CN103131272A - Fluorocarbon paint for building sheet material - Google Patents
Fluorocarbon paint for building sheet material Download PDFInfo
- Publication number
- CN103131272A CN103131272A CN2011103774265A CN201110377426A CN103131272A CN 103131272 A CN103131272 A CN 103131272A CN 2011103774265 A CN2011103774265 A CN 2011103774265A CN 201110377426 A CN201110377426 A CN 201110377426A CN 103131272 A CN103131272 A CN 103131272A
- Authority
- CN
- China
- Prior art keywords
- building board
- fluorocarbon coating
- coating according
- fluorocarbon
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention belongs to the field of building decoration spraying and discloses fluorocarbon paint for a building sheet material and a preparation method thereof. The fluorocarbon paint has high color fidelity, selection diversity, good wear resistance, excellent weatherability, good corrosion resistance, ultraviolet resistance, and long service life, can be dried at a normal temperature, can be used simply, is suitable for a plurality of base materials and has a low price.
Description
Technical field
The invention belongs to the building decoration field, relate to a kind of building board fluorocarbon coating, particularly a kind of calcium silicate board spraying fluorocarbon coating.
Background technology
Along with the raising of expanding economy and living standards of the people, people improve constantly the aesthetic conceptions in room, and the decoration of room metope, floor, furniture etc. is more and more emphasized decorative effect and environmental requirement.
Be described as decorate the most high-grade fluorocarbon coating in boundary with its widely color select, the practicality of remarkable weather resistance, long work-ing life and multiple base material and being widely used.Common to be coated in outdoor coating the longest work-ing life be 5 years, and the work-ing life of fluorocarbon coating can be for 20 years.Simultaneously, can also resist the disadvantageous effect of ultraviolet ray, atrocious weather, complex environment etc. for the fluorocarbon coating of exterior wall.
Fluorocarbon coating in the market is mainly used in the application on concrete construction exterior wall, metal coiled material, aluminium section bar, aluminium-plastic panel, plastic-steel section bar, ceramic tile, road sign, boats and ships surface etc., but it is also less to be applied to the fluorocarbon coating of calcium carbonate sheet material; Also there is the higher drawback of price in fluorocarbon coating simultaneously, and painting effect also remains further to be improved.
Summary of the invention
In order to solve the problem of above-mentioned prior art, a first aspect of the present invention provides a kind of building board fluorocarbon coating, and color is true to nature, wear resistance good, has excellent weather resistance.
In order to solve above-mentioned existing technical problem, a second aspect of the present invention provides the preparation method of a kind of building board with fluorocarbon coating.
A first aspect of the present invention for solving the problems of the technologies described above, provides a kind of building board fluorocarbon coating, and its each component and weight percentage are:
Preferably, described fluorocarbon resin be in hydroxyl fluorocarbon resin, aqueous vinyl fluorine carbon emulsion, vinylidene fluoride water-based fluorine emulsion any one.
Preferably; described titanium dioxide is the rutile type nano titanic oxide particle through surface modification; the particle size range of nanoparticle works to absorb the atmosphere middle-ultraviolet lamp between 20-50nm, reduce ultraviolet ray to the harm of human body and destructiveness, the protective cover of material are filmed and do not fade.
Preferably, described linking agent is blocked isocyanate or butyl etherify melamine resin, improves intensity, thermotolerance, wear resistance, solvent resistance, ageing resistance with this.
Preferably, described catalyzer is a kind of in tindioxide, stannous oleate, stannous octoate, dibutyltin diacetate, dibutyl tin laurate, 2-2-ethylhexoic-dibutyl tin or dibutyl tin oxide, accelerates the curing speed of coating.
Preferably, described adhesion promoter is chlorinated polyvinyl chloride, strengthens the sticking power of coating, obvious moisture resistant performance, the weather resistance of filming that improve.
Preferably, described solvent is at least a of methyl iso-butyl ketone (MIBK) or ethyl acetate.
What preferably, described pigment can be in Rutile type Titanium Dioxide, cobalt blue, high-quality carbon black, beramic color, zinc oxide, deep chrome yellow, cadmium red, mica powder, silica powder is at least a.
Preferably, described auxiliary agent comprises at least a in mould inhibitor, sanitas and membrane-forming agent.
Described filler is ultra-fine barium sulfate, plays acidproof effect.
