CN102719000A - Polyethylene (PE) pipe for coal-bed methane drainage and manufacturing method thereof - Google Patents
Polyethylene (PE) pipe for coal-bed methane drainage and manufacturing method thereof Download PDFInfo
- Publication number
- CN102719000A CN102719000A CN2012101729626A CN201210172962A CN102719000A CN 102719000 A CN102719000 A CN 102719000A CN 2012101729626 A CN2012101729626 A CN 2012101729626A CN 201210172962 A CN201210172962 A CN 201210172962A CN 102719000 A CN102719000 A CN 102719000A
- Authority
- CN
- China
- Prior art keywords
- coal
- pipe
- seam gas
- gas extraction
- managed
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of coal-bed pipes and discloses a polyethylene (PE) pipe for coal-bed methane drainage and a manufacturing method thereof. The PE pipe for coal-bed methane drainage comprises the following raw materials in parts by weight: 50 to 70 parts of PE resin, 20 to 35 parts of flame-retardant master batch, 1 to 4 parts of lubricating agent and 0.5 to 3 parts of brightening agent. According to the PE pipe for the coal-bed methane gas drainage in a coal mine, the domestic gap is filled, the requirement of the coal-bed methane drainage project is met, the PE pipe for the coal-bed methane drainage is low in cost, high in flame-retardant property, high in strength and outstanding in toughness, the performance index accords with the specified Q/WS10-2009 standard, the whole production process of the product is simple and efficient, and the economic benefits are improved.
Description
Technical field
The present invention relates to a kind of coal seam tubing technical field, related in particular to a kind of coal-seam gas extraction with PE pipe and preparation method thereof.
Background technology
As everyone knows, below underground 1000m, also exist coal-seam gas simultaneously in the dark coal seam, it not only contains toxic gas, and contains a large amount of inflammable gases, and this brings very big inconvenience to exploitation, is prone to cause combustion explosion.In recent years, colliery scientific and technical personnel research was carried out extraction to the coal-seam gas at underground 1000m-2000m deep layer place before unminding in the colliery, carried out elder generation and got rid of afterwards and exploit, and made colliery safe working smoothly.
Colliery coal-seam gas gas drainage PE pipe exactly before exploitation, this pipe is put into deep under ground, utilizes the hole on this pipe circumference that coal-seam gas is extracted out.At present, existing high especially abroad with the performance product price, the production cycle is long, need again to buy with foreign exchange; Because it is with high costs, performances such as flame retardant properties, intensity, toughness are difficult to meet increasingly high production requirement, therefore, are badly in need of the colliery coal-seam gas gas drainage PE pipe that a kind of accords with production requires.
Summary of the invention
The coal-seam gas extraction that the purpose of this invention is to provide a kind of low cost, flame retardant properties is good, intensity is high, toughness is outstanding is with PE pipe and preparation method thereof.
In order to solve the problems of the technologies described above, the present invention is able to solve through following technical proposals:
The coal-seam gas extraction is managed with PE, comprises the raw material of following weight part:
Polyvinyl resin 50-70 part;
Flame-retardant master batch 20-35 part;
Lubricant 1-4 part;
Whitening agent 0.5-3 part.
As preferably, described flame-retardant master batch comprises following raw materials by weight percent:
Antimony Trioxide: 99.5Min 15-25%;
Decabromodiphynly oxide 50-60%;
Polyethylene wax 1-6%;
High-pressure polyethylene 15-26%.
As preferably, described flame-retardant master batch comprises following raw materials by weight percent:
Antimony Trioxide: 99.5Min 19%;
Decabromodiphynly oxide 58%;
Polyethylene wax 3%;
High-pressure polyethylene 20%.
As preferably, described whitening agent is white dyes OB.
As preferably, described lubricant is selected in stearic amide, amine hydroxybenzene, BS, the solid paraffin any for use.
As preferably, described coal-seam gas extraction is following with the preparation method of PE pipe:
A, kneading: by prescription, the every kind of raw material weight of accurately weighing heats kneading pot to 80 ℃; Raw material is poured in the pot, and adjustment was stirred 5-10 minute, stopped to stir, and compound was packed subsequent use;
B, compound is put into tablets press carry out granulation;
C, granular compound is dry gets into the forcing machine moulding, through cooling, seal mark, draw, coil, punch, clear up after, get finished product.
As preferably, described control drying temperature is 70-80 ℃, time of drying 1.5-2h.
As preferably, mold temperature is controlled to be 150-220 ℃ among the described step c.
The present invention has significant technique effect owing to adopted above technical scheme:
Colliery coal-seam gas gas drainage PE pipe of the present invention has been filled up domestic blank; Satisfy the demand of coal gas layer extraction engineering, cost is low, and flame retardant properties is good, intensity is high, toughness is outstanding; Performance index accord with Q/WS10-2009 standard code; The whole production technology of product is simple, and efficient is high, has improved economic benefit.
