Emami, 2017 - Google Patents
Development of Probabilistic Models for Long Term Reliability of Sandwich Composites in Saline Freeze/Thaw Environment for Civil Engineering ApplicationsEmami, 2017
View PDF- Document ID
- 15904778840496214894
- Author
- Emami S
- Publication year
External Links
Snippet
Structural engineers commonly use balsa wood and PVC foam as core materials for sandwich composite structures. The long-term reliability and damage mechanism of these composite sandwich structures under severe environmental conditions are still unclear …
- 239000002131 composite material 0 title abstract description 183
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Micelli et al. | Durability of FRP rods for concrete structures | |
| Zhou et al. | Structural behavior of GFRP reinforced concrete columns under the influence of chloride at casting and service stages | |
| Grammatikos et al. | Thermal cycling effects on the durability of a pultruded GFRP material for off-shore civil engineering structures | |
| Shi et al. | Damage characteristics analysis of GFRP-Balsa sandwich beams under Four-point fatigue bending | |
| Fiore et al. | Effect of external basalt layers on durability behaviour of flax reinforced composites | |
| Hota et al. | Degradation mechanism of glass fiber/vinylester-based composite materials under accelerated and natural aging | |
| Wu et al. | Strengthening of concrete structures using fiber reinforced polymers (FRP): design, construction and practical applications | |
| Zhou et al. | Effect of different environments on bond strength of glass fiber-reinforced polymer and steel reinforcing bars | |
| del Rey Castillo et al. | Experimental testing and design model for bent FRP anchors exhibiting fiber rupture failure mode | |
| Saadatmanesh et al. | Environmental effects on mechanical properties of wet lay-up fiber-reinforced polymer | |
| Montaigu et al. | Laboratory characterization and evaluation of durability performance of new polyester and vinylester E-glass GFRP dowels for jointed concrete pavement | |
| Bastani et al. | Rehabilitation of thin walled steel beams using CFRP fabric | |
| Wu et al. | Durability simulation of FRP bridge decks subject to weathering | |
| Ding et al. | Hygroscopic ageing of nonstandard size sandwich composites with vinylester-based composite faces and PVC foam core | |
| Manalo et al. | Effect of simulated hygrothermal environment on the flexural and interlaminar shear strength of particulate-filled epoxy-coated GFRP composites | |
| Abdelkarim et al. | Hollow-core FRP-concrete-steel bridge columns under extreme loading. | |
| Kharwar et al. | Retrofitting techniques of damaged concrete structure for environment concern: A review | |
| Emami | Development of Probabilistic Models for Long Term Reliability of Sandwich Composites in Saline Freeze/Thaw Environment for Civil Engineering Applications | |
| Gonilha et al. | Durability of GFRP-concrete adhesively bonded connections: Experimental and numerical studies | |
| Holly et al. | Bond of GFRP reinforcement with concrete | |
| Heshmati | Hygrothermal durability of adhesively bonded FRP/steel joints | |
| Park | Long-term performance of GFRP reinforced concrete beams and bars subjected to aggressive environments | |
| Johnson | Investigation of glass fibre reinforced polymer reinforcing bars as internal reinforcement for concrete structures | |
| Que et al. | Pull-out tests for GFRP/BFRP/steel bars used as nailing for coal-bearing soil slopes in humid regions | |
| Mousa et al. | Performance of composite structural insulated panels after exposure to floodwater |