Zhao et al., 2016 - Google Patents
Optimized Methods of Recording Pipeline Pressure Fluctuations for Pipeline Integrity AnalysisZhao et al., 2016
- Document ID
- 2685058285223166912
- Author
- Zhao J
- Chevil K
- Chen W
- Been J
- Keane S
- Publication year
- Publication venue
- International Pipeline Conference
External Links
Snippet
A crack growth and remaining life predictive software Pipe-OnLine has recently been developed to predict crack growth of pipeline steels in near neutral pH environments. Pressure fluctuations from Supervisory Control and Data Acquisition (SCADA) data are …
- 238000004458 analytical method 0 title description 6
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
- G01N2203/006—Crack, flaws, fracture or rupture
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Peng et al. | Overall reliability analysis on oil/gas pipeline under typical third-party actions based on fragility theory | |
| Beavers | 2013 Frank Newman Speller Award Lecture: Integrity management of natural gas and petroleum pipelines subject to stress corrosion cracking | |
| Zhao et al. | Crack growth modeling and life prediction of pipeline steels exposed to near-neutral pH environments: dissolution crack growth and occurrence of crack dormancy in stage I | |
| CN112307608B (en) | Austenitic stainless steel pipeline nonlinear fatigue damage life assessment processing method | |
| Zhao et al. | Crack growth modeling and life prediction of pipeline steels exposed to near-neutral pH environments: stage II crack growth and overall life prediction | |
| Yan et al. | Reliability-based crack threat assessment and management | |
| Brennan | Risk based maintenance for offshore wind structures | |
| Zhao et al. | Effect of pressure sampling methods on pipeline integrity analysis | |
| Zhao et al. | Development and validation of load-interaction based models for crack growth prediction | |
| CN112504863B (en) | Method for quantitatively evaluating service life of material | |
| Zhao et al. | Optimized Methods of Recording Pipeline Pressure Fluctuations for Pipeline Integrity Analysis | |
| Nahal et al. | Failure probability assessment for pipelines under the corrosion effect | |
| Dinovitzer et al. | Geometric dent characterization | |
| Zheng et al. | Stress corrosion cracking in pipelines | |
| Moan | Recent research and development relating to platform requalification | |
| Chen et al. | Update of understanding of near-neutral pH SCC crack growth mechanisms and development of pipe-online software for pipeline integrity management | |
| Ahmed et al. | Weather-Related Combined Effect on Failure Propagation and Maintenance Procedures towards Sustainable Gas Pipeline Infrastructure | |
| Newton et al. | Use of a geohazard management program to reduce pipeline failure rates | |
| Unwin et al. | Physics-Based Stress Corrosion Cracking Component Reliability Model cast in an R7-Compatible Cumulative Damage Framework | |
| Chen et al. | Threshold Geometrical Dimensions of Stage II Cracks Versus Required Resolution of Crack-Detection Techniques | |
| Lamborn et al. | Near Neutral pH Stress Corrosion Crack Growth Model Evaluation: PipeOnline™ | |
| Jacobson | Pipeline Stress Corrosion Cracking: Detection and Control | |
| Yadav et al. | Dynamic PRA with component aging and degradation modeled utilizing plant risk monitoring data | |
| Xu et al. | Differences in Near-Neutral pH Crack Growth Behavior Between Oil Pipelines and Gas Pipelines and Corresponding Crack Growth Mitigation Strategies | |
| Zheng | Stress corrosion cracking of oil and gas pipelines in near neutral pH environment: review of recent research |