Prange, 1959 - Google Patents
Corrosion in a hydrocarbon conversion systemPrange, 1959
- Document ID
- 8901653561644128982
- Author
- Prange F
- Publication year
- Publication venue
- Corrosion
External Links
Snippet
Under some inexactiy defined conditions, steels and alloys are attacked by atmospheres resulting from oxidation of hydrocarbon. In a fixed-bed catalytic system for dehydrogenation of butane the metal loss which contaminates the catalyst with a fine oxide dust causes …
- 239000004215 Carbon black (E152) 0 title abstract description 4
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Hoyt et al. | High temperature metal deterioration in atmospheres containing carbon-monoxide and hydrogen | |
| Prange | Corrosion in a hydrocarbon conversion system | |
| JPS6331535A (en) | Apparatus for treating carbon-containing compound having carbon precipitation suppressing property | |
| Greenert | High Temperature Slag Corrosion of Metallic Materials: Part 3—Comparative Resistance of Materials | |
| Hodges | Intergranular corrosion in high purity ferritic stainless steels: Isothermal time-temperature sensitization measurements | |
| Setterlund et al. | Corrosion characteristics of iron-aluminum and iron-chromium-Aluminum alloys in high temperature petroleum applications | |
| Holzworth et al. | The mechanism of knife-line attack in welded type 347 stainless steel | |
| Soma et al. | Multilayered surface oxides within crevices of type 316L stainless steels in high-temperature pure water | |
| Daigo et al. | Effect of chromium ion from autoclave material on corrosion behavior of nickel-based alloys in supercritical water | |
| Klöwer et al. | Metal dusting and carburization resistance of nickel-base alloys | |
| Vuelvas-Rayo et al. | Hot Corrosion Behavior of High‐Chromium, High‐Carbon Cast Irons in NaCl‐KCl Molten Salts | |
| Demo et al. | Intergranular corrosion and embrittlement of ferritic stainless steels | |
| Hill et al. | Metallic corrosion in coal gasification pilot plants | |
| Beck et al. | Corrosion by Aqueous Solutions at Elevated Temperatures and Pressures | |
| de Bruyn et al. | Materials experience in a methane reforming plant | |
| Govorun et al. | Theoretical substantiation and development of economically alloyed welding materials | |
| Heger et al. | Effect of minor constituents on the intergranular corrosion of austenitic stainless steels | |
| Tokura et al. | Coke formation on preoxidized iron and nickel in a CH4-H2 gas atmosphere at 1,000° C | |
| Hopkinson et al. | Internal carburization and oxidation of nickel-chromium alloys in carbon monoxide type atmospheres | |
| McCoy | Corrosion rates for H2S at elevated temperatures in refinery hydrodesulfurization processes | |
| Doi et al. | Investigation of segregation during oxidation of Ni–Cu alloy by in situ photoelectron spectroscopy | |
| Schley et al. | Destructive Accumulation of Nitrogen in 30 Cr 20 Ni Cast Furnace Tubes in Hydrocarbon Cracking Service at 1100 C | |
| Bloom et al. | Corrosion of Steel in Concentrated Lithium Hydroxide Solution at 316 C | |
| Roach | Carburization of cast heat-resistant alloys | |
| Backensto et al. | High-Temperature Hydrogen Sulfide Corrosion of Stainless Steels—A Contribution to the Work of NACE Technical Group Committee T-8 on Refinery Industry Corrosion |