Abstract
Solution-processed organometal halide perovskites are hybrid crystalline semiconductors highly interesting for low-cost and efficient optoelectronics. Their properties are dependent on the crystal structure. Literature shows a variety of crystal phase transition temperatures and often a spread of the transition over tens of degrees Kelvin. We explain this inconsistency by demonstrating that the temperature of the tetragonal-to-orthorhombic phase transition in methylammonium lead triiodide depends on the concentration and nature of local defects. Phase transition in individual nanowires was studied by photoluminescence microspectroscopy and super-resolution imaging. We propose that upon cooling from 160 to 140 K, domains of the crystal containing fewer defects stay in the tetragonal phase longer than highly defected domains that readily transform to the high bandgap orthorhombic phase at higher temperatures. The existence of relatively pure tetragonal domains during the phase transition leads to drastic photoluminescence enhancement, which is inhomogeneously distributed across perovskite microcrystals.
Similar content being viewed by others
Introduction
Recent surge of worldwide attention to organometal halide perovskite (OMHP) materials has already led to solar cells with energy-conversion efficiencies more than 20%1,2,3. These solution-processed materials demonstrate long charge carrier diffusion lengths, low recombination rates, and high absorption coefficients in the whole visible range3,4,5. Because of high luminescence quantum yield, this class of direct bandgap semiconductors is also very attractive for optoelectronic applications such as lasers and light-emitting devices6,7,8.
Although OMHP-based optoelectronics in terms of the achieved efficiencies appears to be a mature technology, the research community is still at the beginning of understanding the complex interplay between excitons, free charge carriers, and various types of structural and electronic defect states9, determining the properties of these materials10,11,12,13,14,15,16,17,18. Moreover, electronic properties of OMHPs are sensitive to light and environment. Light can induce not only defect formation, ion migration, and material degradation, but also in some conditions healing of defect states revealed as an improvement of electrical characteristics and enhancement of photoluminescence (PL)14, 19,20,21,22.
An additional difficulty is that OMHP films are essentially inhomogeneous at the nanoscale and microscale, which greatly affects the observed electronic properties and makes them strongly dependent on the sample preparation method21,22,23,24,25,26,27,28,29. Unmasking the inherent properties from the ensemble averaged response and understanding the effects of nanoscale morphology and crystal structure is an important task for spatially resolved spectroscopy methods and spectroscopy of individual submicrometer crystals21, 22, 24, 30,31,32,33.
Methylammonium lead triiodide (CH3NH3PbI3 or MAPbI3) adopts a perovskite-type crystal structure18. It is cubic at temperatures above 330 K, tetragonal between 330 K and ~160 K, and finally transforms to a low-symmetry orthorhombic crystal structure below 160 K34. These first-order structural phase transitions lead to deformation of the PbI6 octahedra, which alters the electronic and optical properties of the material significantly35,36,37,38.
Although the tetragonal-to-orthorhombic phase transition of MAPbI3 has been described in numerous studies, there is ambiguity in the phase transition temperature. Some studies report that the transition is abrupt, some that it is prolonged over a temperature interval as large as several tens of degrees Kelvin7, 10,11,12, 36, 39. These, and other remarkable features of the phase transition in MAPbI3, were recently discussed in relation to possible strain induced by the grain boundaries in polycrystalline films33. However, the overall understanding that would coherently unite all observations is still missing.
The PL quantum yield of OMHPs increases upon cooling7, 10, 11. Besides this general trend, the PL often becomes especially intense when cooling or heating across the tetragonal-to-orthorhombic phase transition. Although observed in several publications (e.g.,7, 33), the origin of this phenomenon remains unclear. Here we use the PL enhancement effect as a reporter on the processes during the crystal phase transition in MAPbI3.
In order to shed light on these phenomena, we studied the temperature dependence of PL of highly crystalline individual nanowires (NWs) and microplates of MAPbI3. The preparation method used here is known to result in well-defined highly crystalline nanowires, microrods and microplates, as was previously characterized by X-ray diffraction, scanning electron microscopy (SEM), and transmission electron microscopy (TEM)8. By studying a number of well-defined individual objects we removed the uncertainty due to ensemble averaging in inhomogeneous films and the effect of grain boundaries in polycrystalline samples. Super-resolution luminescence localization microscopy allowed us to follow the phase transition in individual MAPbI3 NWs with spatial resolution below the light diffraction limit.
