚-3-基)乙基]硅烷）和7克助剂（均为增塑剂邻苯二甲酸酯），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1500转/分钟的条件下搅拌至混合均匀（搅拌时间为35分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为22分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物40克（均为平均粘度为20000cps、平均分子量为10000、官能度为1.5的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、（甲基）丙烯酸酯40克（其中甲基丙烯酸异辛酯20克、二乙二醇单丙烯酸酯10克、丙烯酸月桂酯5克、季戊四醇三丙烯酸酯5克）、光引发剂3克（均为2,4,6-三甲基苯甲酰-二苯基氧化膦）、硅烷偶联剂10克（均为三甲氧基[2-(7-氧杂二环[4.1.0]庚-3-基)乙基]硅烷）和助剂7克（均为增塑剂邻苯二甲酸酯）。
批量生产时按上述比例配备原料即可。
实施例7
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取50克聚氨酯丙烯酸酯低聚物（其中平均粘度为60000cps、平均分子量为50000、官能度为3的聚氨酯丙烯酸酯20克，平均粘度为40000cps、平均分子量为35000、官能度为1.5的聚氨酯丙烯酸酯30克，这两种聚氨酯丙烯酸酯均由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、40克（甲基）丙烯酸酯（其中甲基丙烯酸十一烷基酯15克、2-甲基丙烯酸环己酯10克、双环苯氧乙基丙烯酸酯10克、甲基丙烯酸异冰片酯5克）、3克光引发剂（其中2-羟基-2-苯基苯乙酮2克，2,4,6-三甲基苯甲酰-二苯基氧化膦1克）、1.8克硅烷偶联剂（均为乙烯基三乙氧基硅烷）和0.2克助剂（均为消泡剂聚二甲基硅氧烷），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1500转/分钟的条件下搅拌至混合均匀（搅拌时间为35分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为30分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物50克（其中平均粘度为60000cps、平均分子量为50000、官能度为3的聚氨酯丙烯酸酯20克，平均粘度为40000cps、平均分子量为35000、官能度为1.5的聚氨酯丙烯酸酯30克，这两种聚氨酯丙烯酸酯均由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、（甲基）丙烯酸酯40克（其中甲基丙烯酸十一烷基酯15克、2-甲基丙烯酸环己酯10克、双环苯氧乙基丙烯酸酯10克、甲基丙烯酸异冰片酯5克）、光引发剂3克（其中2-羟基-2-苯基苯乙酮2克，2,4,6-三甲基苯甲酰-二苯基氧化膦1克）、硅烷偶联剂1.8克（均为乙烯基三乙氧基硅烷）和助剂0.2克（均为消泡剂聚二甲基硅氧烷）。
批量生产时按上述比例配备原料即可。
实施例8
本实施例中，紫外光固化液态光学胶的制备方法依次包括下述步骤：
