Dealuminization of Aluminum BronzeSchussler et al., 1956
- Document ID
- 5204549390122992836
- Author
- Schussler M
- Napolitan D
- Publication year
- Publication venue
- Corrosion
External Links
Snippet
A the widespread use of aluminum bronzes in industry. Among considerations which may be listed are the high physical strength of such alloys, their resistance to wear and galling, resistance to corro-sion and erosion, relative ease of fabrication and low cost. In certain …
- 229910052782 aluminium 0 title abstract description 37
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22F—CHANGING THE PHYSICAL STRUCTURE OF NON-FERROUS METALS AND NON-FERROUS ALLOYS
- C22F1/00—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working
- C22F1/10—Changing the physical structure of non-ferrous metals or alloys by heat treatment or by hot or cold working of nickel or cobalt or alloys based thereon
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Denhard | Effect of composition and heat treatment on the stress corrosion cracking of austenitic stainless steels | |
| Gest et al. | Stress corrosion and hydrogen embrittlement in an aluminum alloy | |
| Streicher | Effect of composition and structure on crevice, intergranular, and stress corrosion of some wrought Ni-Cr-Mo alloys | |
| Pickering et al. | Wedging action of solid corrosion product during stress corrosion of austenitic stainless steels | |
| HARWooD | The Influence of Stress on Corrosion (Part I of Two Parts) | |
| Dean et al. | Stress corrosion behavior of maraging nickel steels in natural environments | |
| Leu et al. | The mechanism of stress corrosion of austenitic stainless steels in hot aqueous chloride solutions | |
| Novak et al. | Comparison of fracture mechanics and nominal stress analyses in stress corrosion cracking | |
| Harris et al. | Effects of hydrogen on the engineering properties of MONEL nickel-copper alloy K-500 | |
| Vollmer | The behavior of steels in hydrogen sulfide environments | |
| Schussler et al. | Dealuminization of Aluminum Bronze | |
| Tsai et al. | Effects of shot peening on corrosion and stress corrosion cracking behaviors of sensitized alloy 600 in thiosulfate solution | |
| Upton | Corrosion Resistance in Sea Water Of Medium Strength Aluminum Bronzes | |
| Wang et al. | Effect of strain rate on hot ductility of a duplex stainless steel | |
| Hasegawa et al. | Corrosion behavior of ultrafine grained austenitic stainless steel | |
| Tiner et al. | Microprocesses in Stress Corrosion of Martensitic Steels | |
| Bradaskja et al. | Deformation behaviour and microstructural evolution during hot compression of AISI 904L | |
| Neumann et al. | Stress-Corrosion Cracking of Type 347 Stainless Steel And Other Alloys in High Temperature Water | |
| Costas | Effect of Phosphorus on the Embrittlement of Copper-Nickel Alloys by Mercury | |
| Casales et al. | Predicting susceptibility to intergranular stress corrosion cracking of Alloy 690 | |
| Mohr et al. | Stress corrosion cracking of ferritic stainless steels in chloride solutions | |
| Szklarska-Smialowska et al. | Comparative studies of SCC in two austenitic stainless steels and alloy 600 on exposure to lithiated water at 350 C | |
| Raghunatha Rao et al. | Effect of chemical composition and ferrite content on room temperature SCC behavior of austenitic weld metals | |
| Nakahara et al. | Stress corrosion cracking susceptibility of nickel-molybdenum alloys by slow strain rate and immersion testing | |
| Krishnan et al. | Room-Temperature Stress Corrosion Cracking Resistance of Post-Weld Heat-Treated Austenitic Weld Metals |