We show that presence of defects controls the phase transition temperature of each particular region of the crystal. We directly observed the formation of domains of different crystal phases within individual NWs and their coexistence in the phase transition range, visible as a patterned (or spotty as we will call it) PL spatial distribution in what appears to be structurally homogeneous NWs. We assign the drastic PL enhancement in the phase transition temperature interval to freezing out the most defected regions of the crystal to the orthorhombic phase. In other words, we propose that the phase transition temperature in MAPbI3 perovskite depends on the concentration of certain defects, which spatially varies in the material at the nanoscale. Our model is based on the theory of phase transitions in solids40, 41, which has not been applied to metal halide perovskites yet. The model qualitatively explains the temperature dependence of the PL properties and the spread of the phase transition over the large temperature interval. Thus, our results consolidate apparently opposing literature data concerning the phase transition temperature.
Results
Overview of temperature-dependent PL
Figure 1 shows SEM images of four NWs, one microplate, and a polycrystalline film (a) together with the temperature dependences of their PL intensity (b). All NWs and the plate possess well-defined rectangular shapes determined by their crystallographic axes, which is in great contrast to the thin film consisting of randomly shaped grains of 100 – 300 nm in size. All samples possessed the PL enhancement effect in a certain temperature region around 150 K. The relative amplitude of the PL enhancement was larger and the temperature region of the enhancement was narrower for individual NWs when compared to the individual plate and the film sample.
Figure 1c and d show temperature-dependent PL spectra of NW#1 while similar data for the other objects are given in Supplementary Figs. 9–13. At temperatures from 295 to 160 K, PL of NW#1 possessed one emission peak corresponding to the tetragonal phase. This peak was observed to monotonically shift toward longer wavelengths upon cooling, which is in agreement with the anomalous Varshi trend with a positive thermal expansion coefficient42. Upon cooling from 160 to 140 K (around the phase transition temperature), the PL peak of the tetragonal phase started to shift toward shorter wavelengths while exhibiting a dramatic flash-like increase of the PL intensity, reaching its maximum at ~150 K. Around this temperature, the PL peak attributed to the orthorhombic phase appeared and its intensity increased upon further cooling11, 12. Thus, in the temperature region from 150 to 130 K, the PL bands of both the tetragonal and orthorhombic phase were observed showing the coexistence of both phases within the individual NWs of high crystallinity over at least a 20 K temperature interval.
The PL intensity from the tetragonal phase decreased until it vanished around 130 K, indicating the absence of the tetragonal phase, which is in agreement with previous X-ray diffraction studies12. At temperatures below 100 K, a low-energy feature appeared (emission peak around 820 nm, see also Supplementary Fig. 3), that has been previously attributed to emission from trap states7, 10, 12.
Figure 1d shows the normalized spectra for both heating and cooling cycles. One can see an apparent thermal hysteresis of the PL peak position of the tetragonal phase and its emission intensity31, which is similar to the recently reported hysteresis of the carrier mobility in perovskite microplates near the phase transition temperature43.
Spatially resolved PL spectra at room temperature
Now let us have a look at how the PL properties of NW#1 change along its length. Spatially resolved PL spectra and PL decay kinetics at room temperature are presented in Fig. 2. The SEM image shows that NW#1 had a uniform rod-like shape with almost constant thickness and without visible grain boundaries. Therefore, NW#1 should absorb the excitation light uniformly along its length. However, the PL intensity and PL lifetime were observed to slightly differ from one spatial location to the other. Higher PL intensity corresponded to a longer PL lifetime. Since the excitation conditions were the same, a longer PL lifetime is indicative of a smaller concentration of non-radiative recombination centers in the bright region A of NW#1 in comparison to the dimmer regions B, C, and D in Fig. 2. PL spectra of the darker regions were slightly broader than those of the bright region A. The spectrum from region D also appeared to be red-shifted by 8 nm in comparison to the one from the high PL intensity region A.
Spatial and spectral inhomogeneity of PL during transition
Luminescence microscopy allowed us to see evolution of the PL intensity distribution over the NW during the phase transition. The Supplementary Information contains a video composed of PL images during the cooling–heating cycle between 295 and 77 K, where a clear spatial redistribution of PL is observed in the temperature region between 160 and 130 K.
