CN103031650A - Processing technology for fabric - Google Patents
Processing technology for fabric Download PDFInfo
- Publication number
- CN103031650A CN103031650A CN2012105402454A CN201210540245A CN103031650A CN 103031650 A CN103031650 A CN 103031650A CN 2012105402454 A CN2012105402454 A CN 2012105402454A CN 201210540245 A CN201210540245 A CN 201210540245A CN 103031650 A CN103031650 A CN 103031650A
- Authority
- CN
- China
- Prior art keywords
- speed
- heavy
- shaping
- fabric
- twist
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a processing technology for a fabric, which comprises the following process steps of: 1, mixing 40 parts by weight of polysulfonamide fibers, 25 parts by weight of fire resistant viscose fibers and 35 parts by weight of wool fibers on a blending willow; 2, carrying out cotton carding processing; 3, adopting a three-passage drawing process; 4, preparing rough yarns; 5, preparing fine yarns; 6, stranding, wherein plied yarns have twist of 630 twists per meter; 7, weaving, wherein loom tension is 17.4N and the turning speed is 300r/min; 8, washing; 8, drying at a drying temperature of 100 DEG C and at a speed of 18m/min; 10, brushing at a speed of 23m/min; 11, shearing for three times in a manner of positively shearing for twice and negatively shearing for once, wherein the speed is 18m/min and a clearance is 0.3mm; 12, softening, wherein a boarding machine is adopted, the speed is 23/min, the temperature is 128 DEG C, the open width is 147cm, 38g/L of a amino silicone softening agent is added, double tanks are adopted, a manner of immersing for twice and rolling for twice is adopted, and the rolling pressure is 3.2bar; and 13, decatizing for 4min by adopting a full decator under a pressure of 0.4bar. According to the invention, when a flame-retardant function of the fabric is implemented, the fabric has the style characteristic and wear comfort of woolen fabrics and a soft hand feeling can be obtained.
Description
Technical field
The present invention relates to a kind of processing technology of cloth, be specifically related to a kind of processing technology of fire-retardant cloth.
Background technology
At present, although the welding protective clothing is various in style, flame-retardant cotton welding protective clothing is still leading kind.Flame-retardant cotton welding protective clothing generally is to adopt special process that Quality Pure Cotton Yarn Production or the canvas that is made into are carried out the secondary flame-proof treatment and obtained flame retardant effect.This flame-retardant cotton clothes are powerful low, and washability is poor, and also there is environmentally harmful material in indivedual fire retardants, and canvas is thick and heavy, and wearability is poor, affects electric welder's operation.
Summary of the invention
The object of the present invention is to provide a kind of processing technology of cloth, have style and features and the snugness of fit of wool fabric when making cloth realize anti-flaming function, and obtain soft feel.
For achieving the above object, the invention provides a kind of processing technology of cloth, comprise following processing step:
1) get PPSU terephthalamide fiber 40 weight portions, Fire resistant viscose fiber 25 weight portions, wool fibre 35 weight portions, mixed at mixing willow;
2) will mix fiber and do comb and parallel cotton fibers prior to spinning processing, doffer speed 16r/min, cylinder speed 260r/min, licker-in speed 620r/min, the heavy 14g/5m of shaping;
3) adopt three road draftings, slubbing number of doubling 8, total draft multiple 7.02, the heavy 16.3g/5m of shaping; Two road number of doubling 6, total draft multiple 6.13, the heavy 15.8g/5m of shaping; Three road number of doubling 6, total draft multiple 6.13, the heavy 15.8g/5m of shaping;
4) rove processed, total draft multiple 7.83, back zone drafting multiple 1.35, roving twist 93 sth. made by twisting/m, ingot speed 630r/min, the heavy 3g/10m of shaping;
5) spun yarn processed, spinning count 50Nm, the twist 788 sth. made by twisting/m, 1.24 times of back zone drafting multiples, ingot speed 10000r/min;
6) plying, spinning twist 630 sth. made by twisting/m;
7) weave warp tension 17.4N, speed of a motor vehicle 300r/min;
8) braying, clear water braying, 62 ℃ of braying temperature, speed 23m/min;
9) oven dry, 100 ℃ of baking temperature, speed 18m/min;
10) bristle, speed 23m/min;
11) cropping, two positive one anti-three cropping, speed 18m/min, cutter is apart from 0.3mm;
12) softness adopts boarding machine, speed 23m/min, and 128 ℃ of temperature, open-width 147cm adds the amino silicon 38g/L of softener, adopts double flute, and two soak two rolls nip pressure 3.2bar;
13) decatizing adopts tank to steam machine, air pressure 0.4bar, time 4min.
