Grachev et al., 2021 - Google Patents
Short-time mechanical properties of EP823-SH ferrite-martensite steel after high-dose neutron irradiationGrachev et al., 2021
- Document ID
- 15265516999920968075
- Author
- Grachev A
- Zabud’ko L
- Leont’eva-Smirnova M
- Naumenko I
- Kryukov F
- Chertopyatov E
- Marinenko E
- Porollo S
- Publication year
- Publication venue
- Atomic Energy
External Links
Snippet
Irradiation of experimental fuel assemblies with uranium-plutonium nitride fuel and shells made of ferritic-martensitic steel EP823-Sh is conducted in order to ensure normal operation of BREST-OD-300 fuel rods in the BOR-60 and BN-600 reactors. This article presents the …
- 229910000831 Steel 0 title abstract description 45
Classifications
-
- G—PHYSICS
- G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
- G21C—NUCLEAR REACTORS
- G21C3/00—Reactor fuel elements and their assemblies; Selection of substances for use as reactor fuel elements
- G21C3/02—Fuel elements
- G21C3/04—Constructional details
- G21C3/06—Casings; Jackets
- G21C3/07—Casings; Jackets characterised by their material, e.g. alloys
-
- Y—GENERAL TAGGING OF NEW TECHNOLOGICAL DEVELOPMENTS; GENERAL TAGGING OF CROSS-SECTIONAL TECHNOLOGIES SPANNING OVER SEVERAL SECTIONS OF THE IPC; TECHNICAL SUBJECTS COVERED BY FORMER USPC CROSS-REFERENCE ART COLLECTIONS [XRACs] AND DIGESTS
- Y02—TECHNOLOGIES OR APPLICATIONS FOR MITIGATION OR ADAPTATION AGAINST CLIMATE CHANGE
- Y02E—REDUCTION OF GREENHOUSE GASES [GHG] EMISSION, RELATED TO ENERGY GENERATION, TRANSMISSION OR DISTRIBUTION
- Y02E30/00—Energy generation of nuclear origin
- Y02E30/30—Nuclear fission reactors
- Y02E30/40—Other aspects relating to nuclear fission
-
- G—PHYSICS
- G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
- G21C—NUCLEAR REACTORS
- G21C17/00—Monitoring; Testing ; Maintaining
- G21C17/02—Devices or arrangements for monitoring coolant or moderator
- G21C17/022—Devices or arrangements for monitoring coolant or moderator for monitoring liquid coolants or moderators
-
- G—PHYSICS
- G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
- G21C—NUCLEAR REACTORS
- G21C3/00—Reactor fuel elements and their assemblies; Selection of substances for use as reactor fuel elements
- G21C3/42—Selection of substances for use as reactor fuel
-
- G—PHYSICS
- G21—NUCLEAR PHYSICS; NUCLEAR ENGINEERING
- G21Y—INDEXING SCHEME RELATING TO NUCLEAR REACTORS, POWER PLANTS AND EXPLOSIVES, TO PROTECTION AGAINST RADIATION, TO THE TREATMENT OF RADIOACTIVELY CONTAMINATED MATERIAL, TO APPLICATIONS OF RADIOACTIVE SOURCES AND TO THE UTILISATION OF COSMIC RADIATION
- G21Y2002/00—PROBLEM
- G21Y2002/104—Inadequate performance, deformation, cracks, rupture
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Aomi et al. | Evaluation of hydride reorientation behavior and mechanical properties for high-burnup fuel-cladding tubes in interim dry storage | |
| Tan et al. | Strain-rate dependent fatigue behavior of 316LN stainless steel in high-temperature water | |
| Samal et al. | Investigation of failure behavior of two different types of Zircaloy clad tubes used as nuclear reactor fuel pins | |
| Yang | Anisotropic effects of radiation-induced hardening in nuclear structural materials: A review | |
| Grachev et al. | Short-time mechanical properties of EP823-SH ferrite-martensite steel after high-dose neutron irradiation | |
| Cinbiz et al. | Report on Design and Failure Limits of SiC/SiC and FeCrAl ATF Cladding Concepts under RIA | |
| Grachev et al. | Post-Reactor Studies of Fuel Rods with Uranium-Plutonium Nitride Fuel with Gas and Liquid-Metal Sublayer | |
| Asayama et al. | Evaluation procedures for irradiation effects and sodium environmental effects for the structural design of Japanese fast breeder reactors | |
| Rostova et al. | Cavitation wear of Eurofer 97, Cr18Ni10Ti and 42HNM alloys | |
| Hojna et al. | Effect of the surface grinding on the environmentally assisted crack initiation of 316 L steel in simulated pressurized water reactor water | |
| Chen | Experimental evaluation and modeling of fatigue of a 316L austenitic stainless steel in high-temperature water and air environments | |
| Neustroev et al. | Investigation of microstructure and mechanical properties of 18Cr-10ni-ti steel irradiated in the core of VVER-1000 reactor | |
| Margolin et al. | Mechanisms of Stress Corrosion Cracking of Irradiated Austenitic Chromium–Nickel Steels Used for WWER and PWR Vessel Internals | |
| Frolov et al. | Comparison of Ring Tension and Compression Test Results for Materials with Low Ductility | |
| Sarkar et al. | Effect of flattening on mechanical properties of Zr-2.5 Nb pressure tube material | |
| Jaramillo et al. | Tensile hoop behavior of irradiated Zircaloy-4 nuclear fuel cladding | |
| Walters et al. | Irradiation issues and material selection for Canadian SCWR components | |
| Cinbiz et al. | The mechanical response evaluation of advanced claddings during proposed reactivity initiated accident conditions | |
| Cho et al. | Susceptibility of Stress Corrosion Crack Initiation of Type 304 SS in Simulated Primary Water Environment of PWR | |
| Glushkova et al. | Examination of ChS-68 Steel Used as a BN-600 Reactor Cladding Material | |
| KOKHONOV et al. | STUDY OF STRESS CORROSION CRACKING SUSCEPTIBILITY OF IRRADIATED FERRITE-MARTENSITIC STAINLESS STEEL 07Kh12NMFB IN SUPERCRITICAL WATER. Part 1. Autoclave testing | |
| Field et al. | Advancements in FeCrAl alloys for enhanced accident tolerant fuel cladding for light water reactors | |
| Cinbiz et al. | Transient Mechanical Test Development for Accident Tolerant Cladding Candidates to Simulate PCMI-like Conditions | |
| Nikulin et al. | Crack resistance of zirconium cladding pipes after high-temperature oxidation | |
| Fedotov et al. | Influence of pre-hydriding on embrittlement of E110 alloy under LOCA conditions |