Figure 3 and the Supplementary Movie nicely show that the PL of the investigated NWs becomes spotty across the phase transition temperature region. Upon further cooling, the relative intensities of the emission spots were drastically changing (see Fig. 3 and the video in Supplementary Information). Above or below the phase coexistence region (T > 160 K or T < 130 K), the PL appeared much more uniform over the length of the NW. More examples of spotty PL patterns appearing in the phase transition region can be found in Supplementary Figs. 7, 9–12.
Figure 4 shows the variation of the PL intensity and spectra along the axis of NW#1 at 145 K—the temperature when the spotty emission is very clear. The PL spectra contain two emission bands associated with the different crystal phases obviously coexisting in the very same NW in the 130 – 150 K temperature range. We found that the intensity of the lower energy emission peak (tetragonal phase) was much higher for the bright spots in comparison to that in the dark regions of the same wire. It is even better illustrated by the spectral image in Fig. 4c, where the PL from the tetragonal phase was clearly stemming from three distinct locations, while the emission of the orthorhombic phase was evenly distributed along the NW length. The spectral images taken during the cooling/heating cycle can be found in Supplementary Fig. 4.
This shows that the PL enhancement is due to the increasing PL intensity from the tetragonal phase only. The spatially resolved measurements show that the PL of the tetragonal phase stems from several small regions within the NW, which positions and sizes will be characterized further below using super-resolution localization microscopy approach.
We employed the concept of Super-resolution Luminescence Micro Spectroscopy (SuperLuMS) to combine super-resolution imaging with spectral measurements31, 44. The idea here is to fit the emission pattern with a combination of several Gaussian peaks, representing the emission from the localized tetragonal domains, and a background emission more uniformly distributed over the NW (Supplementary Note 3). The latter, as we have discussed above, was coming from the orthorhombic phase, and we were able to determine its contribution using the spectral information from the same experiment (Supplementary Figs. 5, 6).
Figure 3 shows the appearance of NW#1 PL images at different temperatures and the results of the fitting procedure applied to the image at 145 K integrated over the NW width. As one can see, the emission pattern can indeed be modeled by an almost uniform background estimated from the orthorhombic phase emission plus four Gaussian peaks characterized by their width and the position of the maximum along the NW (y-axis). The position of the peak gives the PL intensity-weighted center of the tetragonal domains, while the width of the peak can be deconvoluted in order to characterize the domain radius (Supplementary Note 4). The temperature dependencies of the domain center positions and sizes demonstrate that the domains were decreasing in size upon cooling. Domains B and C were initially ~300–400 nm in radius and decreased below the reliable detection limit (100 nm) upon further cooling. Domain A was consistently smaller than 100 nm.
Discussion
The PL quantum yield is determined by the ratio of the efficiencies of the radiative and non-radiative recombination processes. Although the radiative rate in semiconductors is dependent on the concentration of charge carriers9 (since the excitation conditions were kept constant in our experiments), we conclude that the PL enhancement at the phase transition temperatures must mainly be due to a drastic reduction of the non-radiative rates in domains of the tetragonal phase. Non-radiative processes have been discussed in numerous literature reports and attributed to PL quenching on trap states18. In order to explain the PL enhancement, we then need to assume that either the concentration of traps or the efficiency of charge carrier transport toward the traps dramatically decrease in the phase transition temperature region. Below we will argue that both effects most probably take place.
Indeed, it is known that when a solid transforms from one crystal phase to another, the nucleation process depends on the local properties of the material and in particular on the presence of structural and chemical defects45,46,47,48. Theoretically, for first-order phase transitions occurring between phases of different symmetry it is the so-called random local field defects that are especially important40, 41. Depending on the symmetry of such a defect, it can stimulate the transition toward the structure of either higher or lower degree of symmetry. In other words, depending on the symmetry of the defects, the phase transition temperature can increase or decrease. Difference in the local concentration of such defects can result in the phase transition occurring at different temperatures at different spatial locations in the sample. On the basis of this general phenomenon, we present a model below which can qualitatively explain our experimental observations and consolidate the literature results.
