Kuwamura et al., 1987 - Google Patents
Inspection and repair of fatigue cracks in crane runway girdersKuwamura et al., 1987
- Document ID
- 15415258383825378350
- Author
- Kuwamura H
- Hanzawa M
- Publication year
- Publication venue
- Journal of structural engineering
External Links
Snippet
A method is presented for the inspection and repair of fatigue cracks that occur in the bottom tension flanges of crane runway girders. The date of first inspection and the interval of inspection are determined from fatigue crack initiation and propagation tests, respectively …
- 238000007689 inspection 0 title abstract description 37
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Choi et al. | Stress characteristics and fatigue crack behaviour of the longitudinal rib-to-cross beam joints in an orthotropic steel deck | |
| Ahola et al. | Fatigue performance of the welded details of an old, demolished steel railway bridge | |
| Skriko et al. | Fatigue strength of longitudinal load-carrying welds in beams made of ultra-high-strength steel | |
| Kuwamura et al. | Inspection and repair of fatigue cracks in crane runway girders | |
| Frýba et al. | Fatigue properties of orthotropic decks on railway bridges | |
| Fisher | Evolution of fatigue-resistant steel bridges | |
| Tajima et al. | Fatigue strengths of truss made of high strength steels | |
| Mashiri et al. | Fatigue tests and design of thin cold-formed square hollow section-to-plate T connections under cyclic in-plane bending | |
| Tagawa et al. | Experimental proof of reverse bending technique for modifying weld residual stress in weld CTOD specimen and comparison of effect with other techniques | |
| Wardenier et al. | Fatigue behaviour of a welded I-section under a line load in compression | |
| Grimm et al. | The influence of edge treatment on fatigue behavior of thermal cut edges | |
| Pisarski et al. | Significance of splits and pop-ins observed during fracture toughness testing of line pipe steel | |
| MIKI et al. | Fatigue of large-scale welded girders under simulated highway loadings | |
| Stallmeyer et al. | Behavior of Welded Build-Up Beams under Repeated Loads | |
| Catherine et al. | Cleavage toughness of heterogeneous materials and application to welded joints | |
| Bussiba et al. | Fatigue crack growth rates in six pipeline steels | |
| Yamasaki et al. | Fatigue life of welded and bolted repair parts | |
| Barsom¹ | Fatigue considerations for steel bridges | |
| Nussbaumer et al. | On the practical use of weld improvement methods | |
| Skoglund | Fatigue life estimation based on LEFM and the study of initial parameters | |
| Takamori | Improving fatigue strength of welded joints | |
| MORI et al. | Fatigue crack propagation and strength of web-gusset welded joints under varied principal stress direction | |
| Nazarova et al. | On the problem of getting a correct crack shape in fracture toughness specimens of low-carbon steel | |
| Kober et al. | The effect of welding discontinuities on the variability of fatigue life | |
| Ono et al. | Structural stress fatigue assessments of butt-welded joints with thickness step |