NUHA MASHAAN

Roadways are considered one of the most important elements of infrastructure and they play an essential role in our daily lives. In road pavement construction, the use of crumb rubber in the modification of bitumen binder is considered as a smart solution for sustainable development by reusing waste materials. It is believed that crumb rubber modifier (CRM) could be one of the alternative polymer materials in improving bitumen binder performance properties of hot mix asphalt. This study aims to present and discuss the findings from some of the studies, on the use of crumb rubber in asphalt pavement.

To prevent pavement distresses there are various solutions such as adopting new mix designs or utilisation of asphalt additives. The primary aim of this study was to investigate the effect of adding crumb tyre rubber as an additive to SMA mixture performance properties. This study investigated the essential aspects of modified asphalt mixtures in order to better understand the influence of CRM modifiers on volumetric, mechanical, and stiffness properties of SMA mixture. In this study, virgin bitumen 80/100 penetration grade was used, modified with crumb rubber (CRM) at five different modification levels, namely, 6%, 12%, 16%, and 20%, respectively, by weight of the bitumen. The appropriate amount of the added CRM was found to be 12% by weight of bitumen. This percentage results in the maximum level of stability. The resilient modulus (Mr) of modified SMA samples including different percentages of CRM was obviously higher in comparison with that of unmodified samples.

Today, virgin polymer modified asphalt mixes are comparatively more expensive for road pavement. One way to reduce the expense of such construction and to make it more convenient is the application of inexpensive polymer, such as waste polymer. The primary aim of this study was to investigate the effect of adding waste tyre rubber (crumb rubber modifier (CRM)) on the stiffness and fatigue properties of stone mastic asphalt (SMA) mixtures. Various percentages of waste CRM with size of 0.60 mm were added to SMA mixtures. Indirect tensile stiffness modulus test was conducted at temperatures of 5, 25, and 40°C. Indirect tensile fatigue test was conducted at three different stress levels (2000, 2500, and 3000 N). The results show that the stiffness modulus of reinforced SMA samples containing various contents of CRM is significantly high in comparison with that of nonreinforced samples, and the stiffness modulus of reinforced samples is in fact less severely affected by the increased temperature compared to the nonreinforced samples. Further, the results show that CRM reinforced SMA mixtures exhibit significantly higher fatigue lives compared to the nonreinforced mixtures help in and promotion of sustainable technology by recycling of waste materials in much economical and environmental-friendly manner

Crumb rubber modification has been proven to enhance the properties of pure bitumen. This paper looks at some of the international standards for producing crumb rubber modified bitumen (CRMB) and reviews the effect of crumb rubber to the rheology of crumb rubber modified bitumen. The review shows that the rheology of CRMB depends on internal factors such as crumb rubber quantity, particle size, and pure bitumen composition, and external factors such as the mixing time, temperature, and also the modification technique. These factors govern the swelling process of crumb rubber particles that lead to the increase of viscosity of the modified bitumen. However, the mixing temperature and duration can cause rubber particles to depolymerize and subsequently cause loss of viscosity. Crumb rubber modification also improves the properties of bitumen by increasing the storage and loss modulus and enhancing the high and low temperature susceptibility. The effect of crumb rubber to aging properties of CRMB is also discussed. Finally several techniques of chemical modification to terminal blends of CRMB and the subsequent improvement to the settling property of CRMB are explained.

Today, rapid economic and industrial growth generates increasing amounts of waste materials such as waste tyre rubber. Attempts to inspire a green technology which is more environmentally friendly that can produce economic value are a major consideration in the utilization of waste materials. The aim of this study is to evaluate the effect of waste tyre rubber (crumb rubber modifier (CRM)), in stone mastic asphalt (SMA 20) performance. The virgin bitumen (80/100) penetration grade was used, modified with crumb rubber at four different modification levels, namely, 6%, 12%, 16%, and 20% by weight of the bitumen. The testing undertaken on the asphalt mix comprises the indirect tensile (dynamic stiffness), dynamic creep, and wheel tracking tests. By the experimentation, the appropriate amount of CRM was found to be 16% by weight of bitumen. The results show that the addition of CRM into the mixture has an obvious significant effect on the performance properties of SMA which could improve the mixture's resistance against permanent deformation. Further, higher correlation coefficient was obtained between the rut depth and permanent strain as compared to resilient modulus; thus dynamic creep test might be a more reliable test in evaluating the rut resistance of asphalt mixture.