Figure 5 shows a schematic picture of our model. Let us consider the cooling cycle. We assume that the temperature of the transition from tetragonal to orthorhombic phase is higher for domains with high defect concentration (~160 K) and lower for domains with a lower defect concentration (~140 K). Therefore, the defects causing PL quenching stimulate formation of the low-symmetry orthorhombic phase at higher temperatures, or, in other words, they make the low-symmetry phase stable at higher temperature. Thus, at temperatures slightly below 160 K most of the crystal domains with large concentration of such defects must already be in the high-bandgap orthorhombic phase, while most of the relatively clean material remains in the more symmetric tetragonal phase of the lower bandgap. When illuminated at 485 nm, both phases are excited and most of the mobile charges should migrate to low-bandgap tetragonal domains due to the funneling effect, leading to a higher PL quantum yield because these domains possess lower defect concentration12. We also experimentally observed funneling of charge carries from the orthorhombic to the tetragonal domains12 as an increase in PL intensity in the tetragonal phase with the time constant 0.4 ns (Supplementary Fig. 8). Thus, the charge carrier funneling and their confinement in the tetragonal phase domains, which possess a lower concentration of PL quenching defects, explains the emission enhancement effect.
As soon the entire volume of the crystal is transformed to the orthorhombic phase, both effects are gone and the PL intensity drops down. If we heat the sample up, the exact same sequence of events will lead to the similar PL intensity/spectrum behavior but in the reverse order (Fig. 5).
Since breaking into nanodomains of different phases is a random process, although dependent on the concentration and nature of local defects, it is probably not so surprising to observe NW#1 exhibiting the strongest PL enhancement in spatial segment C (Fig. 4), which in fact possessed the lowest PL intensity at room temperature compared to the other regions of the same NW (Fig. 2). It shows that eliminating contributions of the defected regions to PL of the crystal can lead to drastically different spatial emission patterns reflecting local inhomogeneities of the defect concentration and peculiarities of charge diffusion at the nanoscale.
This simple model where a very efficient carrier diffusion over the whole NW is assumed has some difficulties to explain why the PL was gradually decreasing upon further cooling instead of being quasi-constant in the temperature region where pure tetragonal domains are present in the dominant orthorhombic phase (from 150 to 135 K for the cooling cycle). Indeed, due to the charge carrier funneling, even a very small tetragonal domain at, e.g., 135 K should be as bright as the same domain but of a larger size at 150 K. This is, however, not the case as illustrated for peak C in Fig. 4e. To explain this, we propose that the charge carrier funneling distance (or migration volume of charge carries) is substantially smaller than the size of the whole NW. In this case, recombination in a gradually increasing volume of the orthorhombic phase will compete with funneling to the gradually decreasing tetragonal inclusions leading to a decrease in the emission intensity of the latter. In addition, decreasing the domain size may give rise to strain-induced, non-radiative recombination channels.
We also believe that decreasing of the domain size is the reason of the blue shift of the tetragonal phase PL spectrum when cooling over the phase transition region (Fig. 1c). Note that this shift is the opposite of the shift we observed upon cooling of the sample in the pure tetragonal phase (160 K < T < 300 K). Shifting the bandgap toward higher energy means geometrical deformation of the crystal structure toward a smaller Pb–I–Pb bond angle as has been shown theoretically38, 49. Variations of the bandgap energies have also been observed experimentally in perovskite samples with different characteristic sizes, where it was related to the surface-induced strain in small crystallites25, 50. Thus, in the framework of our model, the closer the temperature is to 140 K (in the cooling cycle), the smaller the sizes of the tetragonal inclusions are. Smaller domain sizes mean larger stress from the bulk orthorhombic phase surrounding the tetragonal nanoinclusions, which results in a blue-shifted PL spectrum. The variety of the domain sizes can also explain the variation of the peak position for both PL bands at the different regions of the NW (see Fig. 4d).
Coexistence of nanodomains of different phases inside intact crystals is the origin of several different phenomena and their temperature hysteresis. For example, it should hinder charge diffusion because of charge trapping in domains of the tetragonal phase, as well as scattering on domain boundaries. This agrees with the decrease in charge carrier mobility in MAPbI3 reported around the phase transition temperature of 150 K and its thermal hysteresis43. Solar cell devices exhibit a discontinuity in photovoltaic performance, especially in the trend of the open circuit voltage through the phase transition51. A very strong thermal hysteresis of optical properties was reported for polycrystalline films of MAPbI3 studied by confocal PL microscopy33. Even for large single crystals, thermal hysteresis of absorption spectra, mechanical properties, and geometry of large single crystals of organic–inorganic (C12H25NH3)2PbI4 perovskites was observed52, which is in agreement with our results on individual highly crystalline NWs. As it is the usual case for the first-order phase transitions in solids, the nucleation process depends on the mechanical strain in the crystal, which in turn depends on the nucleation. Therefore, the whole process depends on its history leading to hysteresis. In terms of our model, both defected and clean domains of the crystal possess thermal hysteresis, which leads to the hysteresis of the PL enhancement as well (Fig. 1b).
