CN101117486A - Process for preparing macromolecular compound paint - Google Patents
Process for preparing macromolecular compound paint Download PDFInfo
- Publication number
- CN101117486A CN101117486A CNA2006100150663A CN200610015066A CN101117486A CN 101117486 A CN101117486 A CN 101117486A CN A2006100150663 A CNA2006100150663 A CN A2006100150663A CN 200610015066 A CN200610015066 A CN 200610015066A CN 101117486 A CN101117486 A CN 101117486A
- Authority
- CN
- China
- Prior art keywords
- portions
- added
- container
- parts
- filler
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention provides a preparation process of a polymer compound coating. 60 portions of water are poured into a container firstly, and then 2 portions of polyvinyl alcohol are added and heated to 50 DEG C. 0.005 portions of fluorescent whitening agent is added and heated continually until the substance in the container are all dissolved. 2 portions of thickener liquid are added and the residue cold water is added secondly, heated continually, defoamed with a defoamer, and placed in a special container after cooling. 0.5 portions of crylic acid emulsion are added, and coating and scraping operation is carried out with a filler. The filler comprises 210 portions of superfine heavy calcium carbonate, and 30 percent of adhesive and 70 percent of calcium powder are added serially during the coating and scraping operation, and then mixed and stirred uniformly. The invention has the following advantages of poisonless and tasteless, non-radioactivity, good waterproof performance, strong adhesion, no crack, rolling or mildewing.
Description
Technical field
The present invention relates to a kind of process for preparing macromolecular compound paint.
Background technology
At present, the interior wall coating of selling on the market contains formaldehyde and benzene exceeds standard, and to the human body poisonous and harmful, mouldy, volume skin, crackle often appear in import coating price costliness, and influence is normally used.
Summary of the invention
The objective of the invention is to overcome above-mentioned deficiency, a kind of process for preparing macromolecular compound paint is provided.
Technical scheme of the present invention is: a kind of process for preparing macromolecular compound paint, it is characterized in that: weight % consists of: base-material+auxiliary agent 30-40, filler 60-70, base-material is by 2-6 part polyvinyl alcohol, 2-5 part thickening material liquid, 0.5-1.5 the ACRYLIC EMULSION of part and 87-95 part water constitute, auxiliary agent is made of 0.004-0.008 part fluorescent bleaches and 0.001-0.003 part defoamer, filler is made of 190-230 part superfine heavy calcium carbonate, earlier 60 parts of water inputs are advanced container, add polyvinyl alcohol 2-6 part, when being warmed to 40 ℃, throw in fluorescent bleaches 0.004-0.008 part, the object that continues to heat up in container all dissolves, and adds thickening material liquid 2-5 part, add remaining cold water then for the second time, continue to heat, bubble occurs and disappear with defoamer this moment, till the glue in the container is as clear as crystal, be placed on after the cooling in the special-purpose container, the ACRYLIC EMULSION that adds 0.5-1.5 part is joined filler and is coated with and scrapes operation, and filler is made of 190-250 part superfine heavy calcium carbonate.
The present invention has the following advantages: nonpoisonous and tasteless, "dead", good waterproof performance, strong adhesion, not crackle, do not roll up skin, do not go mouldy.
Embodiment
Embodiment: a kind of process for preparing macromolecular compound paint, earlier 60 parts of water inputs are advanced container, add 2 parts of polyvinyl alcohol, be warmed to 50 ℃, throw in 0.005 part of fluorescent bleaches, the object that continues to be warmed up in the container all dissolves, and adds 2 parts of thickening material liquid, add remaining cold water then for the second time, continue to heat, use the defoamer froth breaking, be placed on after the cooling in the special-purpose container, the ACRYLIC EMULSION that adds 0.5 part, mix filler and be coated with and scrape operation, filler is made of 210 parts of superfine heavy calcium carbonates, is coated with and puts 30% glue when scraping operation, after put 70% calcium powder, mixing and stirring.
Claims (1)
1. process for preparing macromolecular compound paint, it is characterized in that: earlier 60 parts of water inputs are advanced container, add 2 parts of polyvinyl alcohol, be warmed to 50 ℃, throw in 0.005 part of fluorescent bleaches, the object that continues to be warmed up in the container all dissolves, and adds 2 parts of thickening material liquid, add remaining cold water then for the second time, continue to heat, use the defoamer froth breaking, be placed on after the cooling in the special-purpose container, the ACRYLIC EMULSION that adds 0.5 part, mix filler and be coated with and scrape operation, filler is made of 210 parts of superfine heavy calcium carbonates, is coated with and puts 30% glue when scraping operation, after put 70% calcium powder, mixing and stirring.