Preferably, described synergistic agent is at least a in ethylene glycol monobutyl ether, Diethylene Glycol butyl ether.
Preferably, at least a in broken bubble polymkeric substance, polysiloxane, modified organic silicon of described defoamer.
In the above-mentioned coating component, described starting material are that ordinary method makes or are commercially available, and wherein dispersion agent is the 716W of German Degussa company.
Preferably, a kind of building board fluorocarbon coating, its each component and weight percentage are:
A second aspect of the present invention for solving the problems of the technologies described above, provides the preparation method of a kind of building board with fluorocarbon coating, comprises the steps:
(1) add partial solvent in linking agent, stir, obtain the linking agent system;
(2) add titania nanoparticles, adhesion promoter, pigment, auxiliary agent, filler, synergistic agent, defoamer, dispersion agent and residual solvent to mix in fluorocarbon resin, uniform stirring, ultrasonic grinding 0.5-1 hour, or ground 1-2 hour, 200 mesh sieves filter, and obtain coating system;
(3) the linking agent system of step (1) and the coating system of step (2) are mixed, add catalyzer, and get final product.
Fluorocarbon coating color of the present invention is true to nature, wear resistance good, have excellent weather resistance, and is corrosion-resistant, uvioresistant, and the life-span is long; And can select according to specific needs distinct colors.In addition, but fluorocarbon coating Air drying of the present invention is applicable to the application of multiple base material, particularly calcium silicate board, and is cheap, and form of construction work is simple, can be applicable to indoor or outdoor.
Embodiment
Below in conjunction with specific embodiment, such scheme is described further.Should be understood that these embodiment are not limited to limit the scope of the invention for explanation the present invention.The implementation condition that adopts in embodiment can be done further adjustment according to concrete condition.
1 one kinds of building board fluorocarbon coatings of embodiment
1.1 get following raw material by formula:
1.2 above-mentioned raw materials is mixed under agitation condition according to a conventional method, and it is dissolved fully, stirring at low speed (500 rev/mins) approximately 30 minutes is modulated into fluorocarbon coating of the present invention.
The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (13)
1. building board fluorocarbon coating, its each component concentration is as follows with weight fraction:
2. building board fluorocarbon coating according to claim 1, is characterized in that, described fluorocarbon resin can for hydroxyl fluorocarbon resin, aqueous vinyl fluorine carbon emulsion, vinylidene fluoride water-based fluorine emulsion any one.
3. building board fluorocarbon coating according to claim 1, described titanium dioxide are for through showing the rutile type nano titanic oxide particle of modification, and the particle size range of nanoparticle is between 20nm-50nm.
4. building board fluorocarbon coating according to claim 1, is characterized in that, described linking agent is blocked isocyanate or butyl etherify melamine resin.
5. building board fluorocarbon coating according to claim 1, it is characterized in that, described catalyzer is tindioxide, stannous oleate, stannous octoate, dibutyltin diacetate, dibutyl tin laurate, 2-2-ethylhexoic-dibutyl tin or dibutyl tin oxide.
6. building board fluorocarbon coating according to claim 1, is characterized in that, described adhesion promoter is chlorinated polyvinyl chloride.
7. building board fluorocarbon coating according to claim 1, is characterized in that, described solvent is methyl iso-butyl ketone (MIBK) or ethyl acetate.
8. building board fluorocarbon coating according to claim 1, is characterized in that, described pigment can be Rutile type Titanium Dioxide, cobalt blue, high-quality carbon black, beramic color, zinc oxide, deep chrome yellow, cadmium red, mica powder, silica powder etc.
9. building board fluorocarbon coating according to claim 1, is characterized in that, described auxiliary agent comprises mould inhibitor, sanitas and membrane-forming agent.
10. building board fluorocarbon coating according to claim 1, is characterized in that, described filler is ultra-fine barium sulfate, plays acidproof effect.
11. building board fluorocarbon coating according to claim 1 is characterized in that, described synergistic agent is ethylene glycol monobutyl ether, Diethylene Glycol butyl ether any or its mixture.
12. building board fluorocarbon coating according to claim 1 is characterized in that, described defoamer is a kind of for broken bubble polymkeric substance, polysiloxane, modified organic silicon.
13. building board fluorocarbon coating according to claim 1 is characterized in that, described dispersion agent is the 716W of German Degussa company.