Meniscus thermal analysis for detecting defects in continuous cast slabsLai, 2000
View PDF- Document ID
- 11493035112494635668
- Author
- Lai W
- Publication year
External Links
Snippet
Transverse corner cracking was found to be a predominant problem in continuously cast slabs with peritectic carbon contents (0.09-0.16 wt% C). This thesis is based on an industrial plant trial carried out at Dofasco's No. l straight mould continuous caster for low carbon (0.04 …
- 230000005499 meniscus 0 title abstract description 88
Classifications
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/06—Continuous casting of metals, i.e. casting in indefinite lengths into moulds with travelling walls, e.g. with rolls, plates, belts, caterpillars
- B22D11/0637—Accessories therefor
- B22D11/0648—Casting surfaces
- B22D11/0651—Casting wheels
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/04—Continuous casting of metals, i.e. casting in indefinite lengths into open-ended moulds
- B22D11/059—Mould materials or platings
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/16—Controlling or regulating processes or operations
- B22D11/18—Controlling or regulating processes or operations for pouring
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/12—Accessories for subsequent treating or working cast stock in situ
- B22D11/128—Accessories for subsequent treating or working cast stock in situ for removing
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/04—Continuous casting of metals, i.e. casting in indefinite lengths into open-ended moulds
- B22D11/041—Continuous casting of metals, i.e. casting in indefinite lengths into open-ended moulds for vertical casting
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/04—Continuous casting of metals, i.e. casting in indefinite lengths into open-ended moulds
- B22D11/0401—Moulds provided with a feed head
-
- B—PERFORMING OPERATIONS; TRANSPORTING
- B22—CASTING; POWDER METALLURGY
- B22D—CASTING OF METALS; CASTING OF OTHER SUBSTANCES BY THE SAME PROCESSES OR DEVICES
- B22D11/00—Continuous casting of metals, i.e. casting in indefinite lengths
- B22D11/14—Plants for continuous casting
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Mahapatra et al. | Mold behavior and its influence on quality in the continuous casting of steel slabs: Part i. Industrial trials, mold temperature measurements, and mathematical modeling | |
| Brimacombe et al. | Formation of longitudinal, midface cracks in continuously-cast slabs | |
| Sengupta et al. | Micrograph evidence of meniscus solidification and sub-surface microstructure evolution in continuous-cast ultralow-carbon steels | |
| Thomas et al. | Investigation of strand surface defects using mould instrumentation and modelling | |
| El-Bealy | On the formation of macrosegregation and interdendritic cracks during dendritic solidification of continuous casting of steel | |
| Samarasekera et al. | The continuous–casting mould | |
| Park et al. | Thermal and mechanical behavior of copper molds during thin-slab casting (II): Mold crack formation | |
| Thomas | On-line detection of quality problems in continuous casting of steel | |
| JP5575987B2 (en) | Crack diagnosis apparatus and method for solidified shell in mold | |
| Kumar et al. | Development of intelligent mould for online detection of defects in steel billets | |
| Xia et al. | Investigation of mould thermal behaviour by means of mould instrumentation | |
| KR20190029757A (en) | Continuous casting method of steel | |
| Suzuki et al. | Simulation of transverse crack formation on continuously cast peritectic medium carbon steel slabs | |
| Yu et al. | Numerical simulation and experimental investigation of clad teeming process for preparing stainless steel/carbon steel clad ingot | |
| KR101224979B1 (en) | Crack diagnosis device of solidified shell in mold and method thereof | |
| KR101224981B1 (en) | Crack diagnosis device of solidified shell in mold and method thereof | |
| Lai | Meniscus thermal analysis for detecting defects in continuous cast slabs | |
| Cholewa et al. | Diffusion phenomena between alloy steel and gray cast iron in layered bimetallic casting | |
| Jenkins et al. | Investigation of Strand surface defects using Mold instrumentation and Modelling | |
| Yamauchi et al. | Cooling behavior and slab surface quality in continuous casting with alloy 718 mold | |
| Wang et al. | Formation of internal cracks in steel billets during soft reduction | |
| JP2007185675A (en) | Method for predicting surface defect occurrence risk region in continuous cast slab and method for producing continuous cast slab | |
| KR101224961B1 (en) | Crack diagnosis device of solidified shell in mold and method thereof | |
| Ozturk et al. | Effects of nickel coating of mold plates on star crack defects | |
| Chandra | Heat transfer, oil lubrication and mould tapers in steel billets casting machines |