（1）按重量计，取50克聚氨酯丙烯酸酯低聚物（均为平均粘度为50000cps、平均分子量为50000、官能度为1.5的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、40克（甲基）丙烯酸酯（其中甲基丙烯酸月桂酯20克 、甲基丙烯酸羟乙酯15克、1,6-乙二醇二丙烯酸酯5克）、2克光引发剂（均为安息香乙醚）、2克硅烷偶联剂（均为乙烯基三乙氧基硅烷）和1克助剂（其中光稳定剂1-甲基-8-(1,2,2,6,6-五甲基-4-哌啶)癸二酸酯0.5克，增塑剂邻苯二甲酸酯0.5克），并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1400转/分钟的条件下搅拌至混合均匀（搅拌时间为45分钟），得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡（脱泡时间为20－30分钟），得到紫外光固化液态光学胶。
制得的紫外光固化液态光学胶的组成为：聚氨酯丙烯酸酯低聚物50克（均为平均粘度为50000cps、平均分子量为50000、官能度为1.5的聚氨酯丙烯酸酯，该聚氨酯丙烯酸酯由长链多元醇、带异腈酸酯基的单体和丙烯酸单体共聚而成）、（甲基）丙烯酸酯40克（其中甲基丙烯酸月桂酯20克 、甲基丙烯酸羟乙酯15克、1,6-乙二醇二丙烯酸酯5克）、光引发剂2克（均为安息香乙醚）、硅烷偶联剂2克（均为乙烯基三乙氧基硅烷）和助剂1克（其中光稳定剂1-甲基-8-(1,2,2,6,6-五甲基-4-哌啶)癸二酸酯0.5克，增塑剂邻苯二甲酸酯0.5克）。
批量生产时按上述比例配备原料即可。
对上述实施例1－8得到的紫外光固化液态光学胶的性能进行测试，其中：折射率测试使用阿贝折射仪，测试固化前后折射率；硬度测试使用邵氏A型硬度计，测试固化后胶水硬度；粘结强度测试（包括玻璃对玻璃、玻璃对偏光片）使用拉力试验机，具体方法按照ISO 4587；透过率测试使用分光光度计，测试波长为380nm－780nm的光的透过率；弹性模量使用动态机械分析仪（DMA）进行测试；耐侯性测试，在85℃/90%RH条件下放置500h观察性能变化（若进水发雾（标示×）即表示耐侯性差，若无明显变化（标示○）即表示耐候性好）。测试性能如表1所示：
表1
从上表可以看出，实施例1－8的紫外光固化液态光学胶都有良好的耐候性、较低的弹性模量，其光学性能（折射率、透过率）都满足触摸屏贴装使用要求。实施例1、4、6、7的紫外光固化液态光学胶，在玻璃间粘结强度≥1.8MPa、硬度较低（≤25），能很好地满足触摸屏盖板镜头的粘结。实施例2、3、5、8的紫外光固化液态光学胶，在玻璃和偏光片间粘结强度＞0.2MPa、硬度极低（≤15），符合触摸屏显示模块与玻璃的直接粘结要求。
综上所述，本发明提供的紫外光固化胶粘剂具有粘度可调、折射率高、硬度低、内应力小、粘结性好、耐候性佳等特性，能够满足触摸屏盖板镜头的粘结和显示模块的直接粘结两种使用要求。同时，避免了目前液态光学胶存在的膜层硬脆、粘结强度弱、柔软度低，耐候性差等问题，具有一定的市场竞争优势。
Claims (8)
1.一种紫外光固化液态光学胶，其特征在于由下述重量配比的组分组成：聚氨酯丙烯酸酯低聚物40－70份，（甲基）丙烯酸酯20－40份，光引发剂0.1－5份，硅烷偶联剂1－10份，助剂0－10份；
所述聚氨酯丙烯酸酯低聚物是平均粘度为20000－70000cps、平均分子量为10000－50000、官能度为1－3的聚氨酯丙烯酸酯；所述聚氨酯丙烯酸酯低聚物由长链多元醇、带异氰酸酯基的单体和丙烯酸单体共聚而成；
