DR Thornton BSc, 1970 - Google Patents
INGOT TEEMING PRACTICEDR Thornton BSc, 1970
- Document ID
- 6982438616711542529
- Author
- DR Thornton BSc A
- Publication year
- Publication venue
- Steel Times
External Links
Snippet
These are deoxidised steels, in which no gases are evolved during solidification. They are particularly prone to cracking, especially in the 0.18%-0.23% C range (peritectic range). Generally speaking, if the teeming temperature and speed are correct, the cracking …
- 229910000831 Steel 0 abstract description 76
Classifications
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21C—PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
- C21C5/00—Manufacture of carbon-steel, e.g. plain mild steel, medium carbon steel or cast steel or stainless steel
- C21C5/28—Manufacture of steel in the converter
- C21C5/30—Regulating or controlling the blowing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21C—PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
- C21C7/00—Treating molten ferrous alloys, e.g. steel, not covered by groups C21C1/00 - C21C5/00
- C21C7/04—Removing impurities by adding a treating agent
- C21C7/06—Deoxidising, e.g. killing
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21C—PROCESSING OF PIG-IRON, e.g. REFINING, MANUFACTURE OF WROUGHT-IRON OR STEEL; TREATMENT IN MOLTEN STATE OF FERROUS ALLOYS
- C21C1/00—Refining of pig-iron; Cast iron
- C21C1/10—Making spheroidal graphite cast-iron
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/10—Supplying or treating molten metal
- B22D11/11—Treating the molten metal
- B22D11/116—Refining the metal
- B22D11/118—Refining the metal by circulating the metal under, over or around weirs
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/04—Continuous casting of metals, i.e. casting in indefinite lengths into open-ended moulds
- B22D11/0401—Moulds provided with a feed head
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D41/00—Casting melt-holding vessels, e.g. ladles, tundishes, cups or the like
- B22D41/14—Closures
- B22D41/44—Consumable closure means, i.e. closure means being used only once
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/06—Continuous casting of metals, i.e. casting in indefinite lengths into moulds with travelling walls, e.g. with rolls, plates, belts, caterpillars
- B22D11/0637—Accessories therefor
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D27/00—Treating the metal in the mould while it is molten or ductile ; Pressure or vacuum casting
- B22D27/003—Treating the metal in the mould while it is molten or ductile ; Pressure or vacuum casting by using inert gases
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| KR102204170B1 (en) | Gray cast iron inoculant | |
| CN105316558B (en) | Preparation method of boron-containing steel preventing casting blank corner cracking | |
| US3819365A (en) | Process for the treatment of molten metals | |
| EP0512118B1 (en) | Process for continuous casting of ultralow-carbon aluminum-killed steel | |
| DR Thornton BSc | INGOT TEEMING PRACTICE | |
| CA1178014A (en) | Foundry practices | |
| US4348800A (en) | Production of steel products with medium to high contents of carbon and manganese and superior surface quality | |
| US4039326A (en) | Antiscorific powder for the casting of steels into ingot molds | |
| US3718173A (en) | Method of removing alumina scum from a continuous-casting mold | |
| Manninen et al. | Low reoxidation tundish metallurgy at Fundia Koverhar steel plant | |
| CN112501487A (en) | Smelting process and application of 18CrNiMo7-6 steel | |
| US4936553A (en) | Method for retaining slag during the discharge of molten metal from a vessel | |
| EP0268632B1 (en) | Improvements in or relating to the production of iron | |
| GB1428204A (en) | Methood for adding lead to molten steel in a ladle | |
| KR100362659B1 (en) | A method of manufacturing medium carbon steel plate for offshore structure | |
| US4411056A (en) | Production of steel products with medium to high contents of carbon and manganese and superior surface quality | |
| CN208879692U (en) | A kind of reduce pours remaining steel pack lining structure | |
| JPS6345901B2 (en) | ||
| SU1538987A1 (en) | Method of bottom casting of steel | |
| CN116179942A (en) | A kind of 20MnCrS5 steel and its preparation method and application | |
| SU1533823A1 (en) | Method of pouring steel | |
| Iyengar | Rapporteur's Summary | |
| SU781218A1 (en) | Method of low-alloy steel production | |
| Leach | Alloy Steelmaking for Large Forgings | |
| JPS60250860A (en) | Continuous casting method of active molten metal |