Semi-flexible pavement surfacing is a composite pavement that utilizes the porous pavement structure of the flexible bituminous pavement, which is subsequently grouted with appropriate cementitious materials. This study aims to investigate the compressive strength, flexural strength, and workability performance of cementitious grout. The grout mixtures are designed to achieve high strength and maintain flow properties in order to allow the cement slurries to infiltrate easily through unfilled compacted skeletons. A paired-sample t-test was carried out to find out whether water/cement ratio, SP percentages, and use of silica fume influence the cementitious grout performance. The findings showed that the replacement of 5% silica fume with an adequate amount of superplasticizer and water/cement ratio was beneficial in improving the properties of the cementitious grout.

The main objective of this paper is to investigate the relations of rubber size, rubber content, and binder content in determination of optimum binder content for open graded friction course (OGFC). Mix gradation type B as specified in Specification for Porous Asphalt produced by the Road Engineering Association of Malaysia (REAM) was used in this study. Marshall specimens were prepared with four different sizes of rubber, namely, 20 mesh size [0.841 mm], 40 mesh [0.42 mm], 80 mesh [0.177 mm], and 100 mesh [0.149 mm] with different concentrations of rubberised bitumen (4%, 8%, and 12%) and different percentages of binder content (4%-7%). The appropriate optimum binder content is then selected according to the results of the air voids, binder draindown, and abrasion loss test. Test results found that crumb rubber particle size can affect the optimum binder content for OGFC.

An immense problem affecting environmental pollution is the increase of waste tyre vehicles. In an attempt to decrease the magnitude of this issue, crumb rubber modifier (CRM) obtained from waste tyre rubber has gained interest in asphalt reinforcement. The use of crumb rubber in the reinforcement of asphalt is considered as a smart solution for sustainable development by reusing waste materials, and it is believed that crumb rubber modifier (CRM) could be an alternative polymer material in improving hot mix asphalt performance properties. In this paper, a critical review on the use of crumb rubber in reinforcement of asphalt pavement will be presented and discussed. It will also include a review on the effects of CRM on the stiffness, rutting, and fatigue resistance of road pavement construction.

Currently, a serious problem that leads to environmental pollution is the abundance and increase of waste tyres from vehicles. The major approach to solve this issue is to recycle waste tyre rubber including its use as crumb rubber modifier in asphalt pavement. This study aims to investigate the effect of crumb rubber modifier on engineering properties of rubberised asphalt. The physical and rheological properties of rubberised asphalt binder that include different percentages of crumb rubber modifier (0, 4, 8, 12, 16 and 20%) were determined and assessed using various laboratory tests. Results showed that 16% crumb rubber modifier at 180 degrees C blending temperature have a significant effect on modified binder engineering properties. Also, the study promotes the recycle of waste tyre rubber in an environment friendly manner.

Fatigue cracking is an essential problem of asphalt concrete that contributes to pavement damage. Although stone matrix asphalt (SMA) has significantly provided resistance to rutting failure, its resistance to fatigue failure is yet to be fully addressed. The aim of this study is to evaluate the effect of crumb rubber modifier (CRM) on stiffness and fatigue properties of SMA mixtures at optimum binder content, using four different modification levels, namely, 6%, 8%, 10%, and 12% CRM by weight of the bitumen. The testing undertaken on the asphalt mix comprises the dynamic stiffness (indirect tensile test), dynamic creep (repeated load creep), and fatigue test (indirect tensile fatigue test) at temperature of 25°C. The indirect tensile fatigue test was conducted at three different stress levels (200, 300, and 400 kPa). Experimental results indicate that CRM-reinforced SMA mixtures exhibit significantly higher fatigue life compared to the mixtures without CRM. Further, higher correlation coefficient was obtained between the fatigue life and resilient modulus as compared to permanent strain; thus resilient modulus might be a more reliable indicator in evaluating the fatigue life of asphalt mixture.