所述助剂是增塑剂、消泡剂和光稳定剂中的一种或其多种的组合。
2.根据权利要求1所述的紫外光固化液态光学胶，其特征是：所述（甲基）丙烯酸酯是丙烯酸羟乙酯、甲基丙烯酸羟乙酯、4-羟基丁基丙烯酸酯、丙烯酸-2-羟丙酯、甲基丙烯酸羟丙酯、2-羟基-2-丙烯酸丁基酯、1,4-环己烷二甲醇单丙烯酸酯、1,4-环己烷二甲醇甲基丙烯酸酯、1-氯-2-羟丙基丙烯酸酯、1-氯-2-羟丙基甲基丙烯酸酯、二乙二醇单丙烯酸酯、1,6-己二醇单丙烯酸酯、1,6-己二醇二丙烯酸酯、季戊四醇三丙烯酸酯、聚二季戊四醇五丙烯酸酯、三羟甲基丙烷二甲基丙烯酸酯、丙烯酸异冰片酯、甲基丙烯酸异冰片酯、环戊基丙烯酸酯、环戊基丙烯酸甲酯、2-丙烯酸环己基酯、2-甲基丙烯酸环己酯、双环苯氧乙基丙烯酸酯、丙烯酸甲酯、丙烯酸乙酯、甲基丙烯酸乙酯、丙烯酸丙酯、丙基-2-甲基-2-丙烯酸酯、丙烯酸异丙酯、甲基丙烯酸正丁酯、丙烯酸正丁酯、甲基丙烯酸叔丁酯、丙烯酸异丁酯、甲基丙烯酸异丁酯、丙烯酸正戊酯、甲基丙烯酸戊酯、丙烯酸正辛酯、丙烯酸异辛酯、甲基丙烯酸异辛酯、丙烯酸癸酯、甲基丙烯酸癸酯、甲基丙烯酸十一烷基酯、2-丙烯酸十二烷基酯、丙烯酸月桂酯和甲基丙烯酸月桂酯中的一种或其中多种的组合。
3.根据权利要求1所述的紫外光固化液态光学胶，其特征是：所述光引发剂是四乙基米氏酮、1-羟基环己基苯基甲酮、苯基二苯甲酮、羟基二苯甲酮、4,4'-二(N,N-二甲氨基)二苯甲酮、2,2-二乙氧基苯乙酮、2-羟基-2-苯基苯乙酮、2-羟基-2-甲基-1-苯基-1-丙酮、2,4,6-三甲基苯甲酰-二苯基氧化膦、双（2,4,6-三甲基苯甲酰基）苯基氧化膦、安息香甲醚、安息香乙醚和三聚氯氰中的一种或其中多种的组合。
4.根据权利要求1所述的紫外光固化液态光学胶，其特征是：所述硅烷偶联剂是三甲氧基甲硅烷、乙烯基三乙氧基硅烷、3-三甲氧基硅烷丙烯酸丙酯、3-甲基丙烯酰氧丙基三甲氧基硅烷、3-(2,3-环氧丙氧)丙基三甲氧基硅烷、3-[(2,3)-环氧丙氧]丙基甲基二甲氧基硅烷、三甲氧基[2-(7-氧杂二环[4.1.0]庚-3-基)乙基]硅烷、3-氨基丙基三甲氧基硅烷和3-氯丙基三甲氧基硅烷中的一种或其中多种的组合。
5.根据权利要求1所述的紫外光固化液态光学胶，其特征是：所述增塑剂是磷酸酯、烷基磺酸酯、脂肪族二元酸酯、苯多酸酯和环氧化合物中的一种或其中多种的组合。
6.根据权利要求1所述的紫外光固化液态光学胶，其特征是：所述消泡剂是磷酸三丁酯、聚二甲基硅氧烷、聚丙烯酸酯和聚醚中的一种或其中多种的组合。
7.根据权利要求1所述的紫外光固化液态光学胶，其特征是：所述光稳定剂是双(1,2,2,6,6-五甲基-4-哌啶)癸二酸酯、1-甲基-8-(1,2,2,6,6-五甲基-4-哌啶)癸二酸酯、4-羟基-2,2,6,6-四甲基-1-哌啶醇、双（3,5-二叔丁基-4-羟基苄基磷酸单乙酯）镍、2-（2'-羟基-3',5'-二叔丁基苯基）苯并三唑和2-羟基-4-正辛氧基二苯甲酮中的一种或其中多种的组合。
8.权利要求1－7任一项所述的紫外光固化液态光学胶的制备方法，其特征在于依次包括下述步骤：
（1）按重量计，取40－70份聚氨酯丙烯酸酯低聚物、20－40份（甲基）丙烯酸酯、0.1－5份光引发剂、1－10份硅烷偶联剂和0－10份助剂，并加入到清洁、干燥的反应容器中，然后将反应容器中的物料在搅拌速度为1000－1500转/分钟的条件下搅拌至混合均匀，得到胶料；
（2）用真空脱泡机对步骤（1）得到的胶料进行脱泡，得到紫外光固化液态光学胶。