Besides the current study on the single object level, observation of PL enhancement in the phase transition region has been reported for thin film samples in several publications7, 33. The extent of the enhancement and the temperature interval of the enhanced PL vary a lot from sample to sample and even from one individual crystal to another (Fig. 1). However, the general trend that seems to be present is that higher disorder and polycrystallinity result in a less sharp PL enhancement and a broader temperature region of enhanced PL where both phases coexist.
There is a great variety of intrinsic defects (vacancies, substitutions, and interstitials) possible in MAPbI3 26. In principle, defects influencing the phase transition can be of any type and are located in the bulk or on the surface of the crystal. The phase transition may even be induced/prevented by a grain boundary in a polycrystal. The only criterion we can use to select possible defects crucial for the phase transition in the samples possessing PL enhancement is that they, in comparison to other defects, must be the most important channels for non-radiative recombination. If we assume quenching by Shockley–Read–Hall non-radiative recombination, the defects should have relatively deep levels in the bandgap. According to ref. 26 such deep traps can be IMA, IPb and PbI substitutions and Pbi interstitials.
Note that a small extent or even the absence of PL enhancement, which some reports seem to show53, by no means undermines the generality of our model. It only implies that the defects that were determining the phase transition dynamics in those samples were not the ones that were crucial for their PL quantum yield. In this case the local PL yield becomes insensitive to local crystal phase.
In summary, we present a spatially resolved luminescence spectroscopy study of PL temperature dependence for individual MAPbI3 NWs. We confirm the coexistence of domains of both tetragonal and orthorhombic phases in single NWs of high crystallinity across the phase transition temperature region between 160 and 140 K where a strong enhancement by one order of magnitude of the PL quantum yield at ~150 K was observed. Hysteresis of the PL spectrum and PL quantum yield was also seen. The largest observed crystal phase domains possessed sizes in the range of 100–500 nm as estimated by super-resolution analysis of the luminescence images.
We propose that the phase transition temperature in OMHPs is dependent on the defect concentration and their type. Using this concept we can readily explain the PL enhancement effect by suggesting that crystal regions with higher defect concentration transform to the orthorhombic phase at higher temperature upon cooling compared to more pristine crystal regions. Thus, transforming the defected regions to the orthorhombic phase increases PL intensity dramatically. This is because PL stems mostly from low-defect density tetragonal inclusions harvesting charge carriers from higher-energy orthorhombic phase domains. During cooling, physical sizes of the tetragonal inclusions become smaller, which increases the internal strain leading to the observed blue shift of the PL spectrum.
Dependence of the phase transition temperature on the local defect concentration means dependence on the sample preparation, which explains the lack of consensus in the literature on the value of the transition temperature. We stress that our experiment at the single NW level shows that the spread of the transition temperature over tens of degrees Kelvin is an intrinsic effect for MAPbI3 related to defects in general, but not just the consequence of sample polycrystallinity and effects of the grain boundaries. The effect of freezing out defects of a certain type in a particular crystalline phase may lead to ideas of material manipulation based on, e.g., repeatedly running a sample through cooling–heating cycles across the phase transition, which may lead to enhanced optoelectronic properties.
Methods
Sample preparation
NWs of methylammonium lead iodide, CH3NH3PbI3, were synthesized using a procedure described in literature (Supplementary Note 1 and Supplementary Figs. 1, 2)8. Lead acetate was drop-cast from a 100 mg ml−1 solution of PbAc23H2O in water onto cleaned glass slides placed on a hot plate at 65 °C. The films were dried for ~30 min and then immersed into a solution of 40 mg ml−1 methylammonium iodide in isopropanol. The sample was left to convert for at least 24 h to form a sample of NWs and nanoplatelets shown in Supplementary Fig. 1. Individual NWs were mechanically transferred onto Si/SiO2 substrate for PL microspectroscopy measurements. To prepare the thin film sample, we dissolved methylammonium iodide and lead iodide precursors in dimethylformamide (1:1 molar ratio). 100 μl of this solution was then spin-cast onto a glass coverslip for 1 min at 1500 rpm followed by annealing on a hot plate for 45 min at 80 °C.
