Investigation of long-term exposure effects under stress of two titanium structural alloysMartin, 1966
- Document ID
- 12147378006252178506
- Author
- Martin G
- Publication year
- Publication venue
- Stress-Corrosion Cracking of Titanium
External Links
Snippet
Notched and unnotched sheet specimens of two titanium alloys, Ti-6Al-4V and Ti-8Al-lMo-lV, were exposed at 650 F and stressed by a cantilever arrangement to 25 to 30 per cent of their yield stress. Specimens were tested for periods up to 20,000 hr as received, coated with salt …
- 229910045601 alloy 0 title abstract description 59
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Jiang et al. | Effects of oxidation and inter-diffusion on the fracture mechanisms of Cr-coated Zry-4 alloys: An in situ three-point bending study | |
| Lowrie et al. | Composite coatings of CoCrAlY plus platinum | |
| Ranjith Kumar et al. | A critical appraisal of laser peening and its impact on hydrogen embrittlement of titanium alloys | |
| Bataev et al. | Structure and mechanical properties of a two-layered material produced by the E-beam surfacing of Ta and Nb on the titanium base after multiple rolling | |
| Augustin et al. | Intergranular corrosion of 2024 alloy in chloride solutions | |
| Roy et al. | Effect of Al concentration on Fe-17Cr alloy during steam oxidation at 400° C | |
| Zhang et al. | Microstructures and wear resistance of Zr-4 and N36 alloys subjected to pulsed laser surface remelting | |
| Zhu et al. | Significant improvement in hot corrosion resistance of inconel 690 by laser shock peening | |
| Martin | Investigation of long-term exposure effects under stress of two titanium structural alloys | |
| Lindemann et al. | Influence of mechanical surface treatments on the HCF performance of the Ni-superalloy Udimet 720 LI | |
| Petersen | Hot-salt stress-corrosion of titanium: a review of the problem and methods for improving the resistance of titanium | |
| Schuster et al. | Characterisation of Zircaloy corrosion fatigue phenomena in an iodine environment: Part 1: crack growth | |
| Sinigaglia et al. | Hot-salt-stress-corrosion cracking of titanium alloys | |
| JP2000097843A (en) | Evaluation method for corrosion of zirconium-based metals and zirconium-based alloys | |
| Piper et al. | The Relative Stress-Corrosion Susceptibility of Titanium Alloys in the Presence of Hot Salt | |
| Law et al. | Creep-rupture in powder metallurgical nickel-base superalloys at intermediate temperatures | |
| Turley et al. | Elevated-temperature static and dynamic sea-salt stress cracking of titanium alloys | |
| Rideout | Stress Corrosion Cracking of Type 304 Stainless Steel in High-Purity Heavy Water | |
| Baiyao et al. | Mechanical behavior associated with metallurgical aspects of friction stir welded Al–Li alloy exposed to exfoliation corrosion test | |
| Webb et al. | Stress corrosion cracking behavior of Alloy 600 in high temperature water | |
| Goods | The effect of a molten nitrate salt environment on the mechanical properties of INCOLOY alloy 800 | |
| JPH01159362A (en) | Heat treatment of heat exchanger tube made of ni alloy | |
| Russo | Analysis of fractures utilizing the SEM | |
| Ghorani et al. | Effect of Sensitization on Hydrogen Embrittlement in a 5083 Aluminum Alloy | |
| Encrenaz et al. | Hot salt stress corrosion resistance of Ti 6246 alloy |