Experimental determination of the failure surface for DP980 high-strength metal sheets considering stress triaxiality and Lode angleKim et al., 2019
View PDF- Document ID
- 7169821643373960169
- Author
- Kim M
- Lee H
- Hong S
- Publication year
- Publication venue
- The International Journal of Advanced Manufacturing Technology
External Links
Snippet
To meet requirements for reduced fuel consumption of cars, the use of components made of sheets of high-strength steel instead of conventional steel has been on the rise. However, low ultimate elongation of high-strength steel often causes problems during plastic …
- 229910052751 metal 0 title description 9
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Kim et al. | Experimental determination of the failure surface for DP980 high-strength metal sheets considering stress triaxiality and Lode angle | |
| Sun et al. | Determination of mechanical properties of the weld line by combining micro-indentation with inverse modeling | |
| Lee et al. | Fracture in cold upset forging-a criterion and model | |
| Kacem et al. | Failure prediction in the hole-flanging process of aluminium alloys | |
| Dziallach et al. | Sheet metal testing and flow curve determination under multiaxial conditions | |
| Zhang et al. | Comparative experimental study of hot-formed, hot-finished and cold-formed rectangular hollow sections | |
| Qian et al. | Prediction of edge fracture during hole-flanging of advanced high-strength steel considering blanking pre-damage | |
| Haddag et al. | Tribological behaviour and tool wear analyses in rough turning of large-scale parts of nuclear power plants using grooved coated insert | |
| Zeng et al. | Investigation on spinnability of profiled power spinning of aluminum alloy | |
| Kong et al. | Deep drawing and bulging forming limit of dual-phase steel under different mechanical properties | |
| Li et al. | Analysis on fracture initiation and fracture angle in ductile sheet metal under uniaxial tension by experiments and finite element simulations | |
| Li et al. | Fatigue crack growth law of API X80 pipeline steel under various stress ratios based on J‐integral | |
| Kuwabara et al. | Hole expansion simulation considering the differential hardening of a sheet metal | |
| Cavenagh et al. | Influence of the cover plate thickness on the ballistic penetration of re-entrant auxetic structures | |
| Nasheralahkami et al. | Study of sheared edge formability of ultra-high strength DP980 sheet metal blanks | |
| Zheng et al. | Study of thermal forming limit of medium-Mn steel based on finite element analysis and experiments | |
| Huang et al. | Fracture prediction and correlation of alsi hot stamped steels with different models in LS DYNA | |
| Kim et al. | Prediction of shear fracture in multi-stage deep drawing process including ironing process for Al3003 sheet | |
| Vasilescu | Development of a hydraulic bulge test to determine the work hardening behaviour of sheet materials | |
| Ban et al. | Residual stress modelling for stainless-clad bimetallic steel welded circular sections | |
| Yu et al. | Numerical simulation on edge crack of advanced high-strength steel considering blanking induced damage | |
| Toros et al. | The Effects of Material Thickness and Deformation Speed on Springback Behavior of DP600 Steel | |
| Lenzen et al. | Improvement of the drawing ratio of the anisotropic material behaviour under near plane strain conditions for DP600 characterized in elliptic hydraulic bulge test | |
| Seifi et al. | J-integral and CMOD for external inclined cracks on autofrettaged cylinders | |
| Krawczyk et al. | The influence of the punch shape and the cutting method on the limit strain in the hole expansion test |