Temperature-dependent PL microspectroscopy measurements
Temperature-dependent PL microspectroscopy measurements were performed in a variable temperature liquid nitrogen cryostat using a home-built, wide-field luminescence microscope based on Olympus IX71 (Supplementary Note 2). Diode laser (485 nm) in CW mode and pulse mode was used as the excitation source. The luminescence image of single NWs was obtained by ×40 objective lens and detected by the charged-couple device camera after passing through a transmission grating in order to obtain their spectra. Time-resolved PL was measured using a time-correlated single-photon counting system together with excitation by a 485 nm diode laser operating in the pulsed mode. The luminescence was detected by a fast avalanche photodiode coupled with a PicoQuant PicoHarp 300 counting module.
Data availability
The data that support this study are available from the corresponding author upon request.
References
Green, M. A., Ho-Baillie, A. & Snaith, H. J. The emergence of perovskite solar cells. Nat. Photon. 8, 506–514 (2014).
Yang, W. S. et al. High-performance photovoltaic perovskite layers fabricated through intramolecular exchange. Science 348, 1234–1237 (2015).
Brenner, T. M., Egger, D. A., Kronik, L., Hodes, G. & Cahen, D. Hybrid organic—inorganic perovskites: low-cost semiconductors with intriguing charge-transport properties. Nat. Rev. Mater 1, 15007 (2016).
Stranks, S. D. et al. Electron-hole diffusion lengths exceeding 1 micrometer in an organometal trihalide perovskite absorber. Science 342, 341–344 (2013).
Xing, G. et al. Long-range balanced electron- and hole-transport lengths in organic-inorganic CH3NH3PbI3. Science 342, 344–347 (2013).
Tan, Z.-K. et al. Bright light-emitting diodes based on organometal halide perovskite. Nat. Nanotechnol. 9, 687–692 (2014).
Xing, G. et al. Low-temperature solution-processed wavelength-tunable perovskites for lasing. Nat. Mater. 13, 476–480 (2014).
Zhu, H. et al. Lead halide perovskite nanowire lasers with low lasing thresholds and high quality factors. Nat. Mater. 14, 636–642 (2015).
Pelant, I.; Valenta, J. Luminescence Spectroscopy of Semiconductors. (Oxford University Press, 2012).
Fang, H.-H. et al. Photophysics of organic-inorganic hybrid lead iodide perovskite single crystals. Adv. Funct. Mater. 25, 2378–2385 (2015).
Wu, K. et al. Temperature-dependent excitonic photoluminescence of hybrid organometal halide perovskite films. Phys. Chem. Chem. Phys. 16, 22476–22481 (2014).
Kong, W. et al. Characterization of an abnormal photoluminescence behavior upon crystal-phase transition of perovskite CH3NH3PbI3. Phys. Chem. Chem. Phys. 17, 16405–11 (2015).
Saba, M. et al. Correlated electron–hole plasma in organometal perovskites. Nat. Commun. 5, 5049 (2014).
Stranks, S. D. et al. Recombination kinetics in organic-inorganic perovskites: excitons, free charge, and subgap states. Phys. Rev. Appl. 2, 034007 (2014).
Kim, J., Lee, S.-H., Lee, J. H. & Hong, K. The role of intrinsic defects in methylammonium lead iodide perovskite. J. Phys. Chem. Lett. 5, 1312–1317 (2014).
Christians, J. A., Manser, J. S. & Kamat, P. V. Multifaceted excited state of CH3NH3PbI3. Charge separation, recombination, and trapping. J. Phys. Chem. Lett. 6, 2086–2095 (2015).
Wehrenfennig, C., Liu, M., Snaith, H. J., Johnston, M. B. & Herz, L. M. Charge carrier recombination channels in the low-temperature phase of organic-inorganic lead halide perovskite thin films. APL Mater 2, 081513 (2014).
Manser, J. S., Christians, J. A. & Kamat, P. V. Intriguing optoelectronic properties of metal halide perovskites. Chem. Rev. 116, 12956–13008 (2016).
Tian, Y. et al. Mechanistic insights into perovskite photoluminescence enhancement: light curing with oxygen can boost yield thousandfold. Phys. Chem. Chem. Phys. 17, 24978–24987 (2015).
Fang, H.-H., Wang, F., Adjokatse, S., Zhao, N. & Loi, M. A. Photoluminescence enhancement in formamidinium lead iodide thin films. Adv. Funct. Mater. 26, 4653–4659 (2016).
