Cause analysis and mechanism study of cracks in drilling collars

Zhong et al., 2019

Document ID
2867542558287956458
Author
Zhong Z
Li Y
Liu Y
Bao L
Tian Z
Publication year
Publication venue
Engineering Failure Analysis

External Links

Snippet

A drill collar with material of 0Cr20Mn21Ni2N serviced in a coastal continental shelf oilfield, has cracked and leaked after a short period of working. Failure analysis of drill collar was performed by a series of experiments, including Chemical analysis, Fractographic analysis …
Continue reading at www.sciencedirect.com (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
    • C21D7/00—Modifying the physical properties of iron or steel by deformation
    • C21D7/02—Modifying the physical properties of iron or steel by deformation by cold working
    • C21D7/10—Modifying the physical properties of iron or steel by deformation by cold working of the whole cross-section, e.g. of concrete reinforcing bars
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor
    • C21D9/08—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
    • C21D9/00—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor
    • C21D9/50—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor for welded joints
    • C—CHEMISTRY; METALLURGY
    • C21—METALLURGY OF IRON
    • C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
    • C21D1/00—General methods or devices for heat treatments, e.g. annealing, hardening, quenching, tempering
    • C21D1/18—Hardening; Quenching with or without subsequent tempering

Similar Documents

Publication Publication Date Title
Schweitzer Metallic materials: physical, mechanical, and corrosion properties
Eliaz et al. Characteristics of hydrogen embrittlement, stress corrosion cracking and tempered martensite embrittlement in high-strength steels
Mansor et al. A review of the fatigue failure mechanism of metallic materials under a corroded environment
Gonzalez-Rodriguez et al. Effect of microstructure on the stress corrosion cracking of X-80 pipeline steel in diluted sodium bicarbonate solutions
Asahi et al. Role of microstructures on stress corrosion cracking of pipeline steels in carbonate-bicarbonate solution
reza Hajibagheri et al. An experimental investigation of the nature of longitudinal cracks in oil and gas transmission pipelines
Jemblie et al. Fracture toughness and hydrogen embrittlement susceptibility on the interface of clad steel pipes with and without a Ni-interlayer
Escobar et al. Failure analysis of submersible pump system collapse caused by assembly bolt crack propagation by stress corrosion cracking
Fu et al. Stress corrosion cracking behavior of super 13Cr tubing in phosphate packer fluid of high pressure high temperature gas well
Fan et al. The role of delta ferrite in hydrogen embrittlement fracture of 17-4 PH stainless steel
Laitinen et al. Chloride-induced stress corrosion cracking of powder metallurgy duplex stainless steels
El-Sayed Flow enhanced corrosion of water injection pipelines
Zhong et al. Cause analysis and mechanism study of cracks in drilling collars
Zhenqian et al. Failure analysis of vessel propeller bolts under fastening stress and cathode protection environment
Tavares et al. Investigation of the effect of low temperature aging on the mechanical properties and susceptibility to sulfide stress corrosion cracking of 22% Cr duplex stainless steel
Kagay et al. Slow strain rate and rising step load hydrogen embrittlement testing of UNS N07718
Popov et al. Effect of Hydrogenation on Hardness of Metallic Materials Used in Oil and Gas Industry
US20110223443A1 (en) Metallic components for use in corrosive environments and method of manufacturing
Filippov et al. Acoustic detection of stress-corrosion cracking of nitrogen austenitic steels
Hernandez-Sandoval et al. Localized corrosion in an electrical submergible pump (ESP)
Khalifeh Stress Corrosion Cracking
Lashgari et al. Failure analysis and microstructural restoration of a cast duplex stainless steel coupling in a desalination plant
Tavares et al. Intergranular corrosion at a modified surface layer in a supermartensitic stainless steel for chemical injection mandrel
Sharma et al. Experimental Investigation on Corrosion Behaviour of Heat-Treated API X70 Pipeline Steel
Jones et al. An evaluation of the corrosion and mechanical performance of interstitially surface-hardened stainless steel