Influence of curvature and load direction on the air-blast response of singly curved glass fiber reinforced epoxy laminate and sandwich panelsLangdon et al., 2017
- Document ID
- 13424566275967075084
- Author
- Langdon G
- von Klemperer C
- Sinclair G
- Ghoor I
- Publication year
- Publication venue
- Explosion Blast Response of Composites
External Links
Snippet
This chapter reports the results of an experimental investigation into the influence of curvature, construction type, and load direction on the air-blast response of singly curved glass fiber reinforced epoxy laminate and sandwich panels. Equivalent mass glass fiber …
- 230000004044 response 0 title abstract description 33
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Sun et al. | On the structural parameters of honeycomb-core sandwich panels against low-velocity impact | |
| Zhang et al. | Low-velocity impact response and compression after impact behavior of tubular composite sandwich structures | |
| Zhou et al. | The low velocity impact response of foam-based sandwich panels | |
| Gholizadeh | A review of impact behaviour in composite materials | |
| Yaghoubi et al. | Thickness influence on ballistic impact behaviors of GLARE 5 fiber-metal laminated beams: Experimental and numerical studies | |
| Langdon et al. | The air-blast response of sandwich panels with composite face sheets and polymer foam cores: Experiments and predictions | |
| López-Puente et al. | The effect of low temperatures on the intermediate and high velocity impact response of CFRPs | |
| Hörold et al. | Fire stability of glass-fibre sandwich panels: The influence of core materials and flame retardants | |
| Naresh et al. | Single and multi-layer core designs for Pseudo-Ductile failure in honeycomb sandwich structures | |
| Kaboglu et al. | Effects of the core density on the quasi-static flexural and ballistic performance of fibre-composite skin/foam-core sandwich structures | |
| Li et al. | Dynamic failure of basalt/epoxy laminates under blast—Experimental observation | |
| Kelly et al. | Sandwich panel cores for blast applications: materials and graded density | |
| Dolati et al. | Experimental investigation into glass fiber/epoxy composite laminates subjected to single and repeated high-velocity impacts of ice | |
| Gomez et al. | Experimental analysis of the impact behaviour of sandwich panels with sustainable cores | |
| Zaharia et al. | Experimental study of static and fatigue behavior of CFRP-balsa sandwiches under three-point flexural loading | |
| Ao et al. | Impact resistance and damage mechanism of polyurea coated CFRP laminates under quasi-static indentation and low velocity impact | |
| Zhang et al. | Artificial hail ice impact damage of laminated composite T-joint with stitching reinforcement | |
| Celik et al. | The impact response of a Nomex® honeycomb core/E-glass/epoxy composite sandwich structure to increasing velocities: Experimental and numerical analysis | |
| Jean-St-Laurent et al. | Compression after impact behavior of carbon/epoxy composite sandwich panels with Nomex honeycomb core subjected to low velocity impacts at extreme cold temperatures | |
| Zhao et al. | Experimental and numerical investigations of damage and ballistic limit velocity of CFRP laminates subject to harpoon impact | |
| Langdon et al. | Blast response of sandwich structures: The influence of curvature | |
| Karthick et al. | Experimental and numerical investigation on GFRP-aramid honeycomb sandwich panel under bird impact: Estimation of penetration velocity | |
| Langdon et al. | Influence of curvature and load direction on the air-blast response of singly curved glass fiber reinforced epoxy laminate and sandwich panels | |
| Yu et al. | Perforation of aluminium alloy-CFRP bilayer plates under quasi-static and impact loading | |
| Alavi Nia et al. | An empirical study on ballistic resistance of sandwich targets with aluminum facesheets and composite core |