Durability and service life of elements made with SHCC under imposed strainWang et al., 2014
View PDF- Document ID
- 15733382257614245129
- Author
- Wang P
- Wittmann F
- Zhang P
- Lehmann E
- Zhao T
- Publication year
- Publication venue
- SHCC3-3rd Interna-tional RILEM Conference on Strain Hardening Cementitious Composites
External Links
Snippet
Huge strain capacity of SHCC under tensile stress can be reached by multiple crack formation, while the cracks remain bridged by fibers. Under protective conditions the full strain capacity can be used in practice. In this contribution it is shown that even at …
- 102000002013 Transforming Protein 3 Src Homology 2 Domain-Containing 0 title abstract 4
Classifications
-
- C—CHEMISTRY; METALLURGY
- C04—CEMENTS; CONCRETE; ARTIFICIAL STONE; CERAMICS; REFRACTORIES
- C04B—LIME, MAGNESIA; SLAG; CEMENTS; COMPOSITIONS THEREOF, e.g. MORTARS, CONCRETE OR LIKE BUILDING MATERIALS; ARTIFICIAL STONE; CERAMICS; REFRACTORIES; TREATMENT OF NATURAL STONE
- C04B28/00—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements
- C04B28/02—Compositions of mortars, concrete or artificial stone, containing inorganic binders or the reaction product of an inorganic and an organic binder, e.g. polycarboxylate cements containing hydraulic cements other than calcium sulfates
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N33/00—Investigating or analysing materials by specific methods not covered by the preceding groups
- G01N33/38—Investigating or analysing materials by specific methods not covered by the preceding groups concrete; ceramics; glass; bricks
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Zhang et al. | Investigating mechanical properties and self-healing behavior of micro-cracked ECC with different volume of fly ash | |
| Franzoni et al. | Effects of rising damp and salt crystallization cycles in FRCM-masonry interfacial debonding: Towards an accelerated laboratory test method | |
| US7572501B2 (en) | Engineered self healing cementitious composites | |
| Zhang et al. | Self-healing behaviour of multiple microcracks of strain hardening cementitious composites (SHCC) | |
| Sicat et al. | Change of the coefficient of thermal expansion of mortar due to damage by freeze thaw cycles | |
| Herbert et al. | Self-healing of engineered cementitious composites in the natural environment | |
| Lieboldt et al. | Capillary transport of water through textile-reinforced concrete applied in repairing and/or strengthening cracked RC structures | |
| Helson et al. | Durability of soil mix material subjected to wetting/drying cycles and external sulfate attacks | |
| Ma et al. | Influence of freeze-thaw cycles on properties of integral water repellent concrete | |
| Kim et al. | Effect of transport properties of fiber types on steel reinforcement corrosion | |
| Zhang et al. | Water penetration into micro-cracks in reinforced concrete | |
| Wang | Experimental study on water absorption by concrete damaged by uniaxial loading | |
| Fenyvesi | Affect of lightweight aggregate to early age cracking in concrete | |
| Wang et al. | Durability and service life of elements made with SHCC under imposed strain | |
| Nishiwaki et al. | Experimental study on self-healing effect of FRCC with PVA fibers and additives | |
| Wang et al. | Observation of water penetration into cracked and water repellent SHCC after imposed strain by means of neutron radiography | |
| Sierra-Beltran et al. | Performance of SHCC with bacteria for concrete patch repair | |
| Martinola et al. | Modified ECC by means of internal impregnation | |
| Wittmann et al. | Influence of an imposed tensile stress and subsequent self-healing on capillary absorption and chloride penetration into HPFRCC | |
| Gharachorlou et al. | Durability of concrete cylinder specimens strengthened with FRP laminates under penetration of chloride ions | |
| Martinola et al. | Modified ECC applied as an effective chloride barrier | |
| Nováková et al. | Behaviour of basalt fibre reinforced concrete exposed to elevated temperatures | |
| Peng et al. | Improving durability of SHCC under imposed strain by water repellent treatment | |
| Wittmann et al. | Water penetration into strain hardening cementitious composites before and after water-repellent surface impregnation | |
| Jiang et al. | Influence of mechanically induced damage on durability and service life of reinforced concrete structures |