Surface analysis and corrosion resistance of new nickel base thin film alloysPopescu et al., 2014
- Document ID
- 16295126468328344199
- Author
- Popescu A
- Neacşu E
- Yanushkevich K
- Constantin V
- Publication year
- Publication venue
- Surface and Interface Analysis
External Links
Snippet
Electroless Zn–Ni–P thin films were deposited on low carbon steel from an alkaline non‐ cyanide aqueous electrolyte. The newly developed ternary alloys structure and microstructure investigations were carried out via X‐ray diffraction and SEM. Chemical …
- PXHVJJICTQNCMI-UHFFFAOYSA-N nickel data:image/svg+xml;base64,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 data:image/svg+xml;base64,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 [Ni] 0 title abstract description 82
Classifications
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/31—Coating with metals
-
- C—CHEMISTRY; METALLURGY
- C23—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; CHEMICAL SURFACE TREATMENT; DIFFUSION TREATMENT OF METALLIC MATERIAL; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL; INHIBITING CORROSION OF METALLIC MATERIAL OR INCRUSTATION IN GENERAL
- C23C—COATING METALLIC MATERIAL; COATING MATERIAL WITH METALLIC MATERIAL; SURFACE TREATMENT OF METALLIC MATERIAL BY DIFFUSION INTO THE SURFACE, BY CHEMICAL CONVERSION OR SUBSTITUTION; COATING BY VACUUM EVAPORATION, BY SPUTTERING, BY ION IMPLANTATION OR BY CHEMICAL VAPOUR DEPOSITION, IN GENERAL
- C23C18/00—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating
- C23C18/16—Chemical coating by decomposition of either liquid compounds or solutions of the coating forming compounds, without leaving reaction products of surface material in the coating; Contact plating by reduction or substitution, e.g. electroless plating
- C23C18/1601—Process or apparatus
- C23C18/1633—Process of electroless plating
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Oulmas et al. | Comparative study of Cu–Zn coatings electrodeposited from sulphate and chloride baths | |
| Blejan et al. | Corrosion behavior of Zn Ni Al2O3 nanocomposite coatings obtained by electrodeposition from alkaline electrolytes | |
| Abbott et al. | Ionic liquid analogues formed from hydrated metal salts | |
| Narayanan et al. | Deposition of electroless Ni–P graded coatings and evaluation of their corrosion resistance | |
| Mohammadloo et al. | The effect of solution temperature and pH on corrosion performance and morphology of nanoceramic‐based conversion thin film | |
| Veeraraghavan et al. | Corrosion protection of steel using nonanomalous Ni-Zn-P coatings | |
| Fashu et al. | Electrodeposition and characterization of Zn–Sn alloy coatings from a deep eutectic solvent based on choline chloride for corrosion protection | |
| Hasannejad et al. | Synthesis and properties of high corrosion resistant Ni–cerium oxide nano‐composite coating | |
| Shi et al. | Effects of cobalt content on mechanical and corrosion properties of electroless Ni‐Co‐P/TiN nanocomposite coatings | |
| Niu et al. | Surface characterization and corrosion resistance of fluoferrite conversion coating on carbon steel | |
| Faraji et al. | Corrosion resistance of electroless Cu–P and Cu–P–SiC composite coatings in 3.5% NaCl | |
| Baldessin et al. | The influence of Ni and Co concentration in the electroplating bath on Ni‐Co‐W alloys properties | |
| Hammami et al. | Effect of diethanolamine and triethanolamine on the properties of electroplated Zn–Ni alloy coatings from acid bath | |
| Pham et al. | Role of Al and Mg alloying elements on corrosion behavior of zinc alloy‐coated steel substrates in 0.1 M NaCl solution | |
| Omar et al. | The effect of sodium citrate as a complex agent on the corrosion properties of the electroless Ni-P coating | |
| Beheshti et al. | Influence of deposition temperature on the corrosion resistance of electrodeposited zinc‐nickel alloy coatings: Einfluss der Abscheidetemperatur auf die Korrosionsbeständigkeit von galvanisch aufgebrachten Zink‐Nickel‐Beschichtungen | |
| Bera et al. | Characterization and microhardness of Co− W coatings electrodeposited at different pH using gluconate bath: A comparative study | |
| Lei et al. | Surface characterization of growth process for cerium conversion coating on magnesium alloy and its anticorrosion mechanism | |
| Pereira et al. | Influence of amines on the electrodeposition of Zn-Ni alloy from a eutectic-type ionic liquid | |
| Liu et al. | Crystallisation and performance characteristics of high‐temperature annealed electroless Ni‐W‐P coatings | |
| Kordijazi | Optimization of Ni–P–Zn electroless bath and investigation of corrosion resistance of as-plated coatings | |
| Kathavate et al. | Corrosion protection performance of nano-TiO2-containing phosphate coatings obtained by anodic electrochemical treatment | |
| Popescu et al. | Surface analysis and corrosion resistance of new nickel base thin film alloys | |
| Ashassi-Sorkhabi et al. | Electroless Deposition of Ni‐Cu‐P Coatings Containing Nano‐Al2O3 Particles and Study of Its Corrosion Protective Behaviour in 0.5 M H2SO4 | |
| Zhang et al. | Efficiently Improved Corrosion Resistance of Electrodeposition Ni–Cu Coatings via Site‐Blocking Effect of Ce |