Embodiment
Below in conjunction with specific embodiment the present invention is described in further detail:
Embodiment 1
The coal-seam gas extraction is managed with PE, comprises the raw material of following weight part:
70 parts of polyvinyl resins;
30 parts of flame-retardant master batchs;
Wherein: Antimony Trioxide: 99.5Min 19%;
Decabromodiphynly oxide 58%;
Polyethylene wax 3%;
High-pressure polyethylene 20%;
2 parts of stearic amides;
1.5 parts of white dyes OB;
This coal-seam gas extraction is following with the preparation method of PE pipe:
A, kneading: by prescription, the every kind of raw material weight of accurately weighing heats kneading pot to 80 ℃; Raw material is poured in the pot, and adjustment was stirred 5-10 minute, stopped to stir, and compound was packed subsequent use;
B, compound is put into tablets press carry out granulation;
(1) heats and extrude fuselage, head, mould, 145 ℃ in 1 district, 150 ℃ in 2 districts, 3 districts, 155 ℃ in 4 districts～7 districts, 160 ℃ in 8 districts, 165～170 ℃ of machine head port moulds;
(2) start main frame, progressively improve rotating speed to 234r/min by low speed;
(3) tank cooling;
(4) open blower, remove the strip material globule;
(5) pelletizing and main frame speed coordination make size of particles even.
C, granular compound is dry, drying temperature is 80 ℃, time of drying 1.5h.Get into the forcing machine moulding, through cooling, seal mark, draw, coil, punch, clear up after, must finished product.
Condition of molding:
(1) barrel zone temperature 165-220 ℃
(2) head temperature 190-230 ℃
(3) melt temperature 195-205 ℃
(4) cooling sizing water temperature is 20 ℃
It is following that above-mentioned finished product is carried out The performance test results:
| Test event | Standard | Actual measurement |
| Flat | Being depressed into inwall overlaps | Flawless, nothing are destroyed |
| Tensile strength (MPa) | Be not more than 12.4 | 20.4 |
| Elongation rate of tensile failure (%) | Be not less than 350 | 640 |
| Ring stiffness KN/ ㎡ | Be not less than 20 | 85 |
| Combustionproperty | ? | V 0Level |
In a word, the above is merely preferred embodiment of the present invention, and all equalizations of doing according to claim of the present invention change and modify, and all should belong to the covering scope of patent of the present invention.
Claims (8)
1. the coal-seam gas extraction is managed with PE, it is characterized in that, comprises the raw material of following weight part:
Polyvinyl resin 50-70 part;
Flame-retardant master batch 20-35 part;
Lubricant 1-4 part;
Whitening agent 0.5-3 part.
2. coal-seam gas extraction according to claim 1 is managed with PE, it is characterized in that: described flame-retardant master batch comprises following raw materials by weight percent:
Antimony Trioxide: 99.5Min 15-25%;
Decabromodiphynly oxide 50-60%;
Polyethylene wax 1-6%;
High-pressure polyethylene 15-26%.
3. coal-seam gas extraction according to claim 2 is managed with PE, it is characterized in that: described flame-retardant master batch comprises following raw materials by weight percent:
Antimony Trioxide: 99.5Min 19%;
Decabromodiphynly oxide 58%;
Polyethylene wax 3%;
High-pressure polyethylene 20%.
4. coal-seam gas extraction according to claim 1 is managed with PE, it is characterized in that: described whitening agent is white dyes OB.
5. coal-seam gas extraction according to claim 1 is managed with PE, it is characterized in that: described lubricant is selected in stearic amide, amine hydroxybenzene, BS, the solid paraffin any for use.
6. according to the preparation method of the arbitrary described coal-seam gas extraction of claim 1-5, it is characterized in that method is following with the PE pipe:
A, kneading: by prescription, the every kind of raw material weight of accurately weighing heats kneading pot to 80 ℃; Raw material is poured in the pot, and adjustment was stirred 5-10 minute, stopped to stir, and compound was packed subsequent use;
B, compound is put into tablets press carry out granulation;
C, granular compound is dry gets into the forcing machine moulding, through cooling, seal mark, draw, coil, punch, clear up after, get finished product.
7. coal-seam gas extraction according to claim 6 is with the preparation method of PE pipe, and it is characterized in that: described control drying temperature is 70-80 ℃, time of drying 1.5-2h.
8. coal-seam gas extraction according to claim 6 is with the preparation method of PE pipe, and it is characterized in that: mold temperature is controlled to be 150-220 ℃ among the described step c.