Advantage of the present invention and beneficial effect are: a kind of processing technology of cloth is provided, has style and features and the snugness of fit of wool fabric when making cloth realize anti-flaming function, and obtain soft feel.
The specific embodiment
Below in conjunction with specific embodiment, the invention will be further described.Following examples only are used for technical scheme of the present invention more clearly is described, and can not limit protection scope of the present invention with this.
Embodiment 1
A kind of processing technology of cloth comprises following processing step:
1) get PPSU terephthalamide fiber 40 weight portions, Fire resistant viscose fiber 25 weight portions, wool fibre 35 weight portions, mixed at mixing willow;
2) will mix fiber and do comb and parallel cotton fibers prior to spinning processing, doffer speed 16r/min, cylinder speed 260r/min, licker-in speed 620r/min, the heavy 14g/5m of shaping;
3) adopt three road draftings, slubbing number of doubling 8, total draft multiple 7.02, the heavy 16.3g/5m of shaping; Two road number of doubling 6, total draft multiple 6.13, the heavy 15.8g/5m of shaping; Three road number of doubling 6, total draft multiple 6.13, the heavy 15.8g/5m of shaping;
4) rove processed, total draft multiple 7.83, back zone drafting multiple 1.35, roving twist 93 sth. made by twisting/m, ingot speed 630r/min, the heavy 3g/10m of shaping;
5) spun yarn processed, spinning count 50Nm, the twist 788 sth. made by twisting/m, 1.24 times of back zone drafting multiples, ingot speed 10000r/min;
6) plying, spinning twist 630 sth. made by twisting/m;
7) weave warp tension 17.4N, speed of a motor vehicle 300r/min;
8) braying, clear water braying, 62 ℃ of braying temperature, speed 23m/min;
9) oven dry, 100 ℃ of baking temperature, speed 18m/min;
10) bristle, speed 23m/min;
11) cropping, two positive one anti-three cropping, speed 18m/min, cutter is apart from 0.3mm;
12) softness adopts boarding machine, speed 23m/min, and 128 ℃ of temperature, open-width 147cm adds the amino silicon 38g/L of softener, adopts double flute, and two soak two rolls nip pressure 3.2bar;
13) decatizing adopts tank to steam machine, air pressure 0.4bar, time 4min.
The above only is preferred embodiment of the present invention; should be pointed out that for those skilled in the art, under the prerequisite that does not break away from the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the processing technology of a cloth is characterized in that, comprises following processing step:
1) get PPSU terephthalamide fiber 40 weight portions, Fire resistant viscose fiber 25 weight portions, wool fibre 35 weight portions, mixed at mixing willow;
2) will mix fiber and do comb and parallel cotton fibers prior to spinning processing, doffer speed 16r/min, cylinder speed 260r/min, licker-in speed 620r/min, the heavy 14g/5m of shaping;
3) adopt three road draftings, slubbing number of doubling 8, total draft multiple 7.02, the heavy 16.3g/5m of shaping; Two road number of doubling 6, total draft multiple 6.13, the heavy 15.8g/5m of shaping; Three road number of doubling 6, total draft multiple 6.13, the heavy 15.8g/5m of shaping;
4) rove processed, total draft multiple 7.83, back zone drafting multiple 1.35, roving twist 93 sth. made by twisting/m, ingot speed 630r/min, the heavy 3g/10m of shaping;
5) spun yarn processed, spinning count 50Nm, the twist 788 sth. made by twisting/m, 1.24 times of back zone drafting multiples, ingot speed 10000r/min;
6) plying, spinning twist 630 sth. made by twisting/m;
7) weave warp tension 17.4N, speed of a motor vehicle 300r/min;
8) braying, clear water braying, 62 ℃ of braying temperature, speed 23m/min;
9) oven dry, 100 ℃ of baking temperature, speed 18m/min;
10) bristle, speed 23m/min;
11) cropping, two positive one anti-three cropping, speed 18m/min, cutter is apart from 0.3mm;
12) softness adopts boarding machine, speed 23m/min, and 128 ℃ of temperature, open-width 147cm adds the amino silicon 38g/L of softener, adopts double flute, and two soak two rolls nip pressure 3.2bar;
13) decatizing adopts tank to steam machine, air pressure 0.4bar, time 4min.