Tian, Y. et al. Enhanced organo-metal halide perovskite photoluminescence from nanosized defect-free crystallites and emitting sites. J. Phys. Chem. Lett. 6, 4171–4177 (2015).
deQuilettes, D. W. et al. Photo-induced halide redistribution in organic–inorganic perovskite films. Nat. Commun. 7, 11683 (2016).
Grancini, G. et al. Role of microstructure in the electron–hole interaction of hybrid lead halide perovskites. Nat. Photon. 9, 695–701 (2015).
de Quilettes, D. W. et al. Impact of microstructure on local carrier lifetime in perovskite solar cells. Science 348, 683–686 (2015).
Grancini, G. et al. The impact of the crystallization processes on the structural and optical properties of hybrid perovskite films for photovoltaics. J. Phys. Chem. Lett. 5, 3836–3842 (2014).
Yin, W.-J., Shi, T. & Yan, Y. Unusual defect physics in CH3NH3PbI3 perovskite solar cell absorber. Appl. Phys. Lett. 104, 063903 (2014).
Chen, Y., He, M., Peng, J., Sun, Y. & Liang, Z. Structure and growth control of organic-inorganic halide perovskites for optoelectronics: from polycrystalline films to single crystals. Adv. Sci. 3, 1500392 (2016).
Hoke, E. T. et al. Reversible photo-induced trap formation in mixed-halide hybrid perovskites for photovoltaics. Chem. Sci 6, 613–617 (2015).
Zhu, F. et al. Shape evolution and single particle luminescence of organometal halide perovskite nanocrystals. ACS Nano 9, 2948–2959 (2015).
Bischak, C. G., Sanehira, E. M., Precht, J. T., Luther, J. M. & Ginsberg, N. S. Heterogeneous charge carrier dynamics in organic–inorganic hybrid materials: nanoscale lateral and depth-dependent variation of recombination rates in methylammonium lead halide perovskite thin films. Nano Lett. 15, 4799–4807 (2015).
Merdasa, A. et al. Super-resolution luminescence microspectroscopy reveals the mechanism of photoinduced degradation in CH 3 NH 3 PbI 3 perovskite nanocrystals. J. Phys. Chem. C 120, 10711–10719 (2016).
Täuber, D., Dobrovolsky, A., Camacho, R. & Scheblykin, I. G. Exploring the electronic band structure of organometal halide perovskite via photoluminescence anisotropy of individual nanocrystals. Nano Lett. 16, 5087–5094 (2016).
Osherov, A. et al. The impact of phase retention on the structural and optoelectronic properties of metal halide perovskites. Adv. Mater. 28, 10757–10763 (2016).
Baikie, T. et al. Synthesis and crystal chemistry of the hybrid perovskite (CH3NH3)PbI3 for solid-state sensitised solar cell applications. J. Mater. Chem. A 1, 5628 (2013).
Onoda-Yamamuro, N., Matsuo, T. & Suga, H. Calorimetric and IR spectroscopic studies of phase transitions in methylammonium trihalogenoplumbates (II). J. Phys. Chem. Solids 51, 1383–1395 (1990).
Stoumpos, C. C., Malliakas, C. D. & Kanatzidis, M. G. Semiconducting tin and lead iodide perovskites with organic cations: phase transitions, high mobilities, and near-infrared photoluminescent properties. Inorg. Chem. 52, 9019–9038 (2013).
Quarti, C. et al. Structural and optical properties of methylammonium lead iodide across the tetragonal to cubic phase transition: implications for perovskite solar cells. Energy Environ. Sci. 9, 155–163 (2016).
Geng, W., Zhang, L., Zhang, Y.-N., Lau, W.-M. & Liu, L.-M. First-principles study of lead iodide perovskite tetragonal and orthorhombic phases for photovoltaics. J. Phys. Chem. C 118, 19565–19571 (2014).
D’Innocenzo, V. et al. Excitons versus free charges in organo-lead tri-halide perovskites. Nat. Commun. 5, 3586 (2014).
Levanyuk, A. P. & Sigov, A. S. Defects and Structural Phase Transitions. (Gordon and Breach, 1987).
Levanyuk, A. P., Minyukov, S. A. & Vallade, M. Influence of defects on structural phase transitions. J. Phys. Condens. Matter 9, 5313–5320 (1997).
