Effect of Cathodic Polarization Potential on Hydrogen Induced Stress Cracking of Duplex Stainless SteelChang et al., 2013
- Document ID
- 980872251457760924
- Author
- Chang W
- Zhang L
- Wang J
- Yang P
- Wang X
- Lu M
- Publication year
- Publication venue
- NACE CORROSION
External Links
Snippet
Hydrogen induced stress cracking (HISC) has sometimes been experienced when duplex stainless steels are applied as subsea facilities under cathodic protection (CP). The effects of cathodic potential on HISC of duplex stainless steel were studied by electrochemical …
- 229910001039 duplex stainless steel 0 title abstract description 37
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/58—Ferrous alloys, e.g. steel alloys containing chromium with nickel with more than 1.5% by weight of manganese
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Han et al. | Hydrogen embrittlement sensitivity of X100 pipeline steel under different pre-strain | |
| Hao et al. | Electrochemical characterization and stress corrosion cracking of E690 high strength steel in wet-dry cyclic marine environments | |
| Wu et al. | Corrosion behavior of low-alloy steel containing 1% chromium in CO2 environments | |
| Sun et al. | Effect of sulfate-reducing bacteria and cathodic potential on stress corrosion cracking of X70 steel in sea-mud simulated solution | |
| Wan et al. | The effect of hydrogen on stress corrosion behavior of X65 steel welded joint in simulated deep sea environment | |
| Wang et al. | Electrochemical corrosion performance of Cr and Al alloy steels using a J55 carbon steel as base alloy | |
| Zhu et al. | Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution | |
| Qi et al. | Effect of immersion time on the hydrogen content and tensile properties of A350LF2 steel exposed to hydrogen sulphide environments | |
| Ma et al. | Effect of cathodic potentials on the SCC behavior of E690 steel in simulated seawater | |
| Chen et al. | Influence of H2S interaction with prestrain on the mechanical properties of high-strength X80 steel | |
| Elhoud et al. | Hydrogen embrittlement of super duplex stainless steel in acid solution | |
| Zheng et al. | Effect of hydrogen and inclusions on the tensile properties and fracture behaviour of A350LF2 steels after exposure to wet H2S environments | |
| Yu et al. | Experimental and numerical simulation of fatigue corrosion behavior of V150 high-strength drill pipe in air and H2S-dilling mud environment | |
| McCoy et al. | Investigation of the effects of Hydrogen on High Strength Precipitation Hardened Nickel alloys for O&G service | |
| Wu et al. | Microbiologically assisted cracking of X70 submarine pipeline induced by sulfate-reducing bacteria at various cathodic potentials | |
| Li et al. | Corrosion crack failure analysis of 316L hydraulic control pipeline in high temperature aerobic steam environment of heavy oil thermal recovery well | |
| Peng et al. | Material optimization of drill pipe in complex wellbore environments by comparing fatigue life and cost | |
| Luo et al. | Sulfide stress corrosion cracking behavior of G105 and S135 high-strength drill pipe steels in H2S environment | |
| Ziaei et al. | Failure analysis: chloride stress corrosion cracking of AISI 316 stainless steel downhole pressure memory gauge cover | |
| Tagliari et al. | Tensile armor wires submitted to slow strain rate tests in a corrosive environment and cathodic protection: a comparison between two different microstructures | |
| Sun et al. | Analysis of stress corrosion cracking failure of 316L stainless steel flow promoter string in the aggressive oilfield environment | |
| Yan et al. | Corrosion behaviors of SMSS 13Cr and DSS 22Cr in H2S/CO2-oil-water environment | |
| Zhang et al. | Effect of temperature on corrosion behavior of VM110SS casing steel in the CO2/H2S coexistent environment | |
| Chang et al. | Effect of Cathodic Polarization Potential on Hydrogen Induced Stress Cracking of Duplex Stainless Steel | |
| Qi et al. | Effect of H2S partial pressure on the tensile properties of A350LF2 steel in the absence and presence of pre-immersion |