Yildirim et al., 2021 - Google Patents
Performance Properties of Particleboard Panels Modified with Nanocellulose/Boric Acid.Yildirim et al., 2021
- Document ID
- 12730149256921645333
- Author
- Yildirim M
- Candan Z
- Publication year
- Publication venue
- BioResources
External Links
Snippet
The physical and mechanical properties of particleboard panels were evaluated relative to various loading levels of nanocellulose (NC) and boric acid (BA) in the urea-formaldehyde (UF) resin used for panel production. The results showed that NC and BA reinforcement …
- 229920001046 Nanocellulose 0 title abstract description 140
Classifications
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L97/00—Compositions of lignin-containing materials
- C08L97/02—Lignocellulosic material, e.g. wood, straw or bagasse
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L61/00—Compositions of condensation polymers of aldehydes or ketones; Compositions of derivatives of such polymers
- C08L61/20—Condensation polymers of aldehydes or ketones with only compounds containing hydrogen attached to nitrogen
- C08L61/22—Condensation polymers of aldehydes or ketones with only compounds containing hydrogen attached to nitrogen of aldehydes with acyclic or carbocyclic compounds
- C08L61/24—Condensation polymers of aldehydes or ketones with only compounds containing hydrogen attached to nitrogen of aldehydes with acyclic or carbocyclic compounds with urea or thiourea
-
- C—CHEMISTRY; METALLURGY
- C08—ORGANIC MACROMOLECULAR COMPOUNDS; THEIR PREPARATION OR CHEMICAL WORKING-UP; COMPOSITIONS BASED THEREON
- C08L—COMPOSITIONS OF MACROMOLECULAR COMPOUNDS
- C08L97/00—Compositions of lignin-containing materials
- C08L97/005—Lignin
-
- D—TEXTILES; PAPER
- D21—PAPER-MAKING; PRODUCTION OF CELLULOSE
- D21H—PULP COMPOSITIONS; PREPARATION THEREOF NOT COVERED BY SUBCLASSES D21C OR D21D; IMPREGNATING OR COATING OF PAPER; TREATMENT OF FINISHED PAPER NOT COVERED BY CLASS B31 OR SUBCLASS D21G; PAPER NOT OTHERWISE PROVIDED FOR
- D21H17/00—Non-fibrous material added to the pulp, characterised by its constitution; Paper-impregnating material characterised by its constitution
- D21H17/20—Macromolecular organic compounds
- D21H17/33—Synthetic macromolecular compounds
- D21H17/46—Synthetic macromolecular compounds obtained otherwise than by reactions only involving carbon-to-carbon unsaturated bonds
- D21H17/47—Condensation polymers of aldehydes or ketones
- D21H17/49—Condensation polymers of aldehydes or ketones with compounds containing hydrogen bound to nitrogen
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Yildirim et al. | Performance Properties of Particleboard Panels Modified with Nanocellulose/Boric Acid. | |
| Vineeth et al. | Nanocellulose applications in wood adhesives | |
| US8377564B2 (en) | Cellulosic composite | |
| Candan et al. | Physical and mechanical properties of nanoreinforced particleboard composites | |
| US8372900B2 (en) | Cellulosic composite with binder comprising salt of inorganic acid | |
| Kawalerczyk et al. | The effect of nanocellulose addition to phenol-formaldehyde adhesive in water-resistant plywood manufacturing | |
| Candan et al. | Nano-engineered plywood panels: Performance properties | |
| Lengowski et al. | Nanocellulose-reinforced adhesives for wood-based panels | |
| Kwon et al. | Tensile shear strength of wood bonded with urea–formaldehyde with different amounts of microfibrillated cellulose | |
| Jiang et al. | Effect of cellulose nanofibrils on the bond strength of polyvinyl acetate and starch adhesives for wood | |
| Bekhta et al. | Effect of pretreatment of raw material on properties of particleboard panels made from wheat straw | |
| Moradpour et al. | Laminated strand lumber (LSL) reinforced by GFRP; mechanical and physical properties | |
| Yildirim et al. | Chemical performance analysis of nanocellulose/boron-compound-reinforced hybrid UF resin | |
| Lengowski et al. | Nanocellulose-reinforced phenol-formaldehyde resin for plywood panel production | |
| Sarı et al. | Effects of chemical composition of wood and resin type on properties of particleboard | |
| Kord et al. | Characterization and utilization of reed stem as a lignocellulosic resource for particleboard production | |
| Ümit Yalçın | Improved Properties of Particleboards Produced with Urea Formaldehyde Adhesive Containing Nanofibrillated Cellulose and Titanium Dioxide. | |
| Rahman et al. | Effects of the resin content and particle size on the properties of particleboard made of neolamarckia and leucaena particles | |
| Nader et al. | Lignocellulosic micro and nanofibrillated cellulose produced by steam explosion for wood adhesive formulations | |
| CN105291242A (en) | Environment-friendly bamboo-wood composite shaving board with low hygroscopic expansion rate | |
| Eshraghi et al. | Waste paperboard in composition panels | |
| Kawalerczyk et al. | The effect of a phenol-formaldehyde adhesive reinforcement with nanocellulose on the pressing parameters of plywood | |
| Akbulut et al. | Some advantages of three-layer medium-density fibreboard as compared to the traditional single-layer one | |
| Yotov et al. | Lignosulphonate and waste technical hydrolysis lignin as adhesives for eco-friendly fiberboard | |
| Dasiewicz et al. | Characteristics of high-density fibreboard produced with the use of rice starch as a binder |