Varshni, Y. P. Temperature dependence of the energy gap in semiconductors. Physica 34, 149–154 (1967).
Li, D. et al. Size-dependent phase transition in methylammonium lead iodide perovskite microplate crystals. Nat. Commun. 7, 11330 (2016).
Small, A. & Stahlheber, S. Fluorophore localization algorithms for super-resolution microscopy. Nat. Methods 11, 267–279 (2014).
Rao, C. N. R. & Rao, K. J. Phase Transitions in Solids. (McGraw-Hill, 1978).
Fan, S. et al. Defect evolution during the phase transition of hexagonal nickel sulfide studied by positron annihilation spectroscopy. Solid State Commun 202, 64–68 (2015).
Donev, E. U., Lopez, R., Feldman, L. C. & Haglund, R. F. Confocal raman microscopy across the metal−insulator transition of single vanadium dioxide nanoparticles. Nano Lett. 9, 702–706 (2009).
Brockman, J. et al. Increased metal-insulator transition temperatures in epitaxial thin films of V2O3 prepared in reduced oxygen environments. Appl. Phys. Lett. 98, 152105 (2011).
Filip, M. R., Eperon, G. E., Snaith, H. J. & Giustino, F. Steric engineering of metal-halide perovskites with tunable optical band gaps. Nat. Commun. 5, 5757 (2014).
D’Innocenzo, V., Srimath Kandada, A. R., De Bastiani, M., Gandini, M. & Petrozza, A. Tuning the light emission properties by band gap engineering in hybrid lead halide perovskite. J. Am. Chem. Soc. 136, 17730–17733 (2014).
Barone, C. et al. Unravelling the low-temperature metastable state in perovskite solar cells by noise spectroscopy. Sci. Rep. 6, 34675 (2016).
Yangui, A. et al. Rapid and robust spatiotemporal dynamics of the first-order phase transition in crystals of the organic-inorganic perovskite (C12H25NH3)2PbI4. Sci. Rep. 5, 16634 (2015).
Savenije, T. J. et al. Thermally activated exciton dissociation and recombination control the carrier dynamics in organometal halide perovskite. J. Phys. Chem. Lett. 5, 2189–2194 (2014).
Acknowledgements
The work was supported by the Crafoord, Knut&Alice Wallenberg, and Carl Trygger foundations, the Swedish Research Council and NanoLund. A.D. thanks Carl Trygger foundation for postdoctoral scholarship. E.L.U. thanks The Swedish Research Council and Marie Sklodowska Curie Actions, Cofund, Project INCA 600398 for financial support. We thank Jun Li (Chemical Physics, Lund University) for assistance with the sample preparation.
Author information
Authors and Affiliations
Contributions
A.D. and I.G.S.: Designed the experiments. A.D.: Performed all optical experiments and SEM/STEM characterization, analyzed the data, and participated in developing the data interpretation and writing the paper. A.M.: Applied the super-resolution approach to the optical data and participated in writing the paper. E.L.U.: Prepared samples and performed XRD characterization. E.L.U. and A.Y.: Participated in developing of the data interpretation and writing. I.G.S.: Proposed the key concepts for the data interpretation and wrote the paper.
Corresponding author
Ethics declarations
Competing interests
The authors declare no competing financial interests.
Additional information
Publisher's note: Springer Nature remains neutral with regard to jurisdictional claims in published maps and institutional affiliations.
Electronic supplementary material
Rights and permissions
Open Access This article is licensed under a Creative Commons Attribution 4.0 International License, which permits use, sharing, adaptation, distribution and reproduction in any medium or format, as long as you give appropriate credit to the original author(s) and the source, provide a link to the Creative Commons license, and indicate if changes were made. The images or other third party material in this article are included in the article’s Creative Commons license, unless indicated otherwise in a credit line to the material. If material is not included in the article’s Creative Commons license and your intended use is not permitted by statutory regulation or exceeds the permitted use, you will need to obtain permission directly from the copyright holder. To view a copy of this license, visit http://creativecommons.org/licenses/by/4.0/
About this article
Cite this article
Dobrovolsky, A., Merdasa, A., Unger, E.L. et al. Defect-induced local variation of crystal phase transition temperature in metal-halide perovskites. Nat Commun 8, 34 (2017). https://doi.org/10.1038/s41467-017-00058-w
Received:
Accepted:
Published:
DOI: https://doi.org/10.1